Water-based quick-drying primer-topcoat acrylic anti-corrosion paint and preparation method thereof

A technology of water-based acrylic and anti-corrosion coatings, applied in the direction of anti-corrosion coatings, coatings, etc., can solve problems such as toxicity, pollution, human health and environmental pollution

Inactive Publication Date: 2016-02-17
JIANGSU MARINE VICTORY COATING
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these additives are poisonous in themselves, posing serious pollution and threats to human health and the environment
At present, most acrylic paints are solvent-based, and the pollution is serious, so water-based resin paints have become a research hotspot in various countries.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based quick-drying primer-topcoat acrylic anti-corrosion paint and preparation method thereof
  • Water-based quick-drying primer-topcoat acrylic anti-corrosion paint and preparation method thereof
  • Water-based quick-drying primer-topcoat acrylic anti-corrosion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a water-based quick-drying bottom surface-integrated acrylic anticorrosive paint, the components of which are calculated in parts by mass as follows:

[0025]

[0026]

[0027] The preparation steps are as follows:

[0028] Step (1): Add deionized water, wetting agent, dispersant, anti-flash rust agent, defoamer and 28 parts of quick-drying water-based acrylic resin into the disperser according to the preset mass ratio, and set the disperser speed to 200r / min,

[0029] Step (2): Add rutile titanium dioxide, water-based zinc phosphate, water-based aluminum tripolyphosphate, iron oxide yellow, phthalocyanine green, carbon black in sequence, at a medium speed of 900r / min, stirring time 35~45min, and send to the sand mill Disperse to fineness ≤25um;

[0030] Step (3): adding 20 parts of quick-drying water-based acrylic resin and thickener to the mixing tank for mixing paint and dispersing, the dispersion speed is 600r / min, the temperature in the tank is 6...

Embodiment 2

[0033] This embodiment provides a water-based quick-drying bottom surface-integrated acrylic anticorrosive paint, the components of which are calculated in parts by mass as follows:

[0034]

[0035]

[0036] The preparation steps are as follows:

[0037] Step (1): Add deionized water, wetting agent, dispersant, anti-flash rust agent, defoamer and 33 parts of quick-drying water-based acrylic resin into the disperser according to the preset mass ratio, and set the disperser speed to 200r / min,

[0038] Step (2): Add rutile titanium dioxide, water-based zinc phosphate, water-based aluminum tripolyphosphate, iron oxide yellow, phthalocyanine green, carbon black in sequence, at a medium speed of 900r / min, stirring time 35~45min, and send to the sand mill Disperse to fineness ≤25um;

[0039] Step (3): adding 20 parts of quick-drying water-based acrylic resin and thickener to the mixing tank for mixing paint and dispersing, the dispersion speed is 600r / min, the temperature in the tank is 6...

Embodiment 3

[0042] This embodiment provides a water-based quick-drying bottom surface-integrated acrylic anticorrosive paint, the components of which are calculated in parts by mass as follows:

[0043]

[0044] The preparation steps are as follows:

[0045] Step (1): Add deionized water, wetting agent, dispersant, anti-flash rust agent, defoamer and 35 parts of quick-drying water-based acrylic resin into the disperser according to the preset mass ratio, and set the disperser speed to 200r / min,

[0046] Step (2): Add rutile titanium dioxide, water-based zinc phosphate, water-based aluminum tripolyphosphate, iron oxide yellow, phthalocyanine green, carbon black in sequence, at a medium speed of 900r / min, stirring time 35~45min, and send to the sand mill Disperse to fineness ≤25um;

[0047] Step (3): adding 20 parts of quick-drying water-based acrylic resin and thickener to the mixing tank for mixing paint and dispersing, the dispersion speed is 600r / min, the temperature in the tank is 60-75°C, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses water-based quick-drying primer-topcoat acrylic anti-corrosion paint. The paint comprises water-based acrylic resin, rutile type titanium dioxide, water-based aluminium tripolyphosphate, an anti-rust pigment, LT bentonite, phthalocyanine green, iron oxide yellow, deionized water, carbon black and an aid; the deionized water, a wetting agent, a dispersing agent, a defoaming agent and a flash rusting resisting agent are added to a dispersing machine in the preset mass ratio, the rutile type titanium dioxide, the water-based aluminium tripolyphosphate, water-based zinc phosphate, the LT bentonite, the phthalocyanine green and the iron oxide yellow are added sequentially, the water-based acrylic resin is added and sent into a stirring kettle to be heated and dispersed at the high speed, and when the temperature in the kettle is 40 DEG C, a coalescing agent and a thickening agent are added for full mixing. The water-based quick-drying primer-topcoat acrylic anti-corrosion paint is safe and environment-friendly, physical, chemical and construction properties of the water-based quick-drying primer-topcoat acrylic anti-corrosion paint are obviously better than those of existing paint, surface drying is realized within 10 min without heating of a film, curing is realized within 2 h, and the paint is best applicable to high-yield production chain procedure process coating.

Description

Technical field [0001] The invention belongs to the technical field of coatings, and relates to a protective coating and a preparation method thereof, in particular to a water-based quick-drying bottom surface integrated acrylic anticorrosive coating and a preparation method thereof. Background technique [0002] Quick-drying waterborne acrylic resin has the advantages of low VOC content, no peculiar smell, non-combustible and low toxicity. It has many varieties and excellent performance. It is widely used in paint production. Because water-based paints have gradually replaced organic solvent-based paints. However, water-based coatings also have high electrical conductivity, which is easy to cause metal corrosion, and flash rust is easy to occur during the drying process of the coating. Therefore, it is often necessary to add rust inhibitors to water-based paints for metals. In order to achieve a good anti-corrosion effect, the traditional method is to add anti-corrosion agents ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/08C09D7/12
Inventor 陈廷生
Owner JIANGSU MARINE VICTORY COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap