A kind of sealing glue for zinc-manganese battery and preparation method thereof

A zinc-manganese battery and sealing glue technology, which is applied to dry batteries, battery pack parts, circuits, etc., can solve the problems of easy aging, poor sealing performance, etc., and achieve easy coating, long service life and good adhesion Effect

Active Publication Date: 2019-10-01
深圳市天宁达胶粘技术有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a sealing glue for zinc-manganese batteries and a preparation method thereof, which solves the problems of poor sealing performance, easy aging and short service life of zinc-manganese batteries in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sealing glue for zinc-manganese battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A method for preparing a sealant for a zinc-manganese battery of the present invention includes the following steps: 1) heating 40 parts by weight of asphalt at 150°C for 2 hours, adding 20 parts by weight of hydrogenated saturated polybutene, 30 parts by weight of modified epoxy resin, 20 parts by weight of nonylphenol polyoxyethylene ether, 1 part by weight of nano-titanium dioxide and 1 part by weight of nano-flaky aluminum powder, and stir evenly to obtain a crude product; 2) to be obtained in step 1) When the temperature of the crude product is cooled to 80°C, add 20 parts by weight of No. 120 solvent gasoline, 10 parts by weight of aromatic hydrocarbon oil and 20 parts by weight of simethicone oil, stir evenly, filter and pack to obtain the product.

Embodiment 2

[0014] A method for preparing a sealant for a zinc-manganese battery of the present invention includes the following steps: 1) heating 45 parts by weight of asphalt at 180°C for 3 hours, and adding 25 parts by weight of hydrogenated saturated polybutene, 35 parts by weight of modified epoxy resin, 25 parts by weight of nonylphenol polyoxyethylene ether, 3 parts by weight of nano-titanium dioxide and 3 parts by weight of nano-flaky aluminum powder, and stir evenly to obtain a crude product; 2) to be obtained in step 1) When the temperature of the crude product is cooled to 100°C, add 25 parts by weight of No. 120 solvent gasoline, 15 parts by weight of aromatic oil and 15 parts by weight of simethicone oil, stir evenly, filter, and pack to obtain the product.

Embodiment 3

[0016] A method for preparing a sealant for a zinc-manganese battery of the present invention includes the following steps: 1) heating 50 parts by weight of asphalt at 200°C for 5 hours, adding 30 parts by weight of hydrogenated saturated polybutene, 40 parts by weight of modified epoxy resin, 30 parts by weight of nonylphenol polyoxyethylene ether, 5 parts by weight of nano-titanium dioxide and 5 parts by weight of nano-flaky aluminum powder, and stir evenly to obtain a crude product; 2) to be obtained in step 1) When the temperature of the crude product is cooled to 120°C, add 30 parts by weight of No. 120 solvent gasoline, 20 parts by weight of aromatic hydrocarbon oil and 20 parts by weight of simethicone oil, stir evenly, filter and pack to obtain the product.

[0017] Three kinds of sealants for zinc-manganese batteries obtained in Examples 1 to 3 and a certain commercially available sealant for zinc-manganese batteries were tested for performance with reference to the re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sealing glue for a zinc-manganese battery and a preparation method thereof, belonging to the technical field of battery sealing materials. The sealant for zinc-manganese batteries of the present invention comprises the following raw materials in parts by weight: 20-30 parts of hydrogenated saturated polybutene, 30-40 parts of modified epoxy resin, 40-50 parts of asphalt, 20-30 parts of 120 solvent gasoline, 10-20 parts of aromatic hydrocarbon oil, 20-30 parts of nonylphenol polyoxyethylene ether, 10-20 parts of dimethyl silicone oil, 1-5 parts of nano-titanium dioxide, 1-5 parts of nano-flaky aluminum powder; the present invention also provides The preparation method of the above-mentioned sealing glue for zinc-manganese batteries. The sealing glue for zinc-manganese batteries of the present invention has good cohesiveness, sealing performance and creep resistance performance, and also has aging resistance performance, high temperature stability and temperature sensitivity; Good adhesion, no cracking, easy to paint, no peculiar smell, long service life.

Description

technical field [0001] The invention belongs to the technical field of zinc-manganese battery sealing materials, in particular to a sealing glue for zinc-manganese batteries and a preparation method thereof. Background technique [0002] The zinc-manganese battery is a primary battery with manganese dioxide as the positive electrode, zinc as the negative electrode, and ammonium chloride aqueous solution as the main electrolyte. It is commonly known as a dry battery and is also called a Leclanche battery in academia. Zinc-manganese batteries are also called alkaline dry batteries, alkaline zinc-manganese batteries, and alkaline manganese batteries. If the sealing performance of the zinc-manganese battery is not good, the water in the electrolyte will volatilize and affect the normal operation of the battery; at the same time, the oxygen in the air will also enter the interior of the battery to oxidize the zinc and reduce the service life of the battery. It can be seen that t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J195/00C09J163/00C09J123/20C09J171/02C09J183/04C09J11/04H01M2/08H01M6/06H01M50/184H01M50/186H01M50/195
Inventor 苏建丽
Owner 深圳市天宁达胶粘技术有限公司