A kind of aluminum oxide/zirconia composite ceramic nozzle and its manufacturing method

A ceramic nozzle and zirconia technology, applied in the field of nozzle molding, can solve the problems of backward production technology and preparation method, weak anti-corrosion and anti-erosion ability, and low ductility, etc., and achieve low price, high tensile strength, and ductility. good sex effect

Inactive Publication Date: 2017-01-04
刘莉莉
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since ceramic nozzles were introduced into China in the 1990s, the materials have been continuously improved and updated, gradually developing from oxide ceramics to nitride ceramics and carbide ceramics, but the production technology and preparation methods are backward, resulting in the existence of ceramic nozzles in the prior art. Many defects, such as low hardness, poor wear resistance, weak anti-corrosion and anti-erosion ability, low ductility, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The alumina / zirconia composite ceramic nozzle is characterized in that it is made of the following raw materials in parts by weight: alumina 75, zirconia 38, aluminum magnesium spinel 7, rutile 5, paraffin 2, sulfuric acid Cobalt 0.1, soft soil 3, hard soil 2, clay 4.8, nylon 12 0.9, palm oil 0.2, monoglyceride 6, ethylene glycol monobutyl ether 4, polyurethane resin emulsion 8, additive 4, appropriate amount of water.

[0014] The auxiliary agent is made of the following raw materials in parts by weight: polyvinyl alcohol 18, graphite powder 4, feldspar 2, coal gangue 6, acrylic acid 2.8, allyl polyethylene glycol 3.8, benzoyl peroxide 1.9, di Dibutyltin laurate 0.3, sodium hexametaphosphate 1, zinc sulfate 2, sodium selenite 0.4, nano-scale magnesium silicate 2, the preparation method is to crush feldspar and coal gangue to 120-150 mesh, add graphite powder, Stir and mix zinc sulfate, calcinate at 710-820°C for 2-3 hours, quench in water, then add acrylic acid, allyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alumina / zirconia composite ceramic nozzle, which is characterized in that it is made of the following raw materials in parts by weight: alumina 65-80, zirconia 32-45, aluminum magnesium spinel 4-8, Rutile 5‑8, Paraffin 1‑2, Cobalt Sulphate 0.1‑0.3, Soft Soil 3‑4, Hard Soil 2‑3, Clay 4.1‑5.7, Nylon 12 0.6‑0.9, Palm Oil 0.2‑0.4, Monoglyceride 6‑ 9. Ethylene glycol monobutyl ether 4-8, polyurethane resin emulsion 8-12, auxiliary agent 3-4, and appropriate amount of water; the preparation process of the present invention is simple, the yield is high, and the price is low, and the prepared ceramic nozzle has good ductility, Good wear resistance, strong corrosion resistance, high tensile strength, long service life, meet the various needs of different color sorters, and high color sorting efficiency.

Description

technical field [0001] The invention relates to a ceramic nozzle preparation process, which belongs to the technical field of nozzle molding, and in particular to an aluminum oxide / zirconia composite ceramic nozzle and a manufacturing method thereof. Background technique [0002] Since ceramic nozzles were introduced into China in the 1990s, the materials have been continuously improved and updated, gradually developing from oxide ceramics to nitride ceramics and carbide ceramics, but the production technology and preparation methods are backward, resulting in the existence of ceramic nozzles in the prior art. There are many defects, such as low hardness, poor wear resistance, weak anti-corrosion and anti-erosion ability, and low ductility. In order to overcome the shortcomings of the existing technology, it is necessary to improve the existing ceramic nozzle production technology, so as to produce ceramics with low cost, multiple functions, flame retardancy, high hardness, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/10C04B35/622
Inventor 夏建国
Owner 刘莉莉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products