Colorized heat reflecting paint as well as preparation method and application thereof

A technology of heat-reflecting and heat-insulating coatings, applied in the field of coatings, can solve the problems of reduced heat-reflecting performance, reduced heat insulation effect, single color, etc., to achieve the effects of reducing surface temperature, improving heat insulation effect, and prolonging service life

Inactive Publication Date: 2014-07-02
SHANGHAI DATONG TABERNACLE NEW ENERGY SAVING MATERIALS CO LTD
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it turns out that this kind of aspect has caused many "thermal bridges" due to many factors during production, which greatly reduces the thermal insulation effect
[0003] At present, most of the existing thermal insulation coatings have a single color, but the construction market r

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorized heat reflecting paint as well as preparation method and application thereof
  • Colorized heat reflecting paint as well as preparation method and application thereof
  • Colorized heat reflecting paint as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0061] Example 1

[0062] A preparation method of a gray heat-reflective coated metal plate, the method comprises the following steps:

[0063] 1) White heat reflective primer

[0064]

[0065] Grey Thermal Insulation Paint Topcoat

[0066]

[0067] The coating preparation process:

[0068] (1) Preparation of primer:

[0069] First put 40.0 parts of polyester resin into the stirring tank, add 10.0 parts of xylene, 4.5 parts of propylene glycol methyl ether acetate, 3.0 parts of adipic acid ester high-boiling point solvent, stir evenly; add 0.5 parts of bentonite thixotropic agent in proportion, After stirring at high speed for 0.5hr, check whether the thixotropic agent has been stirred evenly (no particles); add 1.5 parts of dispersant, 1.5 parts of wetting agent, 0.5 part of defoamer, and 0.5 part of leveling agent in sequence in proportion, and stir evenly ; Add 25.0 parts of titanium dioxide pigment and 5.0 parts of aluminum silicate in proportion, stir for 0.5-1 ...

Example Embodiment

[0078] Example 2

[0079] A preparation method of a coffee-colored heat-reflective coated metal plate, the method comprises the following steps:

[0080] 1) White heat reflective primer

[0081]

[0082] Brown thermal insulation paint finish

[0083]

[0084] The coating preparation process:

[0085] (1) Preparation of primer:

[0086] First put 28.0 parts of epoxy resin into the stirring tank, add 25.0 parts of xylene and 5.0 parts of n-butanol, and stir evenly; add 1.0 parts of bentonite thixotropic agent in proportion, and stir at high speed for 0.5 hr, check whether the thixotropic agent has been stirred Uniform (no granular); add 1.5 parts of dispersant and 0.5 part of leveling agent in sequence, and stir evenly; add 25.0 parts of titanium dioxide pigment, 5.0 parts of talc, 8.0 parts of zirconium silicate in proportion, and stir for 0.5-1 hours, until the dispersion is uniform; put the above slurry into a sand mill, grind it until the fineness reaches 20-25 mic...

Example Embodiment

[0095] Example 3

[0096] A preparation method of a beige heat-reflecting coated metal plate, the method comprises the following steps:

[0097] 1) White heat reflective primer

[0098]

[0099] Beige thermal insulation paint finish

[0100]

[0101] The coating preparation process:

[0102] (1) Preparation of primer:

[0103] First put 40.0 parts of polyester resin into the stirring tank, add 10.0 parts of xylene, 4.5 parts of propylene glycol methyl ether acetate, 3.0 parts of adipic acid ester high-boiling point solvent, stir evenly; add 0.5 parts of bentonite thixotropic agent in proportion, After stirring at high speed for 0.5hr, check whether the thixotropic agent has been stirred evenly (no particles); add 1.5 parts of dispersant, 1.5 parts of wetting agent, 0.5 part of defoamer, and 0.5 part of leveling agent in sequence in proportion, and stir evenly ; Add 25.0 parts of titanium dioxide pigment and 5.0 parts of aluminum silicate in proportion, stir for 0.5-1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat reflecting paint for a metal plate and a preparation method of the heat reflecting paint. The heat reflecting paint is thin in painting layer, wide in application range and convenient to use. A colorized painting layer is obtained by the heat reflecting paint. Thus, compared with the common heat reflecting paint of a single color, according to the heat reflecting paint disclosed by the invention, the temperature of the surface of the metal plate is greatly decreased, so that the heat entering the metal plate is reduced; and the service life of the metal plate is prolonged.

Description

Technical field [0001] The present invention involves a coating, especially the preparation methods and uses of a colorful heat reflected coatings and coatings. Background technique [0002] With the development of my country's industrialization and urbanization, my country has become the largest construction market in the world. The steel structure system has entered The residential building market, similarly, with the needs of public facilities and urban construction, the demand for building curtain walls has shown an upward trend.However, aluminum and iron are good carriers, but the requirements of national policies on energy conservation for construction are getting higher and higher. Energy saving of steel structure and aluminum curtain wall is particularly critical. Energy -saving materials are also in line with market development needs."Thermal fluorocarbon aluminum veneer" invented the thermal insulation cotton with insulation cotton with insulation on the back to achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/33C09D5/29C09D163/00C09D167/00C09D133/00C09D127/12C09D7/12
Inventor 杨宇奇
Owner SHANGHAI DATONG TABERNACLE NEW ENERGY SAVING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap