Flame-retardant environment-friendly foamed plastic

A foamed plastic and environmentally friendly technology, applied in the field of foamed plastics, can solve problems that affect the absorption of nutrients and water by crops, affect the sustainable use of land, and the land cannot be restored, and achieve good softness and chemical stability. Good aging and improved wear resistance

Inactive Publication Date: 2014-11-05
NINGGUO NINGSHENG RUBBER PROD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The accumulation of waste plastic products mixed in the soil will affect the absorption of nutrients and water by crops, resulting in reduced crop production and affecting agricultural development
Due to its extremely difficult to decompose, landfill treatment will not only occupy a large amount of land, but the occupied land will not be restored for a long time, which will affect the sustainable use of land; if it is disposed of by incineration, it will cause serious air pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The present invention proposes a kind of flame-retardant and environment-friendly foaming plastic, and its raw materials include by weight: 36 parts of ethylene-vinyl acetate copolymer EVA, 69 parts of polycaprolactone PCL, 3.1 parts of 400-mesh soybean meal, 2.8 parts of wood fiber, 1.6 parts of titanate coupling agent NDZ-TTS, 3.3 parts of sodium lactate, 16 parts of foaming agent ADC, 10 parts of zinc oxide, 9.7 parts of citric acid, 12 parts of sodium bicarbonate, 1.8 parts of diisononyl phthalate DINP , 2.4 parts of epoxy octyl stearate, 26 parts of barite powder, 16 parts of pyroxene powder, 10 parts of white carbon black, 6 parts of mica powder, 5 parts of ammonium polyphosphate, 6 parts of melamine sodium polyphosphate, 2,6-di 1.7 parts of tert-butyl-4-methylphenol BHT, 1.4 parts of antioxidant BLE; during the preparation process, add titanate coupling agent NDZ-TTS to barite powder, pyroxene powder, white carbon black, mica powder, polyphosphoric acid Ammonium ...

Embodiment 2

[0016] The present invention proposes a kind of flame-retardant and environment-friendly foaming plastic, and its raw material comprises by weight: 32 parts of ethylene-vinyl acetate copolymer EVA, 72 parts of polycaprolactone PCL, 2.8 parts of 450-mesh soybean meal, 3.6 parts of wood fiber, 1.2 parts of titanate coupling agent NDZ-TTS, 3.6 parts of sodium lactate, 13 parts of foaming agent ADC, 12 parts of zinc oxide, 9 parts of citric acid, 14 parts of sodium bicarbonate, 1.6 parts of diisononyl phthalate DINP , 2.7 parts of epoxy octyl stearate, 23 parts of barite powder, 18 parts of pyroxene powder, 7 parts of white carbon black, 9 parts of mica powder, 3 parts of ammonium polyphosphate, 8 parts of melamine sodium polyphosphate, 2,6-di 1.5 parts of tert-butyl-4-methylphenol BHT, 1.6 parts of antioxidant BLE; during the preparation process, add titanate coupling agent NDZ-TTS to barite powder, pyroxene powder, white carbon black, mica powder, polyphosphoric acid Ammonium an...

Embodiment 3

[0018] The present invention proposes a kind of flame-retardant and environment-friendly foaming plastic, its raw material comprises by weight: 33 parts of ethylene-vinyl acetate copolymer EVA, 70 parts of polycaprolactone PCL, 2.9 parts of 430-mesh soybean meal, 3.2 parts of wood fiber, 1.4 parts of titanate coupling agent NDZ-TTS, 3.5 parts of sodium lactate, 14 parts of foaming agent ADC, 11 parts of zinc oxide, 9.2 parts of citric acid, 13 parts of sodium bicarbonate, 1.7 parts of diisononyl phthalate DINP , 2.6 parts of epoxy octyl stearate, 24 parts of barite powder, 17 parts of pyroxene powder, 8 parts of white carbon black, 8 parts of mica powder, 4 parts of ammonium polyphosphate, 7 parts of melamine sodium polyphosphate, 2,6-di 1.6 parts of tert-butyl-4-methylphenol BHT, 1.5 parts of antioxidant BLE; during the preparation process, add titanate coupling agent NDZ-TTS to barite powder, pyroxene powder, white carbon black, mica powder, polyphosphoric acid Ammonium and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant environment-friendly foamed plastic which comprises the following raw materials in parts by weight: 32-37 parts of ethylene-vinyl acetate (EVA) resin, 68-72 parts of polycaprolactone (PCL), 2.8-3.2 parts of soybean meal, 2.7-3.6 parts of wood fibers, 1.2-1.7 parts of a titanate coupling agent NDZ-TTS, 3-3.6 parts of sodium lactate, 13-17 parts of a foaming agent ADC, 8-12 parts of zinc oxide, 9-10 parts of citric acid, 11-14 parts of sodium hydrogen carbonate, 1.6-1.9 parts of diisononyl phthalate (DINP), 2.2-2.7 parts of epoxy octyl stearate, 23-28 parts of barite powder, 15-18 parts of augite powder, 7-11 parts of white carbon black, 5-9 parts of mica powder, 3-6 parts of ammonium polyphosphate, 5-8 parts of melamine sodium polyphosphate, 1.5-1.8 parts of 2,6-di-tert-butyl-4-methylphenol (BHT) and 1.3-1.6 parts of an antioxidant BLE.

Description

technical field [0001] The invention relates to the technical field of foamed plastics, in particular to a flame-retardant and environment-friendly foamed plastic. Background technique [0002] Plastic materials are widely used, such as toys, plastic bottles, packaging bags, shopping bags, etc. We cannot live without plastics. However, as we all know, ordinary PP / PE plastics are difficult to decompose in the natural environment for hundreds of years, so discarded plastic products - also known as "white garbage" - are recognized as substances that can cause great damage to the environment. The accumulation of waste plastic products mixed in the soil will affect the absorption of nutrients and water by crops, resulting in reduced crop production and affecting agricultural development. Due to its extremely difficult to decompose, landfill treatment will not only occupy a large amount of land, but the occupied land will not be restored for a long time, affecting the sustainable...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L23/08C08L97/02C08L89/00C08K13/06C08K9/04C08K5/098C08K3/36C08K3/34C08K5/12C08K5/15C08K3/32C08K5/3492C08K5/13C08K3/30C08J9/08
Inventor 陶文霖
Owner NINGGUO NINGSHENG RUBBER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products