Low-zirconium mullite draft tube brick and preparation method thereof

A zirconium mullite and guide tube technology is applied in the field of low zirconium mullite guide tube bricks and their preparation, and can solve the problems of shortening the service life of the nuclear power industry, easy falling off of large steel ingots, and reducing the purity of large steel ingots. , to achieve the effect of good thermal shock stability, non-oxidizing high-temperature chemical properties, and high softening temperature under load

Active Publication Date: 2015-03-04
四川锦圆耐材有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The diversion pipe is in direct contact with the molten steel during the pouring process. After the molten steel passes through the diversion pipe and enters the ingot, there is little chance of the inclusions floating up. Therefore, the erosion resistance of the diversion pipe brick directly affects the internal quality of the molten steel and the quality of the ingot. , shorten its service life in the nuclear power industry, and even have potential safety hazards
[0005] In order to improve the purity of steel ingots, the duct bricks are required to have good erosion resistance, thermal stability, high temperature resistance, etc., but the current duct bricks cannot meet this requirement, and they are easy to fall off when pouring large steel ingots, reducing the The purity of large steel ingots limits the use of large steel ingots in the nuclear power industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A low-zirconia mullite duct brick, which is composed of the following raw materials in parts by weight: fused mullite: 50 parts; zirconia: 20 parts; Guangxi white clay: 5 parts; andalusite: 20 parts; kyanite Stone: 3 parts; Lignin: 2 parts.

[0025] The preparation method of this low-zircon mullite duct brick is as follows:

[0026] a. Mix fused mullite, zirconia, andalusite and kyanite in proportion and then pulverize or mix in proportion after pulverization to obtain mixed particles. The mixed particles are, by weight percentage, with a particle size of 200 mesh Particles account for 50~60%, particles with a particle size of 1~3mm account for 30~40%, particles with a particle size of 3~5mm account for 5~10%;

[0027] b. Grind the mixed particles obtained in step a into 200 mesh Guangxi white clay and have a density of 1.22~1.25g / cm 3 The lignin aqueous solution is mixed in proportion to obtain a mixed raw material;

[0028] c. pressing the mixed raw mat...

Embodiment 2

[0033] A low-zirconia mullite duct brick, which is composed of the following raw materials in parts by weight: fused mullite: 45 parts; zirconia: 15 parts; Guangxi white clay: 8 parts; andalusite: 25 parts; kyanite Stone: 2 parts; Lignin: 5 parts.

[0034] The preparation method of this low-zircon mullite duct brick is as follows:

[0035] a. Mix fused mullite, zirconia, andalusite and kyanite in proportion and then pulverize or mix in proportion after pulverization to obtain mixed particles. The mixed particles are, by weight percentage, with a particle size of 200 mesh 60% of particles, 30% of particles with a particle size of 1~3mm, and 10% of particles with a particle size of 3~5mm;

[0036] b. Grind the mixed particles obtained in step a into 200 mesh Guangxi white clay and have a density of 1.22~1.25g / cm 3 The lignin aqueous solution is mixed in proportion to obtain a mixed raw material;

[0037] c. pressing the mixed raw material in step b into adobe;

...

Embodiment 3

[0042] A low-zirconia mullite duct brick, which is composed of the following raw materials in parts by weight: fused mullite: 55 parts; zirconia: 15 parts; Guangxi white clay: 3 parts; andalusite: 20 parts; kyanite Stone: 5 parts; Lignin: 2 parts.

[0043] The preparation method of this low-zircon mullite duct brick is as follows:

[0044] a. Mix fused mullite, zirconia, andalusite and kyanite in proportion and then pulverize or mix in proportion after pulverization to obtain mixed particles. The mixed particles are, by weight percentage, with a particle size of 200 mesh 50% of particles, 40% of particles with a particle size of 1~3mm, and 10% of particles with a particle size of 3~5mm;

[0045] b. Grind the mixed particles obtained in step a into 200 mesh Guangxi white clay and have a density of 1.22~1.25g / cm 3 The lignin aqueous solution is mixed in proportion to obtain a mixed raw material;

[0046] c. pressing the mixed raw material in step b into adobe;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-zirconium mullite draft tube brick and a preparation method thereof, belonging to the field of refractory materials. The low-zirconium mullite draft tube brick comprises the following raw materials by weight: 45 to 55 parts of fused mullite, 15 to 25 parts of zirconia, 3 to 8 parts of Guangxi white mud, 15 to 25 parts of andalusite, 2 to 5 parts of kyanite and 1 to 5 parts of lignin. According to the invention, through selection of types and particle sizes of the raw materials and cooperative usage of sintering temperature and time provided by the invention, the prepared draft tube brick has the characteristics of excellent anti-scouring performance and high temperature resistance, small creep deformation, good thermal stability, etc. and is applicable to vacuum casting of large steel ingots in a nuclear power product.

Description

Technical field [0001] The present invention is the field of refractory materials, which involves a low -sized Mo Lai stone guide tube brick and its preparation methods. Background technique [0002] For a long time, the energy structure of coal -dominated coal has not only adapted to the rapid development of the economy, but also caused more serious social energy and environmental problems.Energy hair faces, coal can be used by humans for 200 to 220 years, and human beings face the severe situation of coal depletion.Greenhouse gases such as carbon dioxide, sulfur oxide and nitrogen oxide, and a large amount of smoke, cause extremely serious damage to the environment.Therefore, it is necessary to actively improve the energy utilization structure and the diversified supply of energy.At present, due to the separation of the dry water period and the period, the hydropower and electricity are not stable enough; and the solar energy and wind energy cannot occupy a large share in the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 宋政德
Owner 四川锦圆耐材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com