Ceramic compound bonding agent bonded to metal

A ceramic composite and bonding agent technology, applied in metal processing equipment, abrasives, manufacturing tools, etc., can solve problems such as insufficient wear resistance, short dressing gap, and affecting production efficiency, and achieve good shape retention, improved processing efficiency, Good self-sharpening effect

Inactive Publication Date: 2014-12-03
QINGDAO QIANXIANG ENVIRONMENTAL PROTECTION TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the traditional resin diamond grinding wheel has good sharpness and good self-sharpening, it has low heat resistance, insufficient wear resistance and short dressing gap, which affects production efficiency; Although the diamond grinding wheel has good sharpness, it has poor wear resistance and is difficult to trim; although the metal diamond grinding wheel has good shape retention, its self-sharpening is not good, and it cann

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A ceramic composite binder combined with metal, characterized in that it includes the following parts by weight: 21 parts of ceramic powder, 14 parts of tin powder, 15 parts of iron ore, 5 parts of boron oxide, and 1 part of calcium oxide , 12 parts of burnt kaolin, 35-74 parts of hydrated aluminum hydroxide, 13.8 parts of active silica powder, 21 parts of raw kaolin, 45 parts of sandstone, 35 parts of bronze powder, 18 parts of boron carbide, and 41.8 parts of calcium stannate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a ceramic compound bonding agent bonded to metal. The agent is characterized by comprising substances in parts by weight as follows: 21-48 parts of ceramic powder, 10-34 parts of tin powder, 11-25 parts of iron ore, 5-13.8 parts of boron oxide, 1-8 parts of calcium oxide, 12-34 parts of calcined kaolin, 35-74 parts of algeldrate, 13.8-41.6 parts of active silica micro powder, 11-21 parts of raw kaolin, 30-45 parts of gravels, 11-35 parts of bronze powder, 4-18 parts of boron carbide and 13.6-41.8 parts of calcium stannate. The agent keeps the characteristics of the good sharpness and the good self-sharpening property of a ceramic bonding agent and has the advantages of the high rigidity and the good shape retention property of a metal bonding agent, so that the comprehensive processing efficiency is improved.

Description

technical field [0001] The invention relates to a ceramic composite binder combined with metal. Background technique [0002] Grinding wheel is the main tool for grinding, which is a porous object composed of abrasive and bonding agent. Diamond abrasives are used as raw materials, and metal powder, resin powder, and ceramics are used as binders respectively. The circular bonded abrasive with a through hole in the center is called a diamond grinding wheel. Due to the characteristics of diamond abrasives (high hardness, high compressive strength, and good wear resistance), diamond abrasives have become ideal tools for grinding hard and brittle materials and cemented carbide in grinding processing, and are widely used in processing low Metal and non-metal hard and brittle materials with iron content. [0003] With the development of science and technology, CNC ultra-precision grinding machines, high-speed and high-precision crankshaft grinding machines and camshaft grinding m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/04
Inventor 田福祯高伟张劭
Owner QINGDAO QIANXIANG ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products