A method for preparing iron ferric oxide nanoparticles

A technology of ferroferric oxide and nanoparticles, which is applied in the field of nanomaterials to achieve the effects of high crystallinity, good dispersion and stability, and high surface activity

Inactive Publication Date: 2015-12-09
SUZHOU UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There is no report on the preparation of iron ferric oxide nanoparticles by using amphoteric hyperbranched polyglycidyl ether modification by solvothermal method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing iron ferric oxide nanoparticles
  • A method for preparing iron ferric oxide nanoparticles
  • A method for preparing iron ferric oxide nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Dissolve 6.0 mL of oleoyl chloride in 60 mL of toluene, and dissolve 2 g of hyperbranched polyglycidyl ether in 80 mL of pyridine. The obtained oleoyl chloride toluene solution is dropped dropwise into the pyridine solution of hyperbranched polyglycidyl ether. After stirring at 30°C for 48 hours, The excess solvent was removed by rotary evaporation at 80°C, and the excess oleoyl chloride was removed by washing with chloroform to obtain amphiphilic hyperbranched polyglycidyl ether.

[0028] Take (NH 4 ) 2 Fe(SO 4 ) 2 .6H 2 0.784g was dissolved in 20mL deionized water, 0.5g amphiphilic hyperbranched polyglycidyl ether was dissolved in 10mL chloroform, and under rapid stirring, the amphiphilic hyperbranched polyglycidyl ether solution was slowly added dropwise to (NH 4 ) 2 Fe(SO 4 ) 2 .6H 2 O aqueous solution, mixed evenly to get Fe 2+ Precursor solution; 1g NaOH was dissolved in 10mL ethanol, and the resulting NaOH solution was added dropwise to the above Fe 2+ ...

Embodiment 2

[0035] Take 1.0 mL of oleoyl chloride and dissolve in 80 mL of toluene, and dissolve 1 g of amino-terminated hyperbranched polymer in 100 mL of pyridine. The obtained oleoyl chloride toluene solution is dropped dropwise into the pyridine solution of amino-terminated hyperbranched polymer, and after stirring at 25 ° C for 40 h, The excess solvent was removed by rotary evaporation at 80°C, and the excess oleoyl chloride was removed by washing with acetone to obtain an amphiphilic amino-terminated hyperbranched polymer.

[0036] FeSO 4 ·7H 2 O1.112g was dissolved in 40mL deionized water, 1g amphiphilic amino-terminated hyperbranched polymer was dissolved in 20mL ethanol, and under rapid stirring, the amphiphilic amino-terminated hyperbranched polymer solution was slowly added dropwise to FeSO 4 ·7H 2 O aqueous solution, mixed evenly to get Fe 2+ Precursor solution; 2g KOH was dissolved in 20mL n-butanol, and the resulting KOH solution was added dropwise to the above Fe 2+ In ...

Embodiment 3

[0038] Dissolve 5.0 mL of oleoyl chloride in 40 mL of diethyl ether, and dissolve 2 g of hyperbranched polyglycidyl ether in 50 mL of methanol. The obtained oleoyl chloride diethyl ether solution is dropped dropwise into the methanol solution of hyperbranched polyglycidyl ether. After stirring at 50°C for 56 hours, Rotary evaporation at 50°C removes excess solvent, washes with ethyl acetate to remove excess oleoyl chloride, and vacuum-dries at 60°C for 12 hours to obtain amphiphilic hyperbranched polyglycidyl ether.

[0039] FeCl 2 4H 2 O0.3976g was dissolved in 20mL deionized water, 0.5g amphiphilic hyperbranched polyglycidyl ether was dissolved in 10mL ethylene glycol, and under rapid stirring, the amphiphilic hyperbranched polyglycidyl ether solution was slowly added dropwise to FeCl 2 4H 2 O aqueous solution, mixed evenly to get Fe 2+ Precursor solution; 15mL concentration of 28% ammonia solution was added dropwise to the above Fe 2+ In the precursor solution, the obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing triiron tetraoxide nanometer particles. A hyperbranched polymer is hydrophobically modified by fatty acyl chloride to prepare an amphiphilic hyperbranched polymer; and the highly dispersed triiron tetraoxide nanometer particles are prepared via a water / organic one-step solvothermal method by virtue of the micelle self-assembly effect of the amphiphilic hyperbranched polymer as a protective agent in a solution, the average particle size of the triiron tetraoxide nanometer particles is 8nm-35nm; the surfaces of the triiron tetraoxide nanometer particles are amphiphilically modified by virtue of encapsulation and dispersion effects of the amphiphilic hyperbranched polymer on the triiron tetraoxide nanometer particles, so that triiron tetraoxide nanometer particles are dispersed and stably exist in solvents with different degrees of polarity, at the same time, a plurality of active groups are given on the surface of the particles, the active groups provide possible sites for the secondary functionalization of particles and the application range of the triiron tetraoxide nanometer particles is extended.

Description

technical field [0001] The invention relates to a method for preparing iron ferric oxide nanoparticles, belonging to the field of nanometer materials. Background technique [0002] Magnetic nanoparticles refer to magnetic particles with a particle size between 1 and 100nm. They are new functional materials integrating nanomaterials and magnetic materials. They have unique optical, electrical, thermal and magnetic properties that conventional solids do not have. performance becomes the focus of attention. Like other nanometer-sized materials, magnetic nanoparticles have the quantum size effect, small size effect, and surface effect of nanoparticles, and at the same time have the unique superparamagnetism of magnetic nanoparticles. These properties and characteristics determine that it has broad application prospects in the fields of hyperthermia treatment of tumors, targeted drug carriers, sewage treatment, catalyst carriers, cell separation, biosensors, and magnetic recordi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/08B82Y30/00
Inventor 陈宇岳熊佳庆徐思峻林红
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com