High-strength steel plate material used for automobile loading part

A high-strength steel plate and automobile load technology, applied in the field of auto parts, can solve the problems of dispersion and density value that cannot be solved at the same time, limit the large-scale development of the steel industry, and the quality stability is not high, so as to achieve high strength, The effect of high yield and high product performance

Inactive Publication Date: 2016-07-27
ANHUI HEKUANG MACHINERY
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although he provided a kind of niobium carbide composite powder with a density value close to molten steel and a kind of niobium carbide composite powder with good dispersion in molten steel, the problems of dispersibility and density value in the steelmaking process cannot be solved at the same time, which limits the steel industry. Large-scale development, and aluminum powder is prone to oxidation, and the quality stability is not high when preparing aluminum-doped niobium carbide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-strength steel plate material for automobile load parts, which is prepared according to the following steps:

[0014] a. Melting: Add low-sulfur phosphorus clean scrap steel into high-frequency induction melting furnace to melt into molten steel, then add recarburizer, wait for the temperature in the furnace to rise to 1500°C, add pig iron, ferrosilicon and ferromanganese, keep warm for 20 minutes and then add After iridium, copper, nickel, magnesium and zirconium are completely melted, add modified niobium carbide, raise the temperature to 1630°C, keep stirring at constant temperature for 5 minutes to obtain matrix alloy liquid;

[0015] b. Detection: Detect the component content of the matrix alloy liquid, add materials to make the elements by weight percentage: carbon: 0.6%, silicon: 0.9%, nickel: 0.2%, manganese: 2.4%, iridium: 0.06%, aluminum : 0.1%, zirconium 0.04%, copper: 0.2%, magnesium: 0.6%, sulfur ≤ 0.015%, phosphorus ≤ 0.015%, the balance is iron and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength steel plate material used for an automobile loading part. Elements of the high-strength steel plate material include, by weight percent, 0.6%-0.8% of carbon, 0.9%-1.3% of silicon, 0.2%-0.4% of nickel, 2.4%-3.5% of manganese, 0.06%-0.08% of iridium, 0.1%-0.2% of aluminum, 0.04%-0.05% of zirconium, 0.2%-0.3% of copper, 0.6%-1.2% of magnesium, smaller than or equal to 0.015% of sulfur, smaller than or equal to 0.015% of phosphorus and the balance iron and inevitable impurities. By means of the high-strength steel plate material used for the automobile loading part, the casting quality of a casting is good, the yield is high, the casting cost is low, the shock-resistance bearing capability is good, and the high-strength steel plate material is high in safety when used as the automobile loading part and is worthy of being popularized.

Description

technical field [0001] The invention relates to the technical field of automobile parts, in particular to a high-strength steel plate material for automobile load parts. Background technique [0002] Iron and steel materials occupy an important position in the mechanical engineering manufacturing industry due to their high strength and good toughness. In recent years, mechanical engineering structures have increasingly developed in the direction of giantization and high parameters, and higher and higher requirements have been put forward for the performance of steel materials. , the addition of particles to strengthen steel materials has many advantages, but it is often at the expense of reducing plasticity and toughness on the premise of increasing strength and hardness. In the article "Preparation Technology and Application of Nano-NbC / Fe(Fe3C) Composite Powder for Iron-Based Materials Strengthened by Adding Particles", Qin Sen chose NbC as the strengthening phase particle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/16C22C38/02C22C38/04C22C38/06C22C38/08C22C38/14C21C7/06C21C7/064C22C33/06
CPCC21C7/06C21C7/064C22C33/06C22C38/002C22C38/02C22C38/04C22C38/06C22C38/08C22C38/14C22C38/16Y02P10/20
Inventor 胡乾桂
Owner ANHUI HEKUANG MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap