Environment-friendly antistatic polypropylene plastic inspection well material restored and modified by waste polypropylene molecular chain and preparation method for environment-friendly antistatic polypropylene plastic inspection well material

A waste polypropylene and polypropylene plastic technology, applied in the field of environmental protection antistatic polypropylene plastic inspection well materials and its preparation, polypropylene materials, can solve the problems of waste polypropylene plastic environmental pollution, waste of resources, etc., to solve environmental pollution and waste of resources, enhance safety issues, and enhance the effect of economic value

Inactive Publication Date: 2015-08-26
雷刚
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0017] The present invention specifically uses components such as waste polypropylene, molecular chain repairing agent, antistatic masterbatch, toughening agent, minerals, compatibilizer, etc., completely solves the environmental pollution and resource waste of waste polypropylene plastics, and further improves the waste polypropylene The economic value of propylene plastic improves the safety of plastic inspection wells in construction operations, and also greatly improves the cost performance of products, bringing good economic benefits to enterprises and increasing the comprehensive competitiveness of enterprises

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The environmentally friendly antistatic polypropylene plastic inspection well material of the present embodiment repaired and modified by the waste polypropylene molecular chain is composed of the following materials by weight percentage:

[0050] Waste polypropylene is 40% of waste washing machine bucket crushing material, and waste woven bag crushing material is 35.9%;

[0051] Molecular chain repair agent, 3%;

[0052] Antistatic masterbatch, 2%;

[0053] Toughening agent is polyethylene, 5%;

[0054] The mineral is talcum powder, 10%;

[0055] The compatibilizer is maleic anhydride grafted polypropylene, 3%,

[0056] Antioxidant is 1010, 0.1%, 168, 0.2%;

[0057] The light stabilizer is 944, 0.2%, 770, 0.2%;

[0058] The lubricant is polyethylene wax 0.4%.

[0059] Concrete preparation method comprises the following steps:

[0060] (1) Place a magnet frame at the feeding funnel of the single-screw extruder to carry out metal filtration on the waste p...

Embodiment 2

[0064] The environmentally friendly antistatic polypropylene plastic inspection well material of the present embodiment repaired and modified by the waste polypropylene molecular chain is composed of the following materials by weight percentage:

[0065] Waste polypropylene is 35% of waste bumper crushing material, and waste woven bag crushing material is 22.9%;

[0066] Molecular chain repair agent, 4%;

[0067] Antistatic masterbatch, 3%;

[0068] The toughening agent is ethylene-octene copolymer, 10%;

[0069] The mineral is calcium carbonate, 20%;

[0070] The compatibilizer is acrylic grafted polypropylene, 4%,

[0071] Antioxidant is 1010, 0.2%, 168, 0.2%;

[0072] The light stabilizer is 944, 0.15%, 770, 0.15%;

[0073] The lubricant is calcium stearate 0.4%.

[0074] The specific preparation method is the same as Example 1 of the present invention.

Embodiment 3

[0076] The environmentally friendly antistatic polypropylene plastic inspection well material of the present embodiment repaired and modified by the waste polypropylene molecular chain is composed of the following materials by weight percentage:

[0077] Waste polypropylene is 25% of waste bumper crushing material, and waste washing machine bucket crushing material is 14.8%;

[0078] Molecular chain repair agent, 5%;

[0079] Antistatic masterbatch, 4%;

[0080] Toughening agent is ethylene-butene copolymer, 15%;

[0081] The mineral is mica, 30%;

[0082] The compatibilizer is maleic anhydride grafted polypropylene, 5%,

[0083] Antioxidant is 1010, 0.2%, 168, 0.2%, DSTP, 0.2%;

[0084] The light stabilizer is 3808, 0.2%;

[0085] The lubricant is 0.4% ethylene bis stearic acid amide.

[0086] The specific preparation method is the same as Example 1 of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly antistatic polypropylene plastic inspection well material restored and modified by a waste polypropylene molecular chain and a preparation method for the environment-friendly antistatic polypropylene plastic inspection well material. The environment-friendly antistatic polypropylene plastic inspection well material consists of the following components in percentage by weight: 36.4-76.2% of waste polypropylene, 3-6% of a molecular chain restoration agent, 2-5% of antistatic master batch, 5-15% of a flexibilizer, 10-30% of minerals, 3-5% of a compatilizer, 0.2-0.6% of an antioxidant, 0.2-0.4% of a light stabilizer and 0.4-1.6% of a lubricant. The environment-friendly antistatic polypropylene plastic inspection well material has the advantage that the polypropylene plastic inspection well material which is excellent in mechanical performance, cold resistance, heat resistance and antistatic effect is prepared by adopting the components of waste polypropylene, the molecular chain restoration agent, the antistatic master batch, the flexibilizer, the minerals, the compatilizer and the like; the waste polypropylene plastic can be greatly recycled because of the preparation of the material, the environmental pollution because of the waste polypropylene plastic and the resource waste are effectively solved, and an electrostatic problem generated in mounting and transporting processes of the plastic inspection well is completely solved, so that the safety of the plastic inspection well in engineering operation is greatly improved.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a polypropylene material, in particular to an environment-friendly antistatic polypropylene plastic inspection well material repaired and modified by waste polypropylene molecular chains and a preparation method thereof. Background technique [0002] With the intensification of economic development and urbanization, the requirements for inspection well standards are getting higher and higher, and inspection wells have also developed from clay bricks, cement blocks, prefabricated concrete inspection wells to plastic inspection wells. Plastic inspection wells generally adopt one-time injection molding, which has fewer steps in the molding process, high output and stable quality. In 2006, my country issued the "Plastic Inspection Wells for Drainage in Construction Areas", which vigorously promoted the development of plastic inspection wells and gradually replaced traditional inspec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L23/08C08L51/06C08J3/22C08K13/02C08K5/098C08K5/20C08K3/34C08K5/134
CPCC08L23/12B29B9/06C08J3/226C08J2323/12C08J2423/12C08K2201/003C08L2201/04C08L2201/08C08L2205/025C08L2205/035C08L2207/20
Inventor 雷刚
Owner 雷刚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap