High-cost-performance and high-stain-resistance elastic flat-coating emulsion paint and preparation method thereof

A cost-effective latex paint technology, applied in latex paint, antifouling/underwater paint, coating, etc., can solve the problems of complex preparation methods, inability to have high stain resistance and high elasticity at the same time, and achieve easy mass production , The preparation method is simple and fast, and the effect of cheap cost

Inactive Publication Date: 2016-04-06
SKSHU PAINT
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a high cost performance, high stain resistance elastic flat latex paint and a preparation method thereof, which overcomes the disadvantages that the existing elastic flat latex paint cannot have high stain resistance and high elasticity at the same time, and the preparation method is complicated. At the same time achieve high stain resistance (stain resistance 2.5MPa, elongation at break at room temperature> 300%, elongation at break at low temperature> 80%), defoaming Excellent, and the advantages of low cost, high cost performance, and simple preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-cost-performance and high-stain-resistance elastic flat-coating emulsion paint and preparation method thereof
  • High-cost-performance and high-stain-resistance elastic flat-coating emulsion paint and preparation method thereof
  • High-cost-performance and high-stain-resistance elastic flat-coating emulsion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A high performance-price ratio and high stain-resistant elastic flat latex paint, which comprises the following components in parts by weight:

[0056]

[0057] Among them, 800 mesh heavy calcium carbonate and calcined kaolin are used as fillers.

[0058] The preparation method of the high cost performance and high stain resistance elastic flat latex paint comprises the following steps carried out in sequence:

[0059] ①At a speed of 500rpm, add cellulose to the water for mixing and disperse for 15 minutes;

[0060] ②Add 2-amino-2-methyl-1-propanol, polyacrylate ammonium salt dispersant, polyhydroxyalkyl ether nonionic wetting agent, ethyl alcohol to the mixture prepared in step ① at a speed of 800rpm Glycol, phosphate ester surfactant, mineral oil defoamer, titanium dioxide, 800 mesh ground calcium carbonate and calcined kaolin are mixed, and then the speed is increased to 1500rpm, and the mixture is dispersed to a fineness of ≤60μm at this speed, Wherein, the con...

Embodiment 2

[0063] A high performance-price ratio and high stain-resistant elastic flat latex paint, which comprises the following components in parts by weight:

[0064]

[0065]

[0066] Among them, 800 mesh heavy calcium carbonate, calcined kaolin and mica powder are used as fillers.

[0067] The preparation method of the high cost performance and high stain resistance elastic flat latex paint comprises the following steps carried out in sequence:

[0068] ①At a speed of 800rpm, add cellulose to the water for mixing and disperse for 8 minutes;

[0069] ②At the speed of 1200rpm, add pH regulator, polycarboxylate sodium salt dispersant, wetting agent, propylene glycol, water-based silicone defoamer, titanium dioxide, 800 mesh weight Calcium carbonate, calcined kaolin and mica powder are mixed, and then the speed is increased to 1800rpm, and the mixture is dispersed to a fineness of ≤60μm at this speed, and the amount of water-based silicone defoamer is 1 / 2 of its total weight ; ...

Embodiment 3

[0072] A high performance-price ratio and high stain-resistant elastic flat latex paint, which comprises the following components in parts by weight:

[0073]

[0074]

[0075] Among them, 800 mesh heavy calcium carbonate, calcined kaolin and precipitated barium sulfate are used as fillers.

[0076] The preparation method of the high cost performance and high stain resistance elastic flat latex paint comprises the following steps carried out in sequence:

[0077] ①At a speed of 600rpm, add cellulose to the water for mixing and disperse for 13 minutes;

[0078] ②At a speed of 1000rpm, add a pH regulator, a mixture of polyacrylic acid ammonium salt dispersant and polycarboxylate sodium salt dispersant, wetting agent, antifreeze, wetting antifreeze, mineral oil to the mixture prepared in step ① in sequence The mixture of antifoaming agent and water-based silicone antifoaming agent, titanium dioxide, and fillers are mixed, and then the speed is increased to 1600rpm, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to high-cost-performance and high-stain-resistance elastic flat-coating emulsion paint. The emulsion paint is prepared from water, cellulose, a pH regulating agent, a dispersing agent, a wetting agent, a wetting anti-freezing agent, an anti-freezing agent, a defoaming agent, titanium dioxide, filler, ultraviolet crosslinking type elastic emulsion, a water-based paint enhancing agent, sterilization preservatives, a mould-preventing agent and other thickening agents except cellulose, wherein the filler is prepared from one or any combination of heavy calcium carbonate, calcined kaolin, precipitated barium sulfate, talcum powder and mica powder. The emulsion paint overcomes the defects that existing elastic flat-coating emulsion paint cannot have high stain resistance and high elasticity at the same time, and a preparation method is complicated, and has the advantages that high stain resistance (stain resistance is smaller than 15%) and high elasticity (room-temperature tensile strength is larger than 2.5 MPa, normal-temperature break elongation is larger than 300%, and low-temperature break elongation is larger than 80%) are achieved at the same time, defoaming performance is excellent, manufacturing cost is low, cost performance is high, and the preparation method is simple and convenient.

Description

technical field [0001] The invention relates to a cost-effective, highly stain-resistant elastic flat-coated latex paint and a preparation method thereof, which are applied in the field of water-based paints for architectural decoration. Background technique [0002] At present, the base material of the exterior wall of buildings is generally cement-based. After being affected by factors such as environment, temperature and humidity changes, the wall is extremely prone to tiny cracks. This not only destroys the beauty of the wall, but also easily erodes the internal wall. [0003] Elastic latex paint is divided into two types: elastic flat coating and elastic napping. The elastic flat latex paint is a thin coating (the dry film thickness of the coating film is about 60um), and the coating film is flat and smooth; while the elastic brushed latex paint is a thick coating (the film thickness is about 300um), and the coating film is flat and smooth. The membrane is three-dimen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/02C09D201/00C09D7/12C09D5/16C09D5/14
CPCC09D201/00C08L2205/02C08L2205/035C09D5/02C09D5/14C09D5/1656C09D7/61C09D7/63C09D7/65
Inventor 洪杰张仁波赖李芳周龙生陆燕凤
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap