A kind of high-reliability low-temperature lead-free solder paste and preparation method thereof

A lead-free solder paste, reliable technology, used in manufacturing tools, welding equipment, metal processing equipment, etc., can solve the problems of poor thermal fatigue reliability, poor wettability, easy to fall off solder joints, etc., to achieve thermal fatigue resistance Good performance, continuous and smooth printing process, reducing the effect of post-weld residue

Active Publication Date: 2018-06-19
广东中实金属有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the actual use process, the above two types of solder pastes have obvious deficiencies and cannot well meet the needs of actual use. Specifically: 1. Sn-Bi58 has a low melting point and good wettability, but Bi itself is brittle. The high content of Bi makes the Sn-Bi solder have high brittleness. After making solder paste, this situation still exists. After soldering, the solder joint has low strength and poor mechanical properties. Under the action of external force, the solder joint is easy to fall off. Thus making electronic devices and equipment invalid
2. Sn-In solder paste has low melting point, good electrical and thermal conductivity, and low toxicity, but there are still problems such as poor thermal fatigue reliability, poor wettability, and cleaning after soldering.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Weigh out 0.35kg of triethylene glycol methyl ether, 0.47kg of rosin, 0.05kg of malonic acid, 0.07kg of suberic acid, and 0.06kg of hydrogenated castor oil, respectively. Triethylene glycol methyl ether was added to the container, the temperature was raised to 100° C., and the mixture was stirred for 3 minutes. Then add rosin, disperse the rosin with a high-speed disperser, and make it all dissolved in the solvent. After the solution is clear and transparent, cool down to 90 ° C, add malonic acid and suberic acid, and disperse with a high-speed disperser for 8 minutes to make the active agent Fully disperse in the liquid, let stand for 5 minutes, then add hydrogenated castor oil, disperse with a high-speed disperser, so that all the thixotropic agent is dissolved in the flux, then take out the dispersing head, and let stand for 8 hours to obtain the required of flux.

[0021] Stir the flux with a spatula for 1 minute, then weigh out the flux and solder powder in a weig...

Embodiment 2

[0023] Weigh out 0.18kg of propylene glycol methyl ether, 0.24kg of ethylene glycol ether, 0.44kg of rosin, 0.05kg of glutaric acid, 0.03kg of citric acid, and 0.06kg of ethylene bis-stearic acid amide. Propylene glycol methyl ether and ethylene glycol ethyl ether were added to the container, the temperature was raised to 95°C, and the mixture was stirred for 4 minutes. Then add rosin, disperse the rosin with a high-speed disperser, and make it all dissolved in the solvent. After the solution is clear and transparent, cool down to 80 ° C, add glutaric acid and citric acid, and disperse with a high-speed disperser for 5 minutes to make the active agent fully Disperse in the liquid, let stand for 10 minutes, then add ethylene bis-stearic acid amide, disperse with a high-speed disperser, so that all the thixotropic agent is dissolved in the flux, then take out the dispersing head, and let stand for 10 hours to obtain this. Invent the required flux.

[0024] Stir the flux with a ...

Embodiment 3

[0026] Weigh out 0.38kg of ethylene glycol methyl ether, 0.41kg of rosin, 0.15kg of adipic acid, 0.02kg of methyl hydrogenated castor oil, and 0.04kg of ethylene bis-stearic acid amide. Ethylene glycol methyl ether was added to the container, the temperature was raised to 90°C, and the mixture was stirred for 5 minutes. Then add rosin, disperse the rosin with a high-speed disperser, and make it all dissolved in the solvent. After the solution is clear and transparent, cool down to 85 ° C, add adipic acid, and disperse with a high-speed disperser for 10 minutes to fully disperse the active agent in the liquid. , let stand for 3 minutes, then add methylated castor oil and ethylene bis-stearic acid amide, disperse with a high-speed disperser, so that all the thixotropic agent is dissolved in the flux, then take out the dispersing head, and let stand for 12 hours, The flux required by the present invention is obtained.

[0027] Stir the flux with a spatula for 2 minutes, then wei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-reliability low-temperature lead-free solder paste and a preparation method thereof. The high-reliability low-temperature lead-free solder paste is prepared by mixing solder powder and flux according to a weight ratio of 88.5-90.0:10-11.5. The solder powder is composed of, by weight, 48-56% of Sn, 1.0-1.4% of Ag, 0.1-0.15% of rare earth Ge / Nd and the balance In. In the selected raw materials, solder powder alloy is low in melting point, excellent in mechanical property and thermal fatigue resistance and capable of meeting high reliability in use of the solder paste in a low-temperature environment; the flux is low in boiling point and capable of meeting the requirement that other components of the flux are dissolved by a solvent in a soldering process, and the flux is basically volatilized to reduce after-soldering residues after soldering is finished; an active agent with a low melting point can guarantee greatest functions in the soldering process to realize removal of an oxide film of a substrate, reduction of surface tension of soldering flux and promotion of moistening of the solder paste and the substrate; a thixotropic agent can guarantee freeness of sedimentation and layering in a solder paste storage process and continuity and smoothness in a printing process.

Description

technical field [0001] The invention relates to the field of connecting materials, in particular to a high-reliability low-temperature lead-free solder paste and a preparation method thereof. Background technique [0002] As a connection material for electrical components, solder paste is widely used. Different components have different requirements for solder paste due to different use requirements, working environments, and electrical characteristics. For the LED industry and some electronic parts chips, electronic materials and substrates that cannot withstand high-temperature soldering, low-temperature solder paste is mainly used to complete the connection process. Therefore, there is an increasing demand for low temperature solders in the market. [0003] Solder paste is a homogeneous mixture of solder and a matching flux. The low-temperature solder pastes currently used in the market are mainly Sn-Bi series and Sn-In series. For the eutectic alloys of these two seri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/26B23K35/362
CPCB23K35/262B23K35/362
Inventor 方瀚宽方喜波梁静珊范欢方瀚楷
Owner 广东中实金属有限公司