A kind of powder coating for ship surface

A powder coating and ship technology, applied in the field of coatings, can solve the problems of affecting the speed of the ship, interfering with the performance of sonar reconnaissance, weakening the combat effectiveness of warships, etc., and achieve the effects of improving corrosion resistance, enriching corrosion-resistant functional groups, and excellent water and oil repellency.

Active Publication Date: 2017-12-19
ANHUI JINDUN PAINT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For ships, marine life greatly affects the speed of the ship. If marine life is attached to the sonar dome, it will interfere with the reconnaissance performance of the sonar and weaken the combat effectiveness of the warship.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of ship surface powder coating that the present invention proposes, its raw material comprises by weight: 75 parts of castor oil modified waterborne polyurethanes, 26 parts of epoxy resins, 8 parts of polytrifluorochloroethylene, 11 parts of hollow glass microspheres, super 14 parts of fine calcium carbonate, 5 parts of talc, 1 part of organic montmorillonite, 1.8 parts of titanate coupling agent KR-TTS, 0.5 parts of curing agent, 0.5 parts of antifungal agent, 23 parts of pigments, of which hollow glass microspheres It is 800 mesh, and the epoxy value of epoxy resin is 0.1 equivalent / 100 grams;

[0017] During the preparation process, superfine calcium carbonate, talcum powder, and organic montmorillonite were added to the mixer and mixed evenly, and then the titanate coupling agent KR-TTS was added, and stirred at a stirring speed of 145rpm for 31min to obtain a surface treatment filler; After the surface treatment filler, castor oil modified water-based polyur...

Embodiment 2

[0019] A kind of ship surface powder coating that the present invention proposes, its raw material comprises by weight: castor oil modified waterborne polyurethane 76 parts, epoxy resin 25 parts, polytrifluorochloroethylene 9 parts, hollow glass microsphere 10 parts, super 14.3 parts of fine calcium carbonate, 4.8 parts of talcum powder, 1.7 parts of organic montmorillonite, 1.7 parts of titanate coupling agent KR-TTS, 0.4 parts of curing agent, 0.6 parts of antifungal agent, 22 parts of pigments, of which hollow glass The beads are 750 mesh, and the epoxy value of the epoxy resin is 0.15 equivalent / 100 grams;

[0020] During the preparation process, superfine calcium carbonate, talcum powder, and organic montmorillonite were added to the mixer and mixed evenly, and then titanate coupling agent KR-TTS was added, and stirred at a stirring speed of 130rpm for 33min to obtain a surface treatment filler; After the surface treatment filler, castor oil modified water-based polyureth...

Embodiment 3

[0022] A kind of ship surface powder coating that the present invention proposes, its raw material comprises by weight: 78 parts of castor oil modified waterborne polyurethanes, 23 parts of epoxy resins, 11 parts of polytrifluorochloroethylene, 8 parts of hollow glass microspheres, super 15 parts of fine calcium carbonate, 4 parts of talcum powder, 3 parts of organic montmorillonite, 1.5 parts of titanate coupling agent KR-TTS, 0.2 parts of curing agent, 0.8 parts of antifungal agent, 20 parts of pigment, of which hollow glass microspheres It is 780 mesh, and the epoxy value of epoxy resin is 0.12 equivalent / 100 grams;

[0023] During the preparation process, superfine calcium carbonate, talcum powder, and organic montmorillonite were added to a mixer and mixed evenly, and then titanate coupling agent KR-TTS was added, and then stirred at a stirring speed of 150 rpm for 30 minutes to obtain a surface treatment filler; After the surface treatment filler, castor oil modified wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
epoxy valueaaaaaaaaaa
epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a powder coating for a ship surface. The powder coating comprises the raw materials in parts by weight: 75-78 parts of castor oil modified waterborne polyurethane, 23-26 parts of epoxy resin, 8-11 parts of polytrifluorochloroethylene, 8-11 parts of hollow glass microspheres, 14-15 parts of calcium carbonate superfine powder, 4-5 parts of talcum powder, 1-3 parts of organic montmorillonoid, 1.5-1.8 parts of a titanate coupling agent KR-TTS, 0.2-0.5 part of a curing agent, 0.5-0.8 part of a mildew preventive and 20-23 parts of a pigment. The powder coating is excellent in hydrophobicity, oleophobicity, dirt prevention property and corrosion resistance; marine organisms are difficultly to attach to the powder coating, and the powder coating is suitable for the use environment on the ship surface.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a powder coating for ship surfaces. Background technique [0002] Anti-fouling coatings are used to prevent the ship from being blocked by marine organisms and causing fouling when the ship is navigating in the ocean. Anti-fouling coatings can keep the water-soaked parts smooth and free of dirt. Antifouling coatings can be divided into: contact type, booster type, diffusion type, and self-throwing type. They are mainly used in antifouling projects such as ships, marine structures, and pipelines in seawater and fresh water. There are more than 18,000 species of organisms in sea areas around the world. It is an attached animal, and more than 600 kinds are attached plants. After marine organisms are attached to the bottom of the ship, the resistance will be increased, the speed will be reduced, the fuel consumption will increase, and the mechanical wear will increase. The adhesi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C09D163/00C09D127/12C09D5/03C09D5/16C09D5/08C09D7/12
CPCC08K2201/005C08L2205/03C09D5/03C09D7/62C09D7/70C09D175/14C08L63/00C08L27/12C08K13/06C08K9/04C08K7/28C08K2003/265C08K3/34C08K3/346
Inventor 梅长林朱恒衡张玉湘
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com