Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Novel zirconium composite ceramic material

A composite ceramic and zirconium technology, applied in the field of new zirconium composite ceramic materials, can solve the problems of affecting enterprise benefits, high porosity, poor oxidation resistance, etc., to improve thermal shock resistance, solve waste residue pollution, and small thermal expansion coefficient. Effect

Inactive Publication Date: 2014-11-19
QINGDAO XIANGHAI ELECTRONICS
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The high-temperature materials used in industrial ceramics, electric power, aviation, heavy metal smelting, ladle bottom blowing furnace, petroleum hot blast furnace, etc. have poor comprehensive performance, poor oxidation resistance and low refractoriness
Improper material selection directly affects the service life, too high porosity, poor thermal shock resistance, poor corrosion resistance, and poor Fe0 slag resistance, which directly affects the profitability of the enterprise and greatly wastes resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A new type of zirconium composite ceramic material, comprising the following parts by weight: 10 parts of titanium corundum, 35 parts of macang soil, 4 parts of aluminum nitride, 15 parts of porcelain stone, 11 parts of bract powder, 3.2 parts of iron oxide, Acrylic resin 5 parts, silicon nitride 5 parts, bovine bone 35 parts, magnesium oxide 11 parts, chromium oxide 3 parts, boron nitride 1.6 parts, zirconium dioxide 15 parts, aluminum oxide 5 parts.

Embodiment 2

[0015] A new type of zirconium composite ceramic material, comprising the following parts by weight: 20 parts of titanium corundum, 50 parts of macang soil, 8 parts of aluminum nitride, 31 parts of porcelain stone, 15 parts of bractite powder, 9 parts of iron oxide, 17 parts of acrylic resin, 13 parts of silicon nitride, 48 parts of bovine bone, 19 parts of magnesium oxide, 9 parts of chromium oxide, 5.4 parts of boron nitride, 40 parts of zirconium dioxide, and 5-11 parts of aluminum oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel zirconium composite ceramic material which is characterized by being prepared from the following substances in parts by weight: 10-20 parts of titanium corundum, 35-50 parts of Macang soil, 4-8 parts of aluminum nitride, 15-31 parts of chinastone, 11-15 parts of maize powder, 3.2-9 parts of ferric oxide, 5-17 parts of acrylic resin, 5-13 parts of silicon nitride, 35-48 parts of ox bones, 11-19 parts of magnesium oxide, 3-9 parts of chromic oxide, 1.6-5.4 parts of boron nitride, 15-40 parts of zirconium dioxide and 5-11 parts of aluminum oxide. The material disclosed by the invention is small in coefficient of thermal expansion, low in cost, resource-saving and high in refractoriness, thermal shock stability resistance and oxidation resistance, and solves the problems of pollution of waste residues and emission of pollution of industrial waste residues. Nitrogen and oxygen in air are fully utilized as fuels, so that the energy sources are saved, thereby achieving the effects on saving energy and reducing emission to a great extent.

Description

technical field [0001] The invention relates to a novel zirconium composite ceramic material. Background technique [0002] The high-temperature materials used in industrial ceramics, electric power, aviation, heavy metal smelting, ladle bottom blowing furnace, petroleum hot blast furnace and other processes have poor comprehensive performance, poor oxidation resistance and low refractoriness. Improper material selection will directly affect the service life, the porosity is too high, the thermal shock resistance is poor, the corrosion resistance is poor, and the Fe0 slag resistance is poor, which directly affects the profit of the enterprise and greatly wastes resources. Contents of the invention [0003] The technical problem to be solved by the invention is to provide a novel zirconium composite ceramic material. [0004] In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is: [0005] A new type ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13
Inventor 张昊亮
Owner QINGDAO XIANGHAI ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products