Low-expansion-rate waste tire rubber powder modified bamboo fiberboard and preparation method thereof

A waste tire rubber, low expansion rate technology, applied in the preparation of animal glue or gelatin, other rubber adhesives, adhesives, etc., to achieve good water and oil resistance, good aging resistance, good light fastness.

Inactive Publication Date: 2015-11-25
ANHUI BAIYI FURNITURE
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Treat waste rubber powder with alkali and compound it with wooden materials, which can improve the performances such as waterproof, shockproof, heat insulation and sound insulation of the material. There is no report on using waste rubber powder for bamboo fiberboard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A low expansion rate waste tire rubber powder modified bamboo fiber board, made of the following raw materials in parts by weight (kg): bamboo fiber 163, 0.2% sodium hydroxide solution, soybean protein isolate 16.4, preservative 1.5, waste tire rubber powder 7.5, ascorbyl palmitate 0.9, nano polytetrafluoroethylene 1.4, melamine cyanurate 1.7, isooctyl tin dimethyldithioglycolate 0.5.

[0017] The described low expansion rate waste tire rubber powder modified bamboo fiber board is characterized in that:

[0018] (1) Pass waste tire rubber powder through a 200-mesh sieve, mix it with 3 times the weight of 0.2% sodium hydroxide solution, stir at 50°C for 20 minutes, and then heat Under the condition of UV aging for 9 hours, and then condensed at 40 ℃ for 4 hours, the rubber powder is processed in this way for one week to obtain modified rubber powder;

[0019] (2) Take 160 parts by weight of 0.2% sodium hydroxide solution, mix and stir with soybean protein isolate, ascor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
tensile strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-expansion-rate waste tire rubber powder modified bamboo fiberboard. The low-expansion-rate waste tire rubber powder modified bamboo fiberboard is prepared by the following raw materials in parts by weight: 162-164 parts of bamboo fibers, a proper amount of 0.2% sodium hydroxide solution, 16.2-16.7 of soy isolate proteins, 1.5-1.6 of preservatives, 7-8 of waste tire rubber powder, 0.8-1 of ascorbyl palmitate, 1.3-1.6 of nanometer polytetrafluoroethylene, 1.5-1.8 of cyanuric acid melamine, and 0.4-0.6 of dimethyl dithioglycolic acid diisooctyl tin. The bamboo fiberboard uses the waste tire rubber powder for modifying, so that the board surface shows excellent hydrophobicity; and ascorbyl palmitate, nanometer polytetrafluoroethylene, cyanuric acid melamine and dimethyl dithioglycolic acid diisooctyl tin are used, so that the board is excellent in water and oil resistance, low in water expanding rate, excellent in ageing resistance, excellent in light resistance and suitable for manufacturing indoor and outdoor office furniture and floors.

Description

technical field [0001] The invention relates to the field of bamboo fiber board manufacturing, in particular to a low expansion rate waste tire rubber powder modified bamboo fiber board and a preparation method thereof. Background technique [0002] Fiberboard has uniform structure, smooth surface and good processability, so it is widely used in furniture manufacturing and construction. At present, the main raw materials for preparing fiberboard are wood fiber and urea-formaldehyde resin adhesive. With the excessive felling of forest resources, how to ensure sufficient supply of raw materials has become an important social and economic issue. In addition, urea-formaldehyde resin is derived from non-renewable petrochemical resources, and it is easy to release free formaldehyde in hot and humid environment, which seriously pollutes the environment and endangers human health. With the continuous rise of crude oil prices and people's increasing concern about their own and envi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/12B27N1/02C09J189/00C09J121/00C09J127/18C09J11/06
Inventor 张友吉
Owner ANHUI BAIYI FURNITURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap