High-temperature resisting, abrasion resisting, corrosion resisting and cavitation resisting nickel-chromium-chromium carbide composite powder and coating and preparing method of coating

A technology of composite powder and chromium carbide, which is applied in coating, metal material coating process, molten spraying, etc., can solve the problems of weak corrosion resistance, poor anti-cavitation protection effect, and inability to adapt to the use requirements, etc., and achieve high Improvement of corrosion resistance, corrosion resistance and cavitation resistance, good solid solution strengthening effect

Active Publication Date: 2016-04-06
MIN OF WATER RESOURCES HANGZHOU MACHINERY DESIGN INST
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with electroplating hard chromium, electroplating NiP, anodic oxidation, etc., the corrosion resistance of nickel-chromium-chromium carbide coatings is relatively weak, especially in some strong corrosive media, such as chloride ions, nitrate ions and other environments. Corrosion resistance is weak, unable to meet the needs of higher use requirements
At the same time, in the turbulent and turbulent water environment, the anti-cavitation protection effect of nickel-chromium-chromium carbide is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Cr powder with a particle size of 5~45μm is used 3 C 2 Ceramic powder, NiCr alloy powder with a particle size of 5-45 μm, pure Nb metal powder with a particle size of 10-55 μm and pure Ta powder with a particle size of 10-55 μm are used as spraying materials, of which Cr 3 C 2 : 70wt%, NiCr: 23wt%, Nb: 3.5wt%, Ta: 3.5wt%. And the powder was mixed in a ball mill for 12 hours to realize the homogenization of the composite powder.

[0022] Lay the composite powder flat and put it in an incubator for drying. The holding temperature is 75°C and the drying time is 3 hours.

[0023] Clean the surface of the 0Cr13Ni5Mo stainless steel sprayed substrate with acetone, and dry it in an incubator at 40°C to remove the oily dirt on the surface. It was blasted using the aerodynamic blasting method described above.

[0024] The composite powder in this example is sprayed by supersonic flame, the kerosene flow rate is 27L / h, the kerosene pressure is 1.6MPa, the oxygen flow rate is...

Embodiment 2

[0027] Cr powder with a particle size of 5~45μm is used 3 C 2 Ceramic powder, NiCr alloy powder with a particle size of 5-45 μm, pure Nb metal powder with a particle size of 10-55 μm and pure Ta powder with a particle size of 10-55 μm are used as spraying materials, of which Cr 3 C 2 : 75wt%, NiCr: 20wt%, Nb: 1.5wt%, Ta: 3.5wt%. And the powder was mixed in a ball mill for 15 hours to realize the homogenization of the composite powder.

[0028] Lay the composite powder flat and put it in an incubator for drying. The holding temperature is 85°C and the drying time is 2.5 hours.

[0029] Clean the surface of the ZG06Cr13Ni4Mo stainless steel spray-coated substrate with alcohol, and dry it in an incubator at 45°C to remove oil stains on the surface. Sandblasting is performed in the above manner.

[0030] The composite powder in this example is sprayed with high-enthalpy plasma, the power of the spray gun is 85kW, the flow rate of argon gas is 250SCFH (cubic feet per hour), the ...

Embodiment 3

[0033] Cr powder with a particle size of 5~45μm is used 3 C 2 Ceramic powder, NiCr alloy powder with a particle size of 5-45 μm, pure Nb metal powder with a particle size of 10-55 μm and pure Ta powder with a particle size of 10-55 μm are used as spraying materials, of which Cr 3 C 2 : 85wt%, NiCr: 12wt%, Nb: 2wt%, Ta: 1wt%. And the powder was mixed in a ball mill for 14 hours to realize the homogenization of the composite powder.

[0034] Lay the composite powder flat and put it in an incubator for drying. The holding temperature is 90°C and the drying time is 2 hours.

[0035] Clean the surface of the 0Cr13Ni5Mo stainless steel spray-coated substrate with alcohol, and dry it in an incubator at 50°C to remove oil stains on the surface. Sandblasting is carried out in the manner described above.

[0036] The composite powder in this example is sprayed with supersonic flame, the kerosene flow rate is 28L / h, the kerosene pressure is 1.7MPa, the oxygen flow rate is 880L / min, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-temperature resisting, abrasion resisting, corrosion resisting and cavitation resisting nickel-chromium-chromium carbide composite powder and a high-temperature resisting, abrasion resisting, corrosion resisting and cavitation resisting nickel-chromium-chromium carbide coating prepared through the composite powder. The composite powder comprises, by weight percentage, 65-85% of Cr3C2, 10-25% of NiCr, 1-5% of Nb and 1-5% of Ta. The coating is prepared in the manner that the composite powder is subjected to hypersonic flame spraying or high-enthalpy plasma spraying or is subjected to hypersonic flame spraying or high-enthalpy plasma spraying, and then the high-enthalpy plasma remelting technology is combined. The coating is greatly improved in the aspects of microhardness, combing strength, corrosion resistance and cavitation resistance. Meanwhile, the production cost is low, the preparing method is reliable in technology, performance is stable, and the coating is suitable for being applied to the fields such as hydraulic machine flow passage components, compressor screws and turbine blades on a large scale.

Description

technical field [0001] The invention relates to a nickel-chromium-chromium carbide composite powder and its coating, in particular to a nickel-chromium-chromium carbide composite powder containing Nb and Ta which are resistant to high temperature, wear, corrosion and cavitation, and its coating and coating. its preparation method. Background technique [0002] Wear, corrosion, cavitation, etc. are the main reasons for the surface failure of mechanical workpieces, which in turn lead to premature scrapping of many mechanical parts, resulting in huge economic losses and waste of resources. In order to improve the anti-corrosion, anti-wear and anti-cavitation ability of the surface of mechanical workpieces, the surface treatment technology is mainly used to strengthen the surface, such as electroplating hard chrome on the surface of piston rod alloy steel, anodic oxidation on the surface of aluminum alloy materials, and coating on the surface of stainless steel of water turbin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C4/06C23C4/129C23C4/134
CPCC23C4/06
Inventor 吴燕明陈小明周夏凉赵坚方勇毛鹏展伏利
Owner MIN OF WATER RESOURCES HANGZHOU MACHINERY DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap