Test method for light resistance of titanium dioxide

A test method, titanium dioxide technology, applied in the preparation of test samples, weather resistance/light resistance/corrosion resistance, measuring devices, etc., can solve problems such as not suitable for long-term use, easy cracking of the test film, and affecting test accuracy. Achieve the effect of optimizing the preparation process and color difference test parameters, short test cycle, and not easy to precipitate

Inactive Publication Date: 2016-07-06
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI +1
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above detection method shortens the detection cycle, after the titanium dioxide is mixed with the resin, it is easy to produce precipitation and the storage time is s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Test method for light resistance of titanium dioxide
  • Test method for light resistance of titanium dioxide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1:

[0023] Take 5.00g of triethanolamine, 2.50g of ethanol, 57.5g of deionized water, stir and mix evenly, add 35g of melamine formaldehyde resin powder after mixing, heat to 50℃ to dissolve completely, and then cool to normal temperature; the above solution is the newly prepared melamine Formaldehyde resin aqueous solution, weigh 1.20g titanium dioxide (test sample) and DuPont titanium dioxide R796 (standard sample), add to 6.0mL melamine formaldehyde resin aqueous solution, ultrasonically disperse for 5min to make the titanium dioxide uniformly dispersed in the resin, Take 2.5 mL of the evenly dispersed mixed solution and evenly coat it on the glass slide, and place it in a drying oven at 70°C for continuous drying for 10 hours. Take it out, put it into the exposure machine for 20min, 40min, 60min, 80min, 120min, and test the color difference ΔE of the test sample and the standard sample before and after exposure.

[0024] After testing and calculation, the color...

Example Embodiment

[0025] Example 2:

[0026] Take 3.00g of triethanolamine, 4.50g of ethanol, 57.5g of deionized water, stir and mix evenly, add 35g of melamine formaldehyde resin powder after mixing, heat to 50℃ to dissolve completely, then cool to normal temperature; the above solution is the newly prepared melamine Formaldehyde resin aqueous solution, weigh 1.20g titanium dioxide (test sample) and DuPont titanium dioxide R796 (standard sample), add to 6.0mL melamine formaldehyde resin aqueous solution, ultrasonically disperse for 5min to make the titanium dioxide uniformly dispersed in the resin, Take 2.5 mL of the evenly dispersed mixed solution and evenly coat it on the glass slide, place it in a drying oven at 80°C, and continue drying for 8 hours. Take it out and put it in the exposure machine for 40 minutes to test the color difference ΔE between the test sample and the standard sample after exposure. After testing and calculation, it can be obtained that the color difference ΔE of the te...

Example Embodiment

[0027] Example 3:

[0028] Take 7.00g of triethanolamine, 2.50g of ethanol, 55.5g of deionized water, stir and mix evenly, add 35g of melamine formaldehyde resin powder after mixing, heat to 50℃ to dissolve completely, then cool to normal temperature; the above solution is the newly prepared melamine Formaldehyde resin aqueous solution, weigh 1.20g titanium dioxide (test sample) and DuPont titanium dioxide R796 (standard sample), add to 6.0mL melamine formaldehyde resin aqueous solution, ultrasonically disperse for 5min to make the titanium dioxide uniformly dispersed in the resin, Take 2.5 mL of the evenly dispersed mixed solution and evenly coat it on the glass slide, and place it in a drying oven at 60°C for continuous drying for 10 hours. Take it out and put it in the exposure machine for 60 minutes to test the color difference ΔE of the test sample and the standard sample after exposure. After testing and calculation, it can be obtained that after 60 minutes of exposure, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Thicknessaaaaaaaaaa
Areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a test method for light resistance of titanium dioxide. The test method includes the following steps that 1, a melamino-formaldehyde resin water solution is prepared and contains triethanolamine, ethyl alcohol and melamino-formaldehyde resin, and the mass fraction of the melamino-formaldehyde resin is 20-50%; 2, titanium dioxide is dispersed in the melamino-formaldehyde resin water solution, and the concentration of titanium dioxide is 0.1-0.5 g/mL; 3, a glass slide is coated with the mixture and then placed in a drying oven and dried to obtain a film; 4, the dried film is taken out and put into a printing-down machine with an iodine gallium light to be exposed under the blazing sun for a long time, and chromatic aberration delta E value before and after the step of exposure under the blazing sun for a long time is tested. The test method is short in test period, the operation process is simple, storage time is long, precipitation does not occur easily, and test results are high in accuracy.

Description

technical field [0001] The invention relates to the field of performance detection methods of titanium dioxide, in particular to a method for testing the light resistance of titanium dioxide. Background technique [0002] Titanium dioxide is the most used white pigment, because it has the highest refractive index (rutile type 2.71, anatase type 2.55) among the known white pigments, so it has unparalleled hiding power and excellent optical properties, becoming a white pigment s King. However, titanium dioxide has photocatalytic activity, and a photocatalytic reaction occurs under sunlight, especially under the irradiation of ultraviolet light, so that the organic matrix around titanium dioxide is oxidatively decomposed, and the paint coating or plastic used with titanium dioxide becomes yellow, cracks, and powders. changes, affecting the use of the product. Therefore, light resistance is an important pigment performance of titanium dioxide. However, at present, the light r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N17/00G01N1/28
CPCG01N1/28G01N1/2813G01N17/004
Inventor 乔玄玄储成义孙爱华晏育刚华原杰吴明宇许高杰郭建军
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap