Tough heat-conductive antibacterial non-stick coating

A non-stick coating, tough technology, used in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of easy cracking of the coating film, poor wear resistance, affecting the long-term use of products, etc. , to achieve the effect of excellent mechanical and thermal comprehensive performance

Inactive Publication Date: 2016-02-24
无锡大塘复合材料有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing ceramic coatings for cooking utensils that meet FDA food safety requirements have the following disadvantages: 1. The coating film is prone to cracking, especially in light-colored products; 2. The wear resistance is not good, affecting Long-lasting use of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of tough heat conduction antibacterial non-stick coating is made up of the following raw materials by weight:

[0013] 2 parts of graphene powder; nano-SiO 2 20 parts of dispersion liquid; 15 parts of alumina sol; 15 parts of zirconia sol; 4 parts of bentonite; 3 parts of iron oxide black; 10 parts of polyimide; 50 parts of polytetrafluoroethylene water-based resin; 8 parts of polyester modified epoxy resin; 3 parts of fluorosilicone oil; 2 parts of silver nitrate; 2 parts of aluminum nitrate; 5 parts of ethylene glycol butyl ether.

Embodiment 2

[0015] A kind of tough heat conduction antibacterial non-stick coating is made up of the following raw materials by weight:

[0016] 1 part of graphene powder; nano-SiO 2 10 parts of dispersion liquid; 10 parts of alumina sol; 10 parts of zirconia sol; 2 parts of bentonite; 1 part of iron oxide black; 8 parts of polyimide; 30 parts of polytetrafluoroethylene water-based resin; 5 parts of polyester modified epoxy resin; 1 part of fluorosilicone oil; 1 part of silver nitrate; 1 part of aluminum nitrate; 3 parts of ethylene glycol butyl ether.

Embodiment 3

[0018] A kind of tough heat conduction antibacterial non-stick coating is made up of the following raw materials by weight:

[0019] 1.5 parts of graphene powder; nano-SiO 2 15 parts of dispersion liquid; 12 parts of alumina sol; 12 parts of zirconia sol; 3 parts of bentonite; 2 parts of iron oxide black; 9 parts of polyimide; 40 parts of polytetrafluoroethylene water-based resin; 7 parts of polyester modified epoxy resin; 2 parts of fluorosilicone oil; 1.5 parts of silver nitrate; 1.5 parts of aluminum nitrate; 4 parts of ethylene glycol butyl ether.

[0020] The parts of each of the above raw materials are parts by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tough heat-conductive antibacterial non-stick coating which is prepared from, by weight, 1-2 parts of graphene powder, 10-20 parts of nano SiO2 dispersion liquid, 10-15 parts of aluminum oxide sol, 10-15 parts of zirconium oxide sol, 2-4 parts of bentonite, 1-3 parts of black iron oxide, 8-10 parts of polyimide, 30-50 parts of polytetrafluoroethylene water-based resin, 5-20 parts of acrylic acid, 5-8 parts of water-soluble polyester modified epoxy resin, 1-3 parts of fluorosilicone oil, 1-2 parts of silver nitrate, 1-2 parts of aluminum nitrate and 3-5 parts of butyl cellosolve. The coating is good in ductility, high in toughness, resistant to wear, not prone to cracking and high in heat conductivity, has the antibacterial function and can be widely applied to kitchen cookware and tableware.

Description

technical field [0001] The invention relates to the technical field of coatings for kitchen utensils, in particular to a tough, heat-conducting, antibacterial and non-stick coating applicable to cooking utensils such as frying pans and baking pans and a preparation method thereof. Background technique [0002] At present, there are two main types of non-stick coatings commonly used in the market, one is fluorine coatings based on polytetrafluoroethylene (PTFE), such as Teflon; the other is based on silica sol and alkoxy Silane monomers are ceramic coatings prepared by sol-gel method (sol-gel). The inorganic nano-coating prepared by sol-gel technology overcomes the problems of poor temperature resistance, flame resistance and hardness of traditional organic coatings, and it has the characteristics of inorganic materials such as thermal stability, wear resistance, scratch resistance and non-combustibility. The coating of this system mainly uses water as a solvent, and there i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/14C09D7/12
Inventor 陈云
Owner 无锡大塘复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com