A kind of anti-yellowing unsaturated polyester resin and its synthetic method

A polyester resin, unsaturated technology, applied in the field of macromolecule chemistry, can solve the problems of product surface pulverization, loss of use function, structural damage, etc., achieve good yellowing resistance and weather resistance, expand the scope of use, and improve yellowing resistance The effect of changing abilities

Active Publication Date: 2018-06-15
广东百汇达新材料有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cured products of this general-purpose unsaturated resin are prone to yellowing when subjected to ultraviolet light, high temperature, oxygen, rain, etc. In severe cases, the surface of the product will be pulverized, the structure will be damaged, and the function will be lost, which limits the application of the resin within a certain range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-yellowing unsaturated polyester resin and its synthetic method
  • A kind of anti-yellowing unsaturated polyester resin and its synthetic method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] formula:

[0013] Reaction kettle formula: antioxidant 1g, adipic acid 290g, maleic anhydride 590g, neopentyl glycol 150g, ethylene glycol 190g, propylene glycol 300g, polymerization inhibitor methyl hydroquinone 0.2g;

[0014] Dilution kettle recipe: 500g styrene, 80g methyl methacrylate, 0.8g paraffin, 0.3g copper naphthenate, 2g light stabilizer.

[0015] Preparation Process:

[0016] Check and confirm whether the equipment, electrical appliances, instruments, valves and raw materials are normal, and put other reaction kettle formula raw materials into the reaction pot according to the recipe, except for the polymerization inhibitor methyl hydroquinone, and raise the temperature after feeding the materials, and the temperature of the raw materials will rise Supply nitrogen to 145°C (speed 0.5m 3 / h), horizontal condenser water supply, when the material temperature rises to 150°C, start stirring, when the distillation temperature rises to 98°C vertical condenser wat...

Embodiment 2

[0018] formula:

[0019] Reaction kettle formula: antioxidant 0.8g, adipic acid 438g, maleic anhydride 490g, neopentyl glycol 150g, ethylene glycol 190g, propylene glycol 300g, polymerization inhibitor methyl hydroquinone 0.2g;

[0020] Dilution kettle recipe: 500g styrene, 0.3g copper naphthenate, 0.8g paraffin, 80g methyl methacrylate, 2g light stabilizer.

[0021] Preparation Process:

[0022] Check and confirm whether the equipment, electrical appliances, instruments, valves and raw materials are normal, and put other reaction kettle formula raw materials into the reaction pot according to the recipe, except for the polymerization inhibitor methyl hydroquinone, and raise the temperature after feeding the materials, and the temperature of the raw materials will rise Supply nitrogen to 148°C (speed 0.5m 3 / h), horizontal condenser water supply, when the material temperature rises to 155 ° C, start stirring, when the distillation temperature rises to 100 ° C vertical conden...

Embodiment 3

[0024] formula:

[0025] Reaction kettle formula: antioxidant 0.8g, adipic acid 290g, maleic anhydride 590g, neopentyl glycol 150g, methyl propylene glycol 270g, propylene glycol 300g, polymerization inhibitor methyl hydroquinone 0.2g;

[0026] Dilution kettle recipe: 500g styrene, 80g methyl methacrylate, 0.2g copper naphthenate, 0.8g paraffin, 2g light stabilizer.

[0027] Preparation Process:

[0028] Check and confirm whether the equipment, electrical appliances, instruments, valves and raw materials are normal, and put other reaction kettle formula raw materials into the reaction pot according to the recipe, except for the polymerization inhibitor methyl hydroquinone, and raise the temperature after feeding the materials, and the temperature of the raw materials will rise Supply nitrogen to 146°C (speed 0.5m 3 / h), horizontal condenser water supply, when the material temperature rises to 153 ° C, start stirring, when the distillation temperature rises to 99 ° C vertical...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides an anti-yellowing unsaturated polyester resin, which comprises the following components by weight percentage: 13-20% of adipic acid, 23-28% of maleic anhydride, 30-33% of glycol, Oxidant 0.04-0.05%, inhibitor 0.01%, styrene 23-24%, methyl methacrylate 4%, paraffin 0.04%, copper naphthenate 0.01% and light stabilizer 0.1%, the binary The alcohol is a mixture of neopentyl glycol, ethylene glycol and propylene glycol, or a mixture of neopentyl glycol, methylpropanediol and propylene glycol. The unsaturated polyester resin of the invention has good yellowing resistance and weather resistance.

Description

technical field [0001] The invention belongs to the field of polymer chemistry, and in particular relates to an unsaturated polyester resin, in particular to a yellowing-resistant unsaturated polyester resin and a synthesis method thereof. Background technique [0002] Unsaturated polyester resins are generally obtained by polycondensation of dibasic acids or acid anhydrides and dibasic alcohols, and then dissolved in crosslinking monomers to form thermosetting resins that can be cured at room temperature. Commonly used dibasic acids include maleic anhydride, fumaric acid, phthalic anhydride, isophthalic acid, and terephthalic acid. Commonly used dibasic alcohols include propylene glycol, ethylene glycol, diethylene glycol, etc. , The cross-linking monomer generally adopts styrene. However, the cured products of this general-purpose unsaturated resin are prone to yellowing when subjected to ultraviolet light, high temperature, oxygen, rain, etc. In severe cases, the surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/52C08G63/16C08G63/78