N-TiO2 silkworm excrement carbonization dual-functional adsorbent and preparation method thereof

A dual-function, adsorbent technology, applied in chemical instruments and methods, physical/chemical process catalysts, separation methods, etc., can solve the problems of difficult hydrophobic high-selectivity adsorption of aldehyde VOCs, etc., to reduce energy consumption, high Capture ability, high reactivity effect

Inactive Publication Date: 2016-12-21
GUANGXI UNIV
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because, if we want the material to increase the adsorption force of aldehyde VOCs, the result will inevitably lead to a corresponding increase in the adsorption force of the material to water molecules. It is difficult to achieve the hydrophobicity of the material and the high selective adsorption of aldehyde VOCs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • N-TiO2 silkworm excrement carbonization dual-functional adsorbent and preparation method thereof
  • N-TiO2 silkworm excrement carbonization dual-functional adsorbent and preparation method thereof
  • N-TiO2 silkworm excrement carbonization dual-functional adsorbent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of N-TiO 2 The preparation method of carbonized silkworm excrement bifunctional adsorbent comprises the following steps,

[0030] (1) Preparation of carbonized silkworm excrement

[0031] in N 2 In the atmosphere, 10.0 g of raw silkworm excrement was raised to 500°C at a heating rate of 5°C / min, kept at 500°C for more than 3 hours, and then cooled to room temperature to obtain carbonized silkworm excrement, which was denoted as CS.

[0032] (2) A-TiO 2 Preparation of carbonized silkworm excrement material;

[0033] Add the ethylene glycol solution (5mL) containing 1.0g butyl titanate dropwise to the aqueous solution containing 0.3g carbonized silkworm excrement (the aqueous solution is 2.5mL), and stir vigorously until fully hydrolyzed to form amorphous TiO 2 , to prepare A-TiO 2 Carbonized silkworm excrement material;

[0034] (3) N-TiO 2 Preparation of carbonized silkworm excrement bifunctional adsorbent;

[0035] The prepared A-TiO 2 Carbonized silkwo...

Embodiment 2

[0037] A kind of N-TiO 2 The preparation method of carbonized silkworm excrement bifunctional adsorbent comprises the following steps,

[0038] (1) Preparation of carbonized silkworm excrement

[0039] in N 2 In the atmosphere, 10.0 g of raw silkworm excrement was raised to 600°C at a heating rate of 2°C / min, kept at 600°C for 8 hours, and then cooled to room temperature until carbonized silkworm excrement was recorded as CS.

[0040](2) A-TiO 2 Preparation of carbonized silkworm excrement material;

[0041] Add the ethanol solution (30mL) containing 1.0g butyl titanate dropwise to the aqueous solution containing 0.6g carbonized silkworm excrement (the aqueous solution is 15mL), and stir vigorously until fully hydrolyzed to form amorphous TiO 2 , to prepare A-TiO 2 Carbonized silkworm excrement material;

[0042] (3) N-TiO 2 Preparation of carbonized silkworm excrement bifunctional adsorbent;

[0043] The prepared A-TiO 2 Carbonized silkworm excrement material 2.0g is...

Embodiment 3

[0045] A kind of N-TiO 2 The preparation method of carbonized silkworm excrement bifunctional adsorbent comprises the following steps,

[0046] (1) Preparation of carbonized silkworm excrement

[0047] in N 2 In the atmosphere, 10.0 g of raw silkworm excrement was raised to 1000°C at a heating rate of 8°C / min, kept at 1000°C for more than 1 hour, and then cooled to room temperature to obtain carbonized silkworm excrement, which was denoted as CS.

[0048] (2) A-TiO 2 Preparation of carbonized silkworm excrement material;

[0049] Add the ethanol solution (15 mL) containing 1.0 g butyl titanate dropwise to the aqueous solution containing 0.9 g carbonized silkworm excrement (the aqueous solution is 30 mL), and stir vigorously until fully hydrolyzed to form amorphous TiO 2 , to prepare A-TiO 2 Carbonized silkworm excrement material;

[0050] (3) TiO 2 - Preparation of N-doped carbonized silkworm excrement bifunctional adsorbent;

[0051] The prepared A-TiO 2 Carbonized s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an N-TiO2 silkworm excrement carbonization dual-functional adsorbent, as well as a preparation method and application thereof. The preparation method comprises the following steps: (1) placing silkworm excrement into a high-temperature tubular furnace, introducing protection gas for purging, heating to 500 to 1,000 DEG C for high-temperature carbonization reaction, and obtaining carbonized silkworm excrement CS; (2) adding butyl titanate into a selective alcohol solvent, then dropwise adding into a carbonized silkworm excrement-containing aqueous solution, hydrolyzing the butyl titanate to generate amorphous TiO2, and obtaining an A-TiO2 / carbonized silkworm excrement material; (3) performing surface modification on the material in a plasma radiation way to obtain an N-doped A-TiO2 / carbonized silkworm excrement material; (4) calcining the material at the temperature of 180 to 500 DEG C, and finally obtaining an N-TiO2 / CS composite material which is the N-TiO2 silkworm excrement carbonization dual-functional adsorbent. The dual-functional adsorption material disclosed by the invention is applied to synchronous adsorption and catalytic degradation of aldehydes and benzene series VOCs (volatile organic compounds).

Description

technical field [0001] The invention belongs to the field of porous carbon materials, in particular to N-TiO 2 Carbonized silkworm excrement bifunctional adsorbent material and its preparation method. Background technique [0002] Porous carbon materials are a kind of high-efficiency commonly used adsorbents. Their adsorption capacity is high and the cost is low. However, the surface of such carbon materials often has abundant hydrophilic groups (oxygen-containing groups), showing strong affinity watery. Therefore, in a humid environment, the adsorption capacity is often greatly reduced due to the competitive adsorption of water vapor molecules, especially for polar VOCs (such as formaldehyde, acetaldehyde, etc.), this problem becomes particularly prominent. Studies have shown that the adsorption capacity of activated carbon to toluene is reduced by 17% under the condition of relative humidity of 3.0RH%, and the adsorption capacity of butane is reduced by 30% under the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/20B01J20/30B01J20/28B01D53/86B01D53/44B01J27/24B01J21/06B01J35/10B01D53/02
CPCB01D53/02B01D53/8668B01J20/06B01J20/20B01J20/28057B01J21/063B01J27/24B01D2257/708B01D2253/10B01J2220/4887B01J35/39B01J35/653B01J35/657
Inventor 赵祯霞武阳胡鹏赵钟兴
Owner GUANGXI UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com