Anti-bacterial resin composite material for dental department and preparation method of anti-bacterial resin composite material

A resin composite material, dental technology, used in dental preparations, dentistry, dental prosthesis and other directions, can solve the problems of limited application of dental resin, poor antibacterial properties, failure of filling treatment, etc., to shorten curing time, excellent antibacterial properties , good biocompatibility

Inactive Publication Date: 2017-02-01
李健
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the oral cavity is a bacterial environment, bacteria are easy to adhere and accumulate on the resin, forming plaque, leading to diseases such as mucositis or dental caries, thus making the filling treatment ineffective
As people have higher and higher requirements on the quality of dental resins, the antibacterial properties of existing dental resins are not very good, which limits the application of dental resins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A dental antibacterial resin composite material, the raw materials of which include the following components by weight: 30 parts of bisphenol A diglycidyl methacrylate, 30 parts of triethylene glycol dimethacrylate, 1,6- 4 parts of hexanediol dimethacrylate, 8 parts of spiro ring orthoester, 0.5 parts of polytetrafluoroethylene, 3.5 parts of camphorquinone, 3 parts of tetraacicular zinc oxide whiskers, 10 parts of modified nano titanium dioxide, chitosan 2 parts of sugar, 2.5 parts of diethylenetriamine, 0.3 parts of polyvinylpyrrolidone, 2.5 parts of sodium p-toluene sulfinate.

Embodiment 2

[0018] A dental antibacterial resin composite material, the raw materials of which include the following components by weight: 45 parts of bisphenol A diglycidyl methacrylate, 10 parts of triethylene glycol dimethacrylate, 1,6- 12 parts of hexanediol dimethacrylate, 2 parts of spiro ring orthoester, 2 parts of polytetrafluoroethylene, 1 part of camphorquinone, 10 parts of four-needle zinc oxide whiskers, 2 parts of modified nano titanium dioxide, chitosan 12 parts of sugar, 1 part of diethylenetriamine, 1 part of polyvinylpyrrolidone, and 1 part of sodium p-toluene sulfinate; wherein, the modifier for modifying nanometer titanium dioxide is tetra-n-butyl titanate.

Embodiment 3

[0020] A dental antibacterial resin composite material, the raw materials of which include the following components by weight: 41 parts of bisphenol A diglycidyl methacrylate, 22 parts of triethylene glycol dimethacrylate, 1,6- 8.6 parts of hexanediol dimethacrylate, 6.8 parts of spiro ring orthoester, 1.3 parts of polytetrafluoroethylene, 2.5 parts of camphorquinone, 6 parts of tetraacicular zinc oxide whiskers, 7 parts of modified nano titanium dioxide, shell polymer 9 parts of sugar, 1.7 parts of diethylenetriamine, 0.76 parts of polyvinylpyrrolidone, and 2 parts of sodium p-toluene sulfinate; wherein, the modifier for modifying nano-titanium dioxide is silane coupling agent KH550.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-bacterial resin composite material for the dental department. The anti-bacterial resin composite material is prepared from the following raw materials in parts by weight: 30-45 parts of bisphenol A-glycidyl methacrylate, 10-30 parts of triethylene-glycol dimethacrylate, 4-12 parts of 1,6-hexanediol dimethacrylate, 2-8 parts of spiro orthoester, 0.5-2 parts of polytetrafluoroethylene, 1-3.5 parts of camphorquinone, 3-10 parts of tetrapod-like zinc oxide whiskers, 2-10 parts of modified nano titanium dioxide, 2-12 parts of chitosan, 1-2.5 parts of diethylenetriamine, 0.3-1 part of polyvinylpyrrolidone, and 1-2.5 parts of sodium p-tolylsulfinate. For the anti-bacterial resin composite material for the dental department and a preparation method of the anti-bacterial resin composite material for the dental department, the preparation method is simple, the operation is easy, and the obtained anti-bacterial resin composite material for the dental department is high in strength, has good attaching degree with teeth, and is excellent in antibacterial property.

Description

technical field [0001] The invention relates to the technical field of resins, in particular to a dental antibacterial resin composite material and a preparation method thereof. Background technique [0002] Dental caries is the lesion of tooth hard tissue caused by multiple factors in the oral cavity, in which the demineralization of inorganic matter and the decomposition of organic matter are its main manifestations. As the time of carious lesions increases, the teeth begin to change from initial color to final substantial lesions. Dental caries and some diseases caused by dental caries are basically not harmful to human life, so human beings tend to ignore these diseases, but if dental caries is not treated early, it may cause some diseases, such as pulpitis, periodontitis, etc., if Severe disease can lead to other diseases, further destroying human health. With the development of economy and technology, dental caries restoration becomes more and more serious, and the re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K6/087A61K6/00C08L35/02C08L27/18C08L5/08C08L39/06C08K13/04C08K7/08C08K3/22C08K5/42C08K5/17A61K6/891
CPCA61K6/69A61K6/70A61K6/891C08L35/02C08L2203/02C08L2205/035C08L27/18C08L5/08C08L39/06C08K13/04C08K7/08C08K2003/2241C08K5/42C08K5/17
Inventor 李健
Owner 李健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products