Photo-cure fluorine modified acrylic acid based inkjet printer ink and preparation method thereof

An inkjet printer, acrylic-based technology, applied in ink, household utensils, applications, etc., can solve the problem of low efficiency of solar cells, and achieve the effect of improving overall efficiency, performance improvement, and large absorption

Inactive Publication Date: 2014-11-19
ZHONGYUAN ENGINEERING COLLEGE
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the optical resonance also causes the nanoparticles to ab

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] One. The ink composition of this embodiment is:

[0039] 0.5-5% light-curable fluorine-modified acrylic resin solution (solid content is 1-10%);

[0040] 0.0001-0.1% of nano aluminum powder;

[0041] 30-70% additives;

[0042] 0.1-5% viscosity regulator;

[0043] The balance is solvent.

[0044] The additive is composed of the following parts by weight: 35-55 parts by weight of ketone; 10-25 parts by weight of alcohol ether ester; 10-20 parts by weight of acid ester; 10-30 parts by weight of alcohol ether.

[0045] The solvent of the photocurable fluorine modified resin solution is one or more of alcohol, ketone, ether, ester, and hydrocarbon, and the solution concentration is 20-30%;

[0046] The solvent is one or more of alcohol, ester, ether, thioether, glycol ether, glycol ether acetate, amine, amide, ketone or hydrocarbon.

[0047] The alcohol is one or more of methanol, ethanol, propanol, isopropanol, butanol, pentanol, hexanol, and fluorinated alcohol.

[00...

Example Embodiment

[0060] Example 2

[0061] One. The ink composition of this embodiment is:

[0062] 0.5% light-curable fluorine-modified acrylic resin solution (solid content is 1-10%);

[0063] 0.0001% of nano aluminum powder;

[0064] 30% additives;

[0065] 0.1% viscosity regulator;

[0066] The balance is solvent.

[0067] The additive is composed of the following components in parts by weight: 35 parts by weight of acetone; 10 parts by weight of alcohol ether ester; 10 parts by weight of methyl acetate; and 10 parts by weight of diethyl ether.

[0068] The solvent of the photocurable fluorine modified resin solution is methanol, and the solution concentration is 20-30%;

[0069] The solvent is methanol.

[0070] The viscosity regulator is N-methyl-2-pyrrolidone or poly-3-methylthiophene.

[0071] 2. The preparation method is:

[0072] (1) Take 500 g of perfluoroalkyl ethyl acrylate and 2 g of hydrogen-containing silicone oil (with a hydrogen content of 0.75%), add them to a three-necked flask equipped...

Example Embodiment

[0079] Example 3

[0080] One. The ink composition of this embodiment is:

[0081] 5% light-curable fluorine-modified acrylic resin solution (solid content is 1-10%);

[0082] 0.1% nano aluminum powder;

[0083] 70% additives;

[0084] 5% viscosity regulator;

[0085] The balance is solvent.

[0086] The additive is composed of the following components in parts by weight: 55 parts by weight of acetone; 25 parts by weight of alcohol ether ester; 20 parts by weight of acid ester; 30 parts by weight of alcohol ether.

[0087] The solvent of the photocurable fluoro-modified resin solution is methyl isopropanone, and the solution concentration is 30%;

[0088] The solvent is methyl acetate.

[0089] The viscosity regulator is N-methyl-2-pyrrolidone or poly-3-methylthiophene.

[0090] 2. The preparation method is:

[0091] (1) Take 500g of perfluorooctyl ethyl acrylate and 25g of hydrogen-containing silicone oil (with a hydrogen content of 0.75%), and add them to a three-necked flask equipped wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses photo-cure fluorine modified acrylic acid based inkjet printer ink and a preparation method thereof, and the photo-cure fluorine modified acrylic acid based inkjet printer ink comprises the following components by weight: 0.5-5% of a photo-cure fluorine modified acrylic acid based resin solution; 0.0001-0.1% of nano aluminum powder; 30-70% of an additive; 0.1-5% of a viscosity regulator; 0.1-5% of a photoinitiator; 0.1-5% of a reactive diluent and the balance of a solvent. The photo-cure fluorine modified acrylic acid based inkjet printer ink product prepared by the method is printed onto the surface of a flexible or thin film solar cell by inkjet printing technology to directly improve the power generation efficiency of the flexible or thin film solar cell.

Description

technical field [0001] The invention relates to an inkjet printer ink for flexible or thin-film solar cells and a preparation method thereof. By using the ink to print on the light-incident surface of the flexible or thin-film solar cells, the efficiency of the flexible or thin-film solar cells can be directly improved. And has the function of self-cleaning. Background technique [0002] Acrylic resin has the characteristics of light color, high transparency, bright and full, tough coating film, strong adhesion, corrosion resistance, etc., and is a commonly used coating material. Because acrylic resin has certain defects in specific occasions, such as hardness, anti-pollution, solvent resistance, poor mechanical properties and high cost, etc., its further application is limited. In recent years, with the continuous improvement and development of polymerization technology and people's emphasis on environmental protection products, the modification of acrylic resin has attrac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/30C09D11/38
Inventor 张迎晨吴红艳
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager