A kind of anti-icing paint and its preparation method and application

An anti-icing and coating technology, applied in chemical instruments and methods, coatings, other chemical processes, etc., can solve problems such as slow development speed and inability to meet requirements, achieve excellent chemical resistance, alleviate icing phenomenon, good hydrophobicity

Active Publication Date: 2017-06-27
NINGBO NOVO NEW MATER TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's wind power technology started relatively late, and wind power blade coating technology was initially imported from abroad, and the development speed was slow. However, with the vigorous development of my country's wind power industry, wind power blade coatings have also developed rapidly; patent CN103992707A discloses a high-performance wind power blade The protective coating and its preparation method use hydroxyacrylic resin as the main film-forming substance, but still cannot meet the requirements of the wind power industry for anti-icing of wind power blades and the like

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-icing paint and its preparation method and application
  • A kind of anti-icing paint and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation method of the anti-icing coating of embodiment 1 may further comprise the steps:

[0033] 1) Add 25g of rutile titanium dioxide, 20g of fluorosilicone resin ETERFLON 4263 (55±1% solid content, hydroxyl value 110±5) and 1.5g of dispersant BYK170 into 13g of butyl acetate solvent, and disperse by ball milling for 30min to obtain a ground color paste , Add 30g fluorosilicone resin ETERFLON 4263, 12g butyl acetate solvent, 0.1g defoamer BYK088, 0.1g leveling agent BYK399, 0.2g rheological additive BYK411, 1g light stabilizer Tinuvin123, 5g matting agent Mix OK500 and 0.1g drier dibutyltin dilaurate evenly, filter and package to obtain component A;

[0034] 2) Take 10g of N3390 curing agent, dilute with 10g of butyl acetate diluent, filter and package to obtain component B;

[0035] 3) The above-mentioned components A and B were mixed, and mechanically stirred to obtain the anti-icing coating of Example 1.

Embodiment 2

[0036] The preparation method of the anti-icing coating of embodiment 2 may further comprise the steps:

[0037] 1) Take 5g of nano-silica, 20g of rutile titanium dioxide, 20g of fluorosilicone resin ETERFLON 4263 (55±1% solid content, hydroxyl value 110±5) and 2g of dispersant TEGO Dispers 610 into 18g of butyl acetate solvent, Sand mill and disperse for 30 minutes to obtain a ground color paste, add 30g fluorosilicone resin ETERFLON 4263, 7g butyl acetate solvent, 0.1g defoamer BYK070, 0.1g leveling agent BYK310, 0.1g light stabilizer Tinuvin292, 0.2g to the color paste Rheological additive BYK405, 5g matting agent OK412 and 0.1g drier dibutyltin dilaurate, mixed evenly, filtered and packaged to obtain component A;

[0038] 2) Take 10g of N3390 curing agent, dilute with 10g of butyl acetate diluent, filter and package to obtain component B;

[0039] 3) The above-mentioned components A and B were mixed, and mechanically stirred to obtain the anti-icing coating of Example 2. ...

Embodiment 3

[0040] The preparation method of the anti-icing coating of embodiment 3 may further comprise the steps:

[0041] 1) Add 2g of nano-alumina and 0.1g of dispersant TEGO Dispers 610 to 10g of butyl acetate, and disperse for 30 minutes by ultrasonic to obtain a nano-alumina dispersion. Take 23g of rutile titanium dioxide, 1g of dispersant TEGO Dispers610, 20g of fluorine Silicone resin ETERFLON 4263 (55±1% solid content, hydroxyl value 110±5) was added to 15g of solvent butyl acetate, sand milled and dispersed for 15min to obtain a grinding paste, the above nano-zinc oxide dispersion, grinding paste, 30g of fluorine Silicone resin ETERFLON 4263, 0.1g defoamer BYK070, 0.3g leveling agent BYK300, 0.2g rheological additive BYK410, 0.1g light stabilizer Tinuvin5050, 5g matting agent OK520 and 0.1g drier stannous octoate, mix well Filter and pack to obtain A component;

[0042] 2) Take 10g of N3390 curing agent, dilute with 10g of butyl acetate diluent, filter and package to obtain co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
flash pointaaaaaaaaaa
flash pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-icing paint. The paint comprises a component A and a component B in a mass ratio of (4-7):1, wherein the component A is prepared from the following ingredients in percentage by mass: 20-80 percent of fluorosilicon resin with solid content of 20-70 percent, 0.05-2 percent of a defoaming agent, 0.05-2 percent of a flatting agent, 0.05-2 percent of a rheological agent, 0.05-5 percent of a light stabilizer, 0.05-2 percent of a matting agent, 0.05-2 percent of drier, 10-60 percent of rutile titanium dioxide, 0.1-20 percent of a dispersant and 20-70 percent of a solvent A; and the component B is prepared from the following ingredients in percentage by mass: 20-80 percent of a polyisocyanate curing agent and 20-80 percent of a solvent B. The anti-icing coating formed by the anti-icing paint has low surface energy and good hydrophobicity, can be used for effectively reducing the ice adhering strength of a base material, has excellent weather resistance and abrasion resistance, has high hardness and strong adhesive force to the base material, can be applied to wind blades, electric wires and cables and other cold surfaces with anti-icing requirement, and can be used for effectively relieving the icing phenomenon of cold surfaces, guaranteeing efficient working of the wind blades, the electric wires and cables and the like and prolonging the service lives of the wind blades, the electric wires and cables.

Description

technical field [0001] The invention relates to the technical field of coating chemical industry, in particular to an anti-icing coating and a preparation method and application thereof. Background technique [0002] The icing phenomenon of wind power, communication, electric power, aviation and transportation equipment brings a lot of inconvenience to people's production and life, and in severe cases will cause significant economic losses. Therefore, how to solve the problem of icing on the surface of key components has always been a research hotspot at home and abroad. . [0003] For example, wind energy, as a green, pollution-free and sustainable new energy source, has become an important part of human energy. The surface of wind turbine blades is very easy to freeze in winter, which affects the dynamic balance of wind turbines. However, wind turbine blades have high rotational speed and large centrifugal force. In the case of severe imbalance, the blades will break, cau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/08C09D7/12C09D5/00C09K3/18
Inventor 吕健勇王健君吴石军邵文义邵永明
Owner NINGBO NOVO NEW MATER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products