Water-based aluminium foil glue composition with high peel strength and controllable viscosity and preparation method

A high peeling, aluminum foil adhesive technology, applied in the direction of adhesive types, ester copolymer adhesives, unsaturated alcohol copolymer adhesives, etc., can solve the problems of high cost, unfavorable environmental protection, poor frost resistance, etc. To achieve the effect of simple production, easy to use on the machine, and enhanced cohesion

Active Publication Date: 2014-06-11
CHANGZHOU INST OF CHEM
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some deficiencies in polyvinyl acetate emulsion adhesives, such as poor water resistance, poor abrasion resistance, and poor frost resistance.
Water-based aluminum foil glue still has two more difficult problems to solve. One is that the peel strength of the current aluminum foil glue of the vinegar-acrylic series is not high, which makes it difficult to be applied to higher-grade tobacco and alcohol packaging. Another problem is that the current The aluminum foil glue in the market is milky white, not delicate, and has a high viscosity, which is not conducive to roller coating on the machine
[0003] Chinese patent CN101676352A discloses an aluminum foil adhesive and its preparation method. Its emulsion belongs to styrene-acrylic emulsion and has strong peel strength. However, due to its high solid content and high cost, it is not competitive in the market, and its viscosity is also unsatisfactory. Adjust within a certain range
[0004] Chinese patent CN1021539971A discloses an aluminum foil adhesive and its preparation method. Its emulsion belongs to the category of vinegar-acrylic emulsion, and its peel strength is not high. At the same time, it contains injection molding agent phthalates, which is not conducive to environmental protection.
[0006] The invention adopts the improvement of the copolymerization performance of styrene-acrylic emulsion to obtain a water-based aluminum foil adhesive with low solid content, which successfully solves the problems of low peel strength, adjustable viscosity and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 (unit gram):

[0035] The formula is as follows:

[0036] Styrene 24, butyl acrylate 76.6, isooctyl acrylate 13.33, acrylic acid 6, deionized water 190, sodium lauryl sulfate 3, nonylphenol polyoxyethylene ether 1, ammonium persulfate 0.48, PVA-1788 20, Ammonia 2, potassium bicarbonate 0.5.

[0037] Place the four-neck flask equipped with a stirrer, reflux condenser, thermometer and dropping funnel in a temperature-controllable heating mantle, add metered distilled water, dispersed emulsifier sodium lauryl sulfate and nonylphenol polysaccharide Oxyethylene ether, buffer potassium bicarbonate, and initiator ammonium persulfate are stirred at a high speed at room temperature to fully dissolve. Then add monomer molecule styrene, butyl acrylate, isooctyl acrylate, acrylic acid, and emulsify for 30 minutes. After the emulsification is over, raise the temperature of the reaction flask to 82°C, add 10% pre-emulsified solution, and after the seeds have polymeriz...

Embodiment 2

[0040] Embodiment 2 (unit gram):

[0041] The formula is as follows

[0042] Styrene 30, butyl acrylate 66, isooctyl acrylate 15, acrylic acid 4, deionized water 190, sodium lauryl sulfate 3, nonylphenol polyoxyethylene ether 1, ammonium persulfate 0.48, PVA-1788 20, Ammonia water 2, potassium bicarbonate 0.5.

[0043] Place the four-neck flask equipped with a stirrer, reflux condenser, thermometer and dropping funnel in a temperature-controllable heating mantle, add metered distilled water, dispersed emulsifier sodium lauryl sulfate and nonylphenol polysaccharide The solution of oxyethylene ether, buffer potassium bicarbonate and initiator ammonium persulfate is stirred at a high speed at room temperature to fully dissolve it. Then add monomer butyl acrylate, isooctyl acrylate, acrylic acid, and emulsify for 30 minutes. After the emulsification is over, raise the temperature of the reaction flask to 82°C, add 15% mass of pre-emulsified solution, after the seed polymerizati...

Embodiment 3

[0046] Embodiment 3 (unit gram):

[0047] Styrene 24, butyl acrylate 76.6, isooctyl acrylate 13.33, ethyl acrylate 2, acrylic acid 4, deionized water 190, sodium lauryl sulfate 3, nonylphenol polyoxyethylene ether 1 ammonium persulfate 0.48, F -316 20, ammonia water 2, ammonium bicarbonate 0.5.

[0048] Place the four-neck flask equipped with a stirrer, reflux condenser, thermometer and dropping funnel in a temperature-controllable heating mantle, add metered distilled water, dispersed emulsifier sodium lauryl sulfate and nonylphenol polysaccharide Oxyethylene ether, buffer ammonium bicarbonate, and initiator ammonium persulfate solution are stirred at a high speed at room temperature to fully dissolve them. Then add monomer butyl acrylate, isooctyl acrylate, ethyl acrylate, acrylic acid, and emulsify for 30 minutes. After the emulsification is completed, raise the temperature of the reaction flask to 82°C, add part of the pre-emulsified solution, and after the seed polymeri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
viscosityaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based aluminium foil glue composition with high peel strength and controllable viscosity and a preparation method. The water-based aluminium foil glue is formed by compounding water-based styrene-acrylic emulsion and dispersion liquid of polyvinyl alcohol. The peel strength can be as high as 12N / (25mm), and the viscosity (100-30000mpa.s) is controllable. The water-based aluminium foil glue comprises the following components: 15-25% of soft monomers, 10-20% of hard monomers, 1-5% of functional monomers, 0.2-0.8% of initiator, 1-4% of emulsifiers, 0.2-1% of PH buffer agent, 1-4% of PH agent, 50-80% of softened water and 5-30% of polyvinyl alcohol dispersion. The glue has strong blue light, excellent bonding capacity and controllable viscosity, is environment-friendly, is relatively low in cost, is easy to dry, has freezing resistance and does not contain plasticizers or harmful substances.

Description

technical field [0001] The invention relates to a water-based aluminum foil glue with low solid content, which has high peel strength, good blue light effect and controllable viscosity. In particular, it relates to the composition and preparation method of the glue. Background technique [0002] As people's awareness of environmental protection becomes stronger and stronger, water-based adhesives have become an important trend in the development of adhesives compared to oil-based adhesives. The product that has an absolute advantage in water-based adhesives is emulsion adhesives, and polyvinyl acetate emulsion adhesives are one of the main varieties. However, there are still some deficiencies in polyvinyl acetate emulsion adhesives, such as poor water resistance, poor abrasion resistance, and poor frost resistance. Water-based aluminum foil glue still has two more difficult problems to solve. One is that the peel strength of the current aluminum foil glue of the vinegar-ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J129/04C08F220/18C08F212/08C08F220/06C08F2/30C08F2/26
Inventor 胥元峰蒋银峰王红丹王公应
Owner CHANGZHOU INST OF CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com