High-tenacity heat-resisting modified phenolic resin controlling cable material

A technology of phenolic resin and heat-resistant modification, which is applied in the direction of plastic/resin/wax insulators, organic insulators, etc., and can solve the problems of controlling cable materials and heat resistance.

Inactive Publication Date: 2016-09-28
安徽华海特种电缆集团有限公司
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The capriciousness and heat resistance of the control cable materials used in the prior art cannot meet the needs of actual use, so it is urgent to develop a control cable material with excellent toughness and heat resistance to meet the needs of actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020]A high-toughness heat-resistant modified phenolic resin control cable material proposed by the present invention, its raw materials include by weight: 60 parts of modified phenolic resin, 20 parts of silicone rubber, 10 parts of epoxy acrylic resin, 5 parts of EPDM rubber 6 parts, 6 parts of polyethylene terephthalate, 3.5 parts of chlorinated polyethylene, 4 parts of linear low density polyethylene, 3 parts of nylon, 5 parts of trifluoropropyl methyl silicone oil, 5 parts of kaolin, 5 parts of nano silicon carbide 5.5 parts of nano-magnesium oxide, 3.5 parts of nano-aluminum hydroxide, 3 parts of nano-silicon dioxide, 3 parts of zinc borate, 2 parts of white carbon black, 2.5 parts of magnesium hydroxide, 3.5 parts of stearic acid, 2 parts of phthalic acid 5.5 parts of isooctyl ester, 3.5 parts of silane coupling agent KH-570, 2.5 parts of chlorinated paraffin, 2 parts of calcium carbonate, 3 parts of antimony trioxide, 4 parts of terephthalic acid, 6 parts of accelerato...

Embodiment 2

[0023] A high-toughness heat-resistant modified phenolic resin control cable material proposed by the present invention, its raw materials include by weight: 30 parts of modified phenolic resin, 30 parts of silicone rubber, 5 parts of epoxy acrylic resin, 8 parts of EPDM rubber 3 parts, 3 parts of polyethylene terephthalate, 5 parts of chlorinated polyethylene, 2 parts of linear low density polyethylene, 5 parts of nylon, 2 parts of trifluoropropyl methyl silicone oil, 9 parts of kaolin, 2 parts of nano silicon carbide 1 part, 8 parts of nano-magnesium oxide, 1 part of nano-aluminum hydroxide, 4 parts of nano-silica, 1 part of zinc borate, 3 parts of white carbon black, 1 part of magnesium hydroxide, 5 parts of stearic acid, 2 parts of phthalic acid 3 parts of isooctyl ester, 5 parts of silane coupling agent KH-5705, 1 part of chlorinated paraffin, 3 parts of calcium carbonate, 2 parts of antimony trioxide, 5 parts of terephthalic acid, 4 parts of accelerator NA, 5 parts of acc...

Embodiment 3

[0026] A high-toughness heat-resistant modified phenolic resin control cable material proposed by the present invention, its raw materials include by weight: 90 parts of modified phenolic resin, 10 parts of silicon rubber, 15 parts of epoxy acrylic resin, 2 parts of EPDM rubber 9 parts of polyethylene terephthalate, 2 parts of chlorinated polyethylene, 6 parts of linear low density polyethylene, 1 part of nylon, 8 parts of trifluoropropyl methyl silicone oil, 1 part of kaolin, 8 parts of nano-silicon carbide 3 parts, 3 parts of nano-magnesium oxide, 6 parts of nano-aluminum hydroxide, 2 parts of nano-silicon dioxide, 5 parts of zinc borate, 1 part of white carbon black, 4 parts of magnesium hydroxide, 2 parts of stearic acid, 2 parts of phthalic acid 8 parts of isooctyl ester, 2 parts of silane coupling agent KH-5702, 4 parts of chlorinated paraffin, 1 part of calcium carbonate, 4 parts of antimony trioxide, 3 parts of terephthalic acid, 8 parts of accelerator NA, 1 part of acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-tenacity heat-resisting modified phenolic resin controlling cable material. The high-tenacity heat-resisting modified phenolic resin controlling cable material is prepared from the raw materials of modified phenolic resin, silicon rubber, epoxy acrylic resin, ethylene propylene diene monomer, polyethylene terephthalate, chlorinated polyethylene, linear low-density polyethylene, nylon, trifluoropropyl methyl silicone oil, kaolin, nanometer silicon carbide, nanometer magnesia, nanometer aluminum hydroxide, nanometer silicon dioxide, zinc borate, white carbon black, magnesium hydroxide, stearic acid, diisooctyl phthalate, a silane coupling agent KH-570, chlorinated paraffin, calcium carbonate, antimonous oxide, terephthalic acid, accelerant NA, accelerant TT, vulcanizing agent DTDM, plasticizing agent and fire retardant. The cable material has excellent tenacity and heat resistance.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to a high-toughness heat-resistant modified phenolic resin control cable material. Background technique [0002] Wires and cables refer to materials used for electricity, communications and related purposes. With the development of society, wires and cables are more and more widely used in various fields, such as transportation, communications, construction, etc. Therefore, the professional field of wires and cables The requirements are also getting higher and higher. [0003] The capriciousness and heat resistance of the control cable materials used in the prior art cannot meet the needs of actual use, so it is urgent to develop a control cable material with excellent toughness and heat resistance to meet the needs of actual use. Contents of the invention [0004] In order to solve the technical problems in the background technology, the present invention proposes a high-toughness...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/14C08L83/04C08L23/16C08L67/02C08L23/28C08L23/08C08L77/00C08L91/06C08K13/02C08K3/34C08K3/22C08K3/36C08K3/38C08K5/09C08K5/12C08K5/5419C08K3/26H01B3/36
CPCC08L61/14C08K2201/011C08K2201/014C08L2201/08C08L2203/202C08L2205/035H01B3/36C08L83/04C08L23/16C08L67/02C08L23/286C08L23/0815C08L77/00C08L91/06C08K13/02C08K3/346C08K3/34C08K2003/222C08K2003/2227C08K3/36C08K2003/387C08K2003/2224C08K5/09C08K5/12C08K5/5419C08K2003/265C08K3/2279
Inventor 谷仁杰邹强沈志海沈志荣赵俊
Owner 安徽华海特种电缆集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap