Nylon corrugated pipe

A technology of bellows and nylon, applied in the field of nylon bellows and its preparation, to achieve the effects of good toughness, long service life and strong impact resistance

Inactive Publication Date: 2014-10-01
ANHUI HAINA SICHUAN PLASTICS TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The absolute value of the mechanical properties of polypropylene is higher than that of polyethylene, but it is still a low variety in plastic materials, and its tensile strength can only reach 30 MPa or a slightly higher level.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of nylon bellows, it is made up of the raw material of following weight parts:

[0020] Phosphite 1, Hexabromocyclododecane 1, Nylon 610 14, Dimethylol Dihydroxyethylene Urea 0.4, Chromium Carbonate 1, Methyl 2,2-Dithienyl Glycolate 2, Epoxy Octyl Stearate 4. Hexagonal boron nitride 4, montmorillonite powder 8, polyvinylidene fluoride 3, dipropylene glycol 3, ammonium dihydrogen phosphate 2, polypropylene 96, compound additive 5;

[0021] Described composite auxiliary agent is made up of the raw material of following weight part:

[0022] Polypropylene 30, polyvinylidene fluoride 20, titanium nitride 1, silicone oil 2, sepiolite powder 20, dithiocyanomethane 0.2, polyacrylate isooctyl 3, ammonium octamolybdate 0.5, 2,6-di Tert-butyl p-cresol 0.4;

[0023] Mix the above-mentioned polypropylene with polyvinylidene fluoride, heat it at 120°C for 30 minutes, add titanium nitride, grind it evenly, add dithiocyanomethane, stir and disperse at 300 rpm for 3-5 minutes,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nylon corrugated pipe, comprising the following raw materials in parts by weight: 1-2 parts of phosphite ester, 1-2 parts of hexabromocyclododecane, 10-14 parts of nylon 610, 0.4-1 part of di-methylol di-hydroxy ethylene urea, 1-2 parts of chromic carbonate, 1-2 parts of 2,2-dithienyl methyl glycolate, 2-4 parts of epoxy ethylhexyl stearate, 2-4 parts of hexagonal boron nitride, 6-8 parts of montmorillonite powder, 2-3 parts of polyvinylidene fluoride, 2-3 parts of dipropylene glycol, 1-2 parts of ammonium dihydrogen phosphate, 90-96 parts of polypropylene and 5-7 parts of compound additive. The corrugated pipe disclosed by the invention has good high temperature resistance, good acid and alkali corrosion resistance, strong shock resistance, excellent physical property, good tenacity, high surface hardness, and long service life, and is especially applicable to being used as a dry corrugated pipe material under a high-temperature condition.

Description

technical field [0001] The invention mainly relates to the field of pipe materials, in particular to a nylon corrugated pipe and a preparation method thereof. Background technique [0002] Polypropylene has high crystallinity and regular structure, so it has excellent mechanical properties. The absolute value of the mechanical properties of polypropylene is higher than that of polyethylene, but it is still a relatively low variety in plastic materials, and its tensile strength can only reach 30 MPa or a slightly higher level. Polypropylene with a larger isotactic index has higher tensile strength, but as the isotactic index increases, the impact strength of the material decreases, but it does not change after falling to a certain value. [0003] Temperature and loading rate have a great influence on the toughness of polypropylene. When the temperature is higher than the glass transition temperature, the impact fracture is ductile fracture, and below the glass transitio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L77/06C08L27/16C08K13/06C08K9/00C08K3/34C08K3/28C08K5/372C08K5/13C08K3/38C08K5/1515
CPCC08L23/12C08L2201/08C08L2203/18C08L2205/025C08L2205/035
Inventor 强健娜
Owner ANHUI HAINA SICHUAN PLASTICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products