POSS-block-containing acrylate copolymer super-hydrophobic coating and preparing method thereof

A super-hydrophobic coating and acrylate technology, applied in the field of polymer materials and surface science, to achieve excellent self-cleaning performance, excellent super-hydrophobic performance, and promote the development of surface roughness

Inactive Publication Date: 2015-12-09
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as far as the reports on the preparation of superhydrophobic coatings by spraying are concerned, their application objects are also limited to nanoparticle dispersions and multi-component polymer mixtures, and spraying a single-component solution of organic-inorganic hybrid polymers to prepare superhydrophobic coatings. layer has not seen any reports yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • POSS-block-containing acrylate copolymer super-hydrophobic coating and preparing method thereof
  • POSS-block-containing acrylate copolymer super-hydrophobic coating and preparing method thereof
  • POSS-block-containing acrylate copolymer super-hydrophobic coating and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] 1) Preparation of POSS-containing block acrylate copolymer

[0046] Preparation of POSS-containing acrylate block copolymers by atom transfer radical polymerization (ATRP): First, add 3.7mL methyl methacrylate (MMA), 6.2mL butyl acrylate (BA), 1.7mL to a 100mL reaction eggplant flask Hydroxyethyl methacrylate (HEMA), 7mL solvent cyclohexanone, 244μL ligand N,N,N',N",N"-pentamethyldiethylenetriamine (PMDETA), 102μL initiator a bromopropane Ethyl acid (EPN‐Br) and 0.0777g of catalyst cuprous chloride (CuCl), the reaction system was frozen-evacuated-thawing cycle in liquid nitrogen for 5 times to remove oxygen, and then the reaction system was under the protection of argon atmosphere at 70 ℃ The reaction was carried out at the temperature for 16 hours, and the obtained product was washed and precipitated with excess petroleum ether three times after cooling, and was dried in a vacuum oven for three days to constant weight, thereby obtaining a macromolecular initiator. 2.8...

Embodiment 2

[0059] 1) Preparation of POSS-containing block acrylate copolymer

[0060] Preparation of POSS-containing acrylate block copolymers by atom transfer radical polymerization (ATRP): First, add 3.7mL methyl methacrylate (MMA), 6.2mL butyl acrylate (BA), 1.7mL to a 100mL reaction eggplant flask Hydroxyethyl methacrylate (HEMA), 7mL solvent cyclohexanone, 491μL ligand N,N,N',N",N"-pentamethyldiethylenetriamine (PMDETA), 205μL initiator a bromopropane Ethyl acid (EPN-Br) and 0.1566g of catalyst cuprous chloride (CuCl), the reaction system was cooled in liquid nitrogen - vacuumed - thawed for 5 times to remove oxygen, and then the reaction system was under the protection of argon atmosphere at 70 ° C The reaction was carried out at the temperature for 16 hours, and the obtained product was washed and precipitated with excess petroleum ether three times after cooling, and was dried in a vacuum oven for three days to constant weight, thereby obtaining a macromolecular initiator. Disso...

Embodiment 3

[0070] 1) Preparation and characterization of POSS-containing block acrylate copolymer

[0071]Preparation of POSS-containing acrylate block copolymers by atom transfer radical polymerization (ATRP): First, add 3.7mL methyl methacrylate (MMA), 6.2mL butyl acrylate (BA), 1.7mL to a 100mL reaction eggplant flask Hydroxyethyl methacrylate (HEMA), 7mL solvent cyclohexanone, 146μL ligand N,N,N',N",N"-pentamethyldiethylenetriamine (PMDETA), 61μL initiator a bromopropane Acid ethyl ester (EPN‐Br) and 0.0466g of catalyst cuprous chloride (CuCl), the reaction system was frozen-evacuated-thawing cycle in liquid nitrogen for 5 times to remove oxygen, and then the reaction system was under the protection of argon atmosphere at 70 ℃ The reaction was carried out at the temperature for 16 hours, and the obtained product was washed and precipitated with excess petroleum ether three times after cooling, and was dried in a vacuum oven for three days to constant weight, thereby obtaining a macro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Contact angleaaaaaaaaaa
Static contact angleaaaaaaaaaa
Roll angleaaaaaaaaaa
Login to View More

Abstract

The invention discloses a POSS-block-containing acrylate copolymer super-hydrophobic coating and a preparing method thereof. The preparing method includes the steps of when preparing is carried out, pre-treating a base material; preparing a POSS-block-containing acrylate copolymer solution; spraying the prepared copolymer solution to the pre-treated base material, and obtaining the super-hydrophobic coating with the thickness of 10 micrometers to 200 micrometers. The POSS-block-containing acrylate copolymer super-hydrophobic coating is independently made of POSS-block-containing acrylate copolymers, the static water contact angle of the coating is larger than 150 degrees, the rolling angle is smaller than 8 degrees, and the grade of the adhesive force of the coating is the zero grade or the first grade. The super-hydrophobic coating and the preparing method have the advantages that an operation technology is simple, and cost is quite low; in addition, the operation environment is friendly, raw materials are easy to get, and industrial large-scale production is facilitated.

Description

technical field [0001] The invention relates to a superhydrophobic coating, in particular to a superhydrophobic coating containing a POSS block acrylate copolymer and a preparation method thereof, belonging to the field of polymer materials and surface science. Background technique [0002] Superhydrophobic coating refers to a type of coating with a static contact angle of more than 150° to water and a rolling angle of less than 10°. This coating has broad application prospects in the fields of self-cleaning, oil-water separation, and anti-icing. [0003] Inspired by the lotus leaf effect, the preparation of superhydrophobic coatings needs to meet two conditions, namely micro-nano composite rough structure and low surface energy substances. Fluorine-containing substances, especially those containing fluorocarbon long-chain structures, are widely used to modify surfaces because of their extremely low surface energy to achieve the purpose of obtaining low surface energy coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D153/00C09D5/16C08F293/00C03C17/30
Inventor 皮丕辉王鹏侯昆文秀芳徐守萍程江
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com