A kind of environment-friendly high-gloss waterproof printing paper and its preparation method

A high-gloss, printing paper technology, applied in paper, papermaking, textiles and papermaking, etc., to achieve the effect of reducing printing error rate, good gloss, and enhancing stability

Active Publication Date: 2018-07-20
安徽文峰新材料科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the economy and the popularization of office supplies, printers and printing paper are used more and more widely. Different printing documents have different requirements for printing paper. Ability is more important, and there are relatively few related products in China at present, so a printing paper that can be used for color inkjet is needed, which has a good waterproof effect, can handle ink well, and achieves fast absorption and good adhesion. color reproduction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An environmentally friendly high-gloss waterproof printing paper, made of the following raw materials by weight percentage: 18% hardwood pulp fiber, 27% softwood pulp fiber, 8% polystyrene fiber, 12% polypropylene fiber, and 10% titanium dioxide fiber , hydroxyethyl methylcellulose 2%, ammonium zirconium carbonate 2%, polyacrylate latex 10%, surface treatment agent 2%, zinc white 9%;

[0015] Among them, the surface treatment agent is made by mixing titanate coupling agent TMC-311, heptafluoropropane, and zinc methionine at a mass ratio of 3:1:1.

[0016] Wherein, the fineness of the polystyrene fiber is 50-70TEX, and the length is 15-25mm; the fineness of the polypropylene fiber is 22-28TEX, and the length is 5-15mm; the fineness of the titanium dioxide fiber is 25-40TEX , the length is 8-20mm.

[0017] A preparation method of environment-friendly high-gloss waterproof printing paper, comprising the steps of:

[0018] (1) Mix hardwood pulp fibers and softwood pulp fi...

Embodiment 2

[0023] An environmentally friendly high-gloss waterproof printing paper, made of the following raw materials in weight percentage: 15% hardwood pulp fiber, 30% softwood pulp fiber, 7% polystyrene fiber, 10% polypropylene fiber, and 8% titanium dioxide fiber , hydroxyethyl methylcellulose 3%, ammonium zirconium carbonate 2%, polyacrylate latex 12%, surface treatment agent 3%, zinc white 10%;

[0024] Among them, the surface treatment agent is made by mixing titanate coupling agent TMC-311, heptafluoropropane, and zinc methionine at a mass ratio of 3:1:1.

[0025] Its preparation method is identical with embodiment 1.

Embodiment 3

[0027] An environmentally friendly high-gloss waterproof printing paper, made of the following raw materials in weight percentage: 20% hardwood pulp fiber, 26% softwood pulp fiber, 7% polystyrene fiber, 12% polypropylene fiber, and 12% titanium dioxide fiber , 2% hydroxyethyl methylcellulose, 1% ammonium zirconium carbonate, 12% polyacrylate latex, 2% surface treatment agent, 6% zinc white;

[0028] Among them, the surface treatment agent is made by mixing titanate coupling agent TMC-311, heptafluoropropane, and zinc methionine at a mass ratio of 3:1:1.

[0029] Its preparation method is identical with embodiment 1.

[0030] The whiteness of the printing paper prepared by the method in the present invention is 92%. A control group 1 is set, and the hardwood pulp fiber and softwood pulp fiber are the main materials. Other raw materials are the same as the preparation method in Example 1. A control group 2 is set. The treatment agent is a conventional titanate coupling agent, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly high-gloss waterproof printing paper and a preparation method thereof. The raw materials for preparing the environment-friendly high-gloss waterproof printing paper include hardwood pulp fibers, softwood pulp fibers, polystyrene fibers, polypropylene fibers, titanium dioxide fibers, hydroxyethyl methyl cellulose, zirconium ammonium carbonate, polyacrylic ester latex, surface treating agent and zinc oxide. Compared with the prior art, the environment-friendly high-gloss waterproof printing paper has the advantages that the paper sheet has excellent absorption and air permeability; the chemical auxiliaries and fillers are utilized to enhance the stability of the inner structure of the paper sheet; the polystyrene fibers and the polypropylene fibers are acquired by recycling wastes and are safe and environmentally friendly; after the surface treating agent is mixed with the polyacrylic ester latex, an excellent protecting layer is formed on the surface of the paper sheet and the oxidation resistance is increased; the printing paper prepared according to the method has the whiteness of 92% and will not change color after long-term storage; the glossiness of the printed color image is high; the printing error rate in the printing process can be reduced; the working efficiency is increased.

Description

technical field [0001] The invention belongs to the technical field of processing special printing paper, and in particular relates to an environment-friendly high-gloss waterproof printing paper and a preparation method thereof. Background technique [0002] With the development of the economy and the popularization of office supplies, printers and printing paper are used more and more widely. Different printing documents have different requirements for printing paper. Ability is more important, and there are relatively few related products in China at present, so a printing paper that can be used for color inkjet is needed, which has a good waterproof effect, can handle ink well, and achieves fast absorption and good adhesion. Color reproduction. Contents of the invention [0003] The object of the present invention is to provide an environment-friendly high-gloss waterproof printing paper and a preparation method thereof for the existing problems. [0004] The present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H15/12D21H13/14D21H13/36D21H17/26D21H17/67D21H17/66D21H17/37D21H21/14D21H21/38
CPCD21H13/14D21H13/36D21H15/12D21H17/26D21H17/37D21H17/66D21H17/675D21H21/14D21H21/38
Inventor 顾劲松
Owner 安徽文峰新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com