A kind of medium permittivity low-loss microwave dielectric ceramic and its preparation method

A microwave dielectric ceramic and electric constant technology, applied in the field of material science, can solve the problems of high sintering temperature or resonant frequency temperature coefficient, production and utilization limitations of microwave ceramic materials, low dielectric constant, etc. Good performance and easy operation

Active Publication Date: 2017-09-12
RES INST OF XIAN JIAOTONG UNIV & SUZHOU
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the microwave ceramic material system with medium dielectric constant mainly includes BaTi 4 o 9 / Ba 2 Ti 9 o 20 system, (Zr, Sn)TiO 4 、BiNbO 4 system, etc., but there are problems such as low relative permittivity (less than 40), high temperature coefficient of sintering temperature or resonance frequency, etc., which limit the production and utilization of microwave ceramic materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of medium permittivity low-loss microwave dielectric ceramic and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] According to the ceramic composition expression Zr 0.675 (Mg 1 / 3 Nb 2 / 3 ) 0.325 TiO 4 +0.2wt%MnCO 3 Weigh the raw material ZrO 2 , MgO, Nb 2 o 5 、TiO 2 and MnCO 3 , mixed thoroughly and ball milled at a speed of 200r / min for 4h, then dried at 120°C, passed through a 120-mesh sieve, and then pressed into pieces, kept at 1000°C in an air atmosphere for 4h to obtain a sample briquette; the sample was burned After the block is pulverized, carry out secondary ball milling, the ball milling time is 5h, and dry at 120°C, mix the powder with the aqueous solution of polyvinyl alcohol to make micron-sized spherical particles, pass through the 60-mesh and 120-mesh double-layer sieves Sieve to obtain the required ceramic material with 60 mesh to 120 mesh, press the ceramic material into shape, and sinter at 1280°C for 2 hours in air to obtain a medium dielectric constant and low loss microwave dielectric ceramic material.

[0030] The performance index of the tested ceram...

Embodiment 2

[0032] According to the ceramic composition expression Zr 0.675 (Mg 1 / 3 Nb 2 / 3 ) 0.325 TiO 4 +0.5wt%MnCO 3 Weigh the raw material ZrO 2 , MgO, Nb 2 o 5 、TiO 2 and MnCO 3 , mixed thoroughly and ball milled at a speed of 200r / min for 4h, then dried at 120°C, passed through a 120-mesh sieve, and then pressed into pieces, kept at 1000°C in an air atmosphere for 4h to obtain a sample briquette; the sample was burned After the block is pulverized, carry out secondary ball milling, the ball milling time is 5h, and dry at 120°C, mix the powder with the aqueous solution of polyvinyl alcohol to make micron-sized spherical particles, pass through the 60-mesh and 120-mesh double-layer sieves Sieve to obtain the required ceramic material with 60 mesh to 120 mesh, press the ceramic material into shape, and sinter at 1280°C for 2 hours in air to obtain a medium dielectric constant and low loss microwave dielectric ceramic material.

[0033] The performance index of the tested ceram...

Embodiment 3

[0035] According to the ceramic composition expression Zr 0.65 (Mg 1 / 3 Nb 2 / 3 ) 0.35 TiO 4 +0.2wt%MnCO 3 Weigh the raw material ZrO 2 , MgO, Nb 2 o 5 、TiO 2 and MnCO 3 , mixed thoroughly and ball milled at a speed of 200r / min for 4h, then dried at 120°C, passed through a 120-mesh sieve, and then pressed into pieces, kept at 1000°C in an air atmosphere for 4h to obtain a sample briquette; the sample was burned After the block is pulverized, carry out secondary ball milling, the ball milling time is 5h, and dry at 120°C, mix the powder with the aqueous solution of polyvinyl alcohol to make micron-sized spherical particles, pass through the 60-mesh and 120-mesh double-layer sieves Sieve to obtain the required ceramic material with 60 mesh to 120 mesh, press the ceramic material into shape, and sinter at 1260°C for 2 hours in air to obtain a microwave dielectric ceramic material with a medium dielectric constant and low loss.

[0036] The performance index of the tested ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality factoraaaaaaaaaa
resonant frequency temperature coefficientaaaaaaaaaa
relative permittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a microwave dielectric ceramic with medium dielectric constant and low loss. The composition expression of the ceramic is Zr(1-x)(Mg1 / 3Nb2 / 3)xTiO4+ywt%MnCO3, wherein 0.325≤x≤0.4, 0.2≤ y≤0.5, y is the mass percentage of MnCO3 in Zr(1-x)(Mg1 / 3Nb2 / 3)xTiO4, and the present invention also provides a method for preparing microwave dielectric ceramics with medium dielectric constant and low loss correspondingly. The medium dielectric constant and low loss microwave dielectric ceramics provided by the present invention have low sintering temperature, high relative permittivity and quality factor, and the temperature coefficient of resonance frequency is close to zero. This kind of ceramics can be used as radio frequency multilayer ceramic capacitors, Dielectric materials such as chip microwave dielectric resonators or filters, ceramic antennas, and multi-chip components.

Description

technical field [0001] The invention relates to the technical field of material science, in particular to a medium dielectric constant low-loss microwave dielectric ceramic and a preparation method thereof. Background technique [0002] Microwave dielectric ceramics is a new type of functional ceramic material developed in the past twenty years. It refers to a ceramic material used as a dielectric material in circuits in the microwave frequency band (mainly 300MHz to 300GHz frequency band) and fulfills one or more functions. It is a key material for the manufacture of microwave dielectric filters and resonators. This material is a new type of functional ceramic material developed with the rapid development of the mobile communication industry in recent decades. Its outstanding features are high dielectric constant, low loss, and small temperature coefficient of resonance frequency, and it is used to make dielectric materials. Microwave components such as resonators, dielect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/49C04B35/622C04B35/64
Inventor 周迪李文博庞利霞赵金雄
Owner RES INST OF XIAN JIAOTONG UNIV & SUZHOU