Anti-cracking mortar and preparation method thereof

A technology of anti-cracking mortar and quartz sand, applied in the field of building materials, can solve the problems of surface hollowing, easy mildew, falling off, etc., and achieve the effect of improving shrinkage performance, strong applicability, and improving cracking resistance.

Inactive Publication Date: 2016-09-28
王星烨
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing traditional mortar has exposed many defects during use, such as surface hollowing, cracking, falling off, easy to mildew, etc., so it is increasingly unable to meet people's requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1, an anti-cracking mortar made of the following raw materials in parts by weight (kg): cement 280, quartz sand 240, xonotlite 100, slag powder 60, expanded slag beads 14, EVA redispersible latex powder 6 , polysiloxane emulsion 3, calcium sulfoaluminate expansion agent 4, polypropylene fiber 2, polyimide fiber 1, vitrified microbeads 10, propylene carbonate 1, silane coupling agent KH550 1, magnesium hydroxide 7. Dioctyl adipate 0.1, silicon boride 0.2, bamboo charcoal powder 0.2, melamine water reducer 3, guar gum 2, citric acid 5.

[0015] A preparation method of anti-crack mortar, comprising the following steps:

[0016] (1) Weigh each raw material by weight;

[0017] (2) Soak the vitrified microbeads in 10% hydrogen peroxide solution for 7 hours, take them out, wash them with deionized water, dry them, then add propylene carbonate and silane coupling agent KH550, at 180 rpm Stir for 12 minutes, and dry to obtain modified vitrified microbeads;

[0018] (3...

Embodiment 2

[0020] Example 2, an anti-cracking mortar made of the following raw materials in parts by weight (kg): cement 300, quartz sand 250, xonotlite 110, slag powder 70, expanded slag beads 16, EVA redispersible latex powder 7 , polysiloxane emulsion 4, calcium sulfoaluminate expansion agent 5, polypropylene fiber 3, polyimide fiber 2, vitrified microbeads 11, propylene carbonate 2, silane coupling agent KH550 2, magnesium hydroxide 8. Dioctyl adipate 0.2, silicon boride 0.3, bamboo charcoal powder 0.3, melamine water reducer 4, guar gum 3, citric acid 6.

[0021] A preparation method of anti-crack mortar, comprising the following steps:

[0022] (1) Weigh each raw material by weight;

[0023] (2) Soak the vitrified microbeads in 12% hydrogen peroxide solution for 8 hours, take them out, wash them with deionized water, dry them, then add propylene carbonate and silane coupling agent KH550, at 200 rpm Stir for 13 minutes and dry to obtain modified vitrified microbeads;

[0024] (3)...

Embodiment 3

[0026] Example 3, an anti-cracking mortar made of the following raw materials in parts by weight (kg): cement 320, quartz sand 260, xonotlite 120, slag powder 80, expanded slag beads 18, EVA redispersible latex powder 8 , polysiloxane emulsion 5, calcium sulfoaluminate expansion agent 6, polypropylene fiber 4, polyimide fiber 3, vitrified microbeads 12, propylene carbonate 3, silane coupling agent KH5503, magnesium hydroxide 9 , dioctyl adipate 0.3, silicon boride 0.4, bamboo charcoal powder 0.4, melamine superplasticizer 5, guar gum 4, citric acid 7.

[0027] A preparation method of anti-crack mortar, comprising the following steps:

[0028] (1) Weigh each raw material by weight;

[0029] (2) Soak the vitrified microbeads in a hydrogen peroxide solution with a concentration of 10-15% for 9 hours, take it out, wash it with deionized water, dry it, then add propylene carbonate and silane coupling agent KH550, and turn it at 220 rpm Stir for 14 minutes at a time, and dry to ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-cracking mortar and a preparation method thereof and relates to the technical field of building materials. The anti-cracking mortar is mainly prepared from cement, quartz sand, xonotlite, furnace slag powder, expanded slag beads, EVA re-dispersible latex powder, polysiloxane emulsion, calcium sulphoaluminate expansion agents, polypropylene fiber, polyimide fiber, glass beads, magnesium hydroxide, melamine water reducer, guar gum, citric acid and the like. The polysiloxane emulsion is added into the mortar, so that the hollowing resistance of the mortar is improved; through the calcium sulphoaluminate expansion agents and the polypropylene fiber, the shrinkage performance of the hardened mortar is improved, thus the cracking resistance of the mortar is improved; through the components such as magnesium hydroxide and glass beads and the like, the heat preservation performance and the performance stability of the mortar are improved; the produced mortar is high in overall performance and high in applicability.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an anti-crack mortar and a preparation method thereof. Background technique [0002] Mortar is made by mixing inorganic cementitious material with fine aggregate and water in proportion, also known as mortar. For masonry and plastering projects, it can be divided into masonry mortar and plastering mortar. The former is used for masonry and component installation of bricks, stones, blocks, etc.; the latter is used for walls, floors, roofs and beams. Plastering of the surface of the column structure, etc., to meet the requirements of protection and decoration. Some of the ordinary mortar materials are gypsum, lime plaster or clay mixed with fibrous reinforcing materials and water to prepare a paste, which is called ash, paste, mud or cement. Commonly used are hemp knife ash (lime plaster mixed with hemp knife), paper ash (lime plaster mixed with paper rebar), gypsum as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/42C04B22/14C04B16/06C04B22/06C04B14/24
CPCC04B28/00C04B2111/343C04B2201/05C04B2201/10C04B2201/50C04B14/06C04B14/043C04B18/14C04B18/141C04B2103/0057C04B24/42C04B22/14C04B16/0633C04B16/0691C04B14/24C04B24/045C04B22/066C04B14/321C04B14/36C04B24/305C04B24/06C04B24/38
Inventor 王星烨
Owner 王星烨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap