Sweat-resistant water-based polyurethane composite paint and method for preparing same

A technology of water-based polyurethane and composite coatings, applied in the field of coatings, can solve problems such as hidden dangers to human health, unfavorable environmental protection, and lack of anti-sweat performance, and achieve good antibacterial activity, good resistance to weak acid substances, and improved anti-sweat performance.

Inactive Publication Date: 2016-06-15
HUZHOU GUOXIN MATERIALS
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yet this coating has following defect when being applied to button: 1, belongs to solvent-based coating, is unfavorable for environmental protection; Sweat is weakly acidic, and it is corrosive to button coatings and buttons. In addition, sweat is easy to breed bacteria, which poses hidden dangers to human health. The existing coatings basically do not have anti-sweat performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sweat-resistant water-based polyurethane composite paint and method for preparing same
  • Sweat-resistant water-based polyurethane composite paint and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Anti-perspiration type water-based polyurethane composite coating, by weight, includes the following components: 56 parts of one-component aliphatic acrylic modified water-based polyurethane dispersion, 0.6 part of polysiloxane, 0.3 part of tert-butanol, silicon fluoride 0.5 parts of ketone, 0.3 parts of silicone oil, 3.2 parts of dipropylene glycol butyl ether, 15 parts of barium sulfate, 16 parts of deionized water, 0.8 parts of hydroxypropyl cellulose, 1.5 parts of metal zinc drier, vinyl triethoxysilane 0.5 parts, compound antiperspirant 12.5 parts.

[0028] Its preparation method is as follows:

[0029] A, air-dry the stem of the agarwood, grind it for 2 hours with a mortar, pass through a 40-mesh sieve to obtain the agarwood powder, add a mass concentration of 70% ethanol solution and stir for 2 hours, the weight ratio of the agarwood powder to ethanol is 1: 8. Ultrasonic extraction at 80W ultrasonic power for 30 minutes, microwave extraction at 400W microwave po...

Embodiment 2

[0033] Anti-sweat type water-based polyurethane composite coating, by weight, includes the following components: 64 parts of one-component aliphatic acrylic modified water-based polyurethane dispersion, 0.5 part of polysiloxane, 0.4 part of tert-butanol, silicon fluoride 0.2 parts of ketone, 0.5 parts of silicone oil, 3.6 parts of dipropylene glycol butyl ether, 17 parts of mica powder, 18 parts of deionized water, 0.6 parts of hydroxypropyl cellulose, 1.3 parts of metal zinc drier, vinyl triethoxysilane 0.5 parts, compound antiperspirant 14 parts.

[0034] Its preparation method is as follows:

[0035] A, air-dry the stem of the agarwood, grind it for 2 hours with a mortar, pass through a 40-mesh sieve to obtain the agarwood powder, add a mass concentration of 70% ethanol solution and stir for 2 hours, the weight ratio of the agarwood powder to ethanol is 1: 8. Ultrasonic extraction at 80W ultrasonic power for 30 minutes, microwave extraction at 400W microwave power for 5 mi...

Embodiment 3

[0039] Anti-sweat type water-based polyurethane composite coating, by weight, includes the following components: 50 parts of one-component aliphatic acrylic modified water-based polyurethane dispersion, 0.6 part of polysiloxane, 0.3 part of tert-butanol, silicon fluoride 0.4 parts of ketone, 0.4 parts of silicone oil, 3.5 parts of dipropylene glycol butyl ether, 21 parts of mica powder, 20 parts of deionized water, 1.5 parts of hydroxypropyl cellulose, 1.1 parts of metal zinc drier, vinyl triethoxysilane 0.5 parts, 13 parts of compound antiperspirant.

[0040] Its preparation method is as follows:

[0041] A, air-dry the stem of the agarwood, grind it for 2 hours with a mortar, pass through a 40-mesh sieve to obtain the agarwood powder, add a mass concentration of 70% ethanol solution and stir for 2 hours, the weight ratio of the agarwood powder to ethanol is 1: 8. Ultrasonic extraction at 80W ultrasonic power for 30 minutes, microwave extraction at 400W microwave power for 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides sweat-resistant water-based polyurethane composite paint. The sweat-resistant water-based polyurethane composite paint comprises, by weight, 50-64 parts of water-based polyurethane dispersion, 0.5-0.7 part of dispersing agents, 0.3-0.6 part of wetting agents, 0.1-0.5 part of defoaming agents, 0.2-0.7 part of leveling agents, 3-4 parts of film-forming auxiliaries, 14-22 parts of fillers, 16-21 parts of deionized water, 0.6-1.5 parts of thickening agents, 1-1.5 parts of metal zinc driers, 0.5 part of vinyl triethoxysilane and 12-14 parts of composite sweat-resistant agents. The invention further provides a method for preparing the sweat-resistant water-based polyurethane composite paint. The sweat-resistant water-based polyurethane composite paint and the method have the advantage that the water-based polyurethane composite paint is excellent in sweat-resistant performance.

Description

Technical field: [0001] The invention relates to a coating, in particular to an anti-perspiration type water-based polyurethane composite coating and a preparation method thereof. Background technique: [0002] Polyurethane (PU for short) is a resin polymerized by polyisocyanate (containing -NCO) and macromolecular polyol (containing -OH). Due to the existence of a large number of hydrogen bonds in the polyurethane macromolecules, the intermolecular forces are large, and the macromolecular chains are stable to most chemical substances. Permeability, wear resistance, toughness and strong adhesion, etc., and there are many factors that can be changed in polyurethane macromolecules. Molecular design and structure adjustment can be carried out according to different actual conditions, so that it can better meet actual needs. Polyurethane coatings can be divided into two categories: solvent-based and water-based. [0003] With the progress of society, the development of scienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D5/14C09D7/12
CPCC09D175/14C08L2205/02C08L2205/025C08L2205/035C09D5/14C09D7/61C09D7/63C09D7/65C08L83/04C08L83/08C08K13/06C08K9/10C08K5/1545
Inventor 董芬芳
Owner HUZHOU GUOXIN MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap