A kind of determination method of total iron content in vanadium slag

A determination method and technology for iron content, applied in the field of chemical detection, can solve the problems of incomplete dissolution of the sample, interference with the total iron content, large measurement error, etc., and achieve the effect of good promotion and application prospects, fast analysis speed, and reduction of test errors.

Active Publication Date: 2016-06-01
WUKUN STEEL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The titration method is used to measure the total iron content in the vanadium slag, and the total iron can be measured after the sample is completely dissolved, but due to the high content of vanadium pentoxide in the vanadium slag, the sample is not completely dissolved by the conventional sample di

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of determination method of total iron content in vanadium slag
  • A kind of determination method of total iron content in vanadium slag
  • A kind of determination method of total iron content in vanadium slag

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1

[0041] ——Detection of total iron content in vanadium slag sample

[0042] Reagents for detection:

[0043] Sodium hydroxide: (solid).

[0044] Sulfuric acid: the concentration is (ρ1.84g / mL).

[0045] Phosphoric acid: The concentration is (ρ1.69g / mL).

[0046] Hydrochloric acid: the concentration is (ρ1.19g / mL).

[0047] Titanium trichloride: the concentration is (150g / L-200g / L).

[0048] Sodium hydroxide solution: the concentration is 50g / L.

[0049] Hydrochloric acid: (1+1).

[0050] Hydrochloric acid: (5+95).

[0051] Ammonia thiocyanate solution: the concentration is 50g / L.

[0052] Stannous chloride solution 100g / L: Weigh 10g of stannous chloride and dissolve it in 20mL of hot hydrochloric acid (ρ1.19g / mL), dilute to 100mL with water, and shake well.

[0053] Sodium tungstate solution 250g / L: Weigh 25g sodium tungstate and dissolve it in 95mL water (filter if it is turbid), add 5mL phosphoric acid (4.2), shake well.

[0054] Titanium trichloride solution: Pipette 5mL tita...

Example Embodiment

[0075] Example 2

[0076] ——Detection of total iron content in vanadium slag sample

[0077] Detection reagent: same as Example 1

[0078] Sample detection:

[0079] A. Sample pretreatment: crush the sample to a particle size ≤0.125mm, dry it at 105-110℃ for 1.5-2.5h, seal it in a desiccator, and cool it to 20-25℃.

[0080] Steps B, C, D, E, and F are the same as in Example 1.

[0081] G. Content calculation: The iron content in the sample is calculated as follows:

[0082] c——The concentration of potassium dichromate standard titration solution is 0.0400 (mol / L);

[0083] m——The mass of the sample in step B is 0.2000g;

[0084] V 0 ——The titration blank test solution consumes potassium dichromate and the standard titration solution volume is 0.00ml;

[0085] V——The titration sample solution consumes potassium dichromate. The standard titration solution volume is 34.50ml;

[0086] 55.85-per mole mass of iron, in grams per mole (g / mol).

[0087]

[0088]

[0089] =38.54

Example Embodiment

[0090] Example 3

[0091] ——Detection of total iron content in vanadium slag sample

[0092] Detection reagent: same as Example 1

[0093] Sample detection:

[0094] A. Sample pretreatment: crush the sample to a particle size ≤0.125mm, dry it at 105-110℃ for 1.5-2.5h, seal it in a desiccator, and cool it to 20-25℃.

[0095] Steps B, C, D, E, and F are the same as in Example 1.

[0096] G. Content calculation: The iron content in the sample is calculated as follows:

[0097] c——The concentration of potassium dichromate standard titration solution is 0.0400 (mol / L);

[0098] m——The mass of the sample in step B is 0.2000g;

[0099] V 0 ——The titration blank test solution consumes potassium dichromate and the standard titration solution volume is 0.00ml;

[0100] V——The titration sample solution consumes potassium dichromate and the standard titration solution volume is 6.95ml;

[0101] 55.85-per mole mass of iron, in grams per mole (g / mol).

[0102]

[0103]

[0104] =7.76

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for testing total iron content in vanadium slag. A sample is smashed and dried, the smashed sample and sodium hydroxide are mixed uniformly in a corundum crucible, then sodium hydroxide is added, melting is carried out, melt is dissolved in hot water in a beaker, boils slightly for 2-3 minutes and then is cooled to be at the room temperature through water cooling, filtering is carried out through medium-speed filter paper, the beaker and sediment are washed for five to six times through sodium hydroxide solutions, the sediment on the filer paper is washed in the original beaker through hot water and hot hydrochloric acid and boils slightly for 5 minutes, stannous chloride is dripped into the solution and is faint yellow, and the solution is cooled to be at the room temperature through water cooling. Sodium tungstate solutions are dripped for ten times, tungsten blue is produced through titanium trichloride solutions in a reduction mode, potassium dichromate solutions are dripped until the blue color disappears, sulphur and phosphorus mixed acid solutions of 15 millimeters are added, aniline sulfonic acid sodium indicators are dripped for three to five times, potassium dichromate standard titration solutions are dripped until the solutions are purple stably, and the total iron content in the sample is calculated according to the formula shown in the instruction. The method is good in accuracy, reproducibility and stability and is especially suitable for detecting the total iron content in the vanadium slag.

Description

technical field [0001] The invention belongs to the technical field of chemical detection, and in particular relates to a method for measuring total iron content in vanadium slag. Background technique [0002] Vanadium slag is a general term for vanadium oxide-containing slag obtained by oxidation blowing of vanadium-containing molten iron or vanadium-containing iron concentrate by wet extraction of vanadium. It is used for smelting and producing vanadium alloys and metals. Raw material of vanadium. The main component of vanadium slag is V 2 0 5 , P, CaO and SiO 2 And Fe content. Among them, the content of total iron has an important influence on the performance of the product, so the accurate determination of its content has very important practical significance for smelting production. Determination of total iron content in vanadium slag, there is no quantitative analysis and determination method. The content of total iron in other materials such as iron ore is mostl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N31/16G01N31/22
Inventor 郑玲陶俊孙肖媛李文生王宁
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap