Preparation method of cement product

A technology for cement products and sulfoaluminate cement, applied in chemical instruments and methods, hydraulic material layered products, layered products, etc., can solve the problem of continuous production, unguaranteed product quality, and high production costs problems, to achieve the effect of quality controllable, safe and reliable operation method

Inactive Publication Date: 2017-02-15
ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional curing method is natural curing. Natural curing is to put the formed cement products in the natural environment, use the ambient temperature, and sprinkle water to keep them moist. The disadvantage of this method is that it requires a lot of manpower and can only be produced at room temperature. Continuous production, poor control of temperature and humidity, high production costs, and unguaranteed product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The cement product includes a bottom material layer, a middle material layer and a fabric layer, and the middle material layer is arranged between the bottom material layer and the fabric layer;

[0025] The primer layer is mainly prepared from the following raw materials, in parts by weight, 150 parts of sulphoaluminate cement, 11 parts of fly ash, 3 parts of silica fume, 9 parts of sawdust, 3 parts of plant fiber, and 14 parts of slag And 4 parts of admixture.

[0026] The middle material layer is mainly prepared from the following raw materials, in parts by weight, 350 parts of sulfoaluminate cement, 25 parts of fly ash, 7 parts of silica fume, 50 parts of sawdust, 3 parts of plant fiber, red brick powder 13 parts, 14 parts of diatomite, 8 parts of quartz sand, 2 parts of silicon carbide, 13 parts of bentonite, 3 parts of magnesium oxide, 3 parts of mica powder, 3 parts of calcium stearate, 3 parts of potassium permanganate, butyl acetate 3 parts and 4 parts of admi...

Embodiment 2

[0039] The cement product includes a bottom material layer, a middle material layer and a fabric layer, and the middle material layer is arranged between the bottom material layer and the fabric layer;

[0040] The primer layer is mainly prepared from the following raw materials, in parts by weight, 100 parts of sulphoaluminate cement, 5 parts of fly ash, 1 part of silica fume, 5 parts of sawdust, 1 part of plant fiber, and 10 parts of slag And admixture 1 part.

[0041] The middle material layer is mainly prepared from the following raw materials, in parts by weight, 200 parts of sulphoaluminate cement, 20 parts of fly ash, 1 part of silica fume, 40 parts of sawdust, 1 part of plant fiber, red brick powder 5 parts, 5 parts of diatomite, 5 parts of quartz sand, 1 part of silicon carbide, 10 parts of bentonite, 1 part of magnesium oxide, 1 part of mica powder, 1 part of calcium stearate, 1 part of potassium permanganate, butyl acetate 1 part and 1 part of admixture;

[0042] ...

Embodiment 3

[0054] The cement product includes a bottom material layer, a middle material layer and a fabric layer, and the middle material layer is arranged between the bottom material layer and the fabric layer;

[0055] The primer layer is mainly prepared from the following raw materials, in parts by weight, 200 parts of sulphoaluminate cement, 20 parts of fly ash, 5 parts of silica fume, 15 parts of sawdust, 5 parts of plant fiber, and 20 parts of slag And admixture 5 parts.

[0056] The middle material layer is mainly prepared from the following raw materials, in parts by weight, 400 parts of sulphoaluminate cement, 30 parts of fly ash, 10 parts of silica fume, 70 parts of sawdust, 5 parts of plant fiber, red brick powder 20 parts, 20 parts of diatomite, 10 parts of quartz sand, 5 parts of silicon carbide, 20 parts of bentonite, 5 parts of magnesium oxide, 5 parts of mica powder, 5 parts of calcium stearate, 5 parts of potassium permanganate, butyl acetate 5 parts and 5 parts of adm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a cement product. The preparation method comprises the following steps: (1) preparing raw materials for a cement product, mixing the raw materials with water, stirring the mixture, then adding the mixture into a die, and carrying out wet plate moulding; (2) placing the wet plate into a curing kiln to carry out first curing, and controlling the curing temperature in a range of 25 to 30 DEG C and the humidity more than 85%; (3) performing demoulding, after demoulding, placing the sheet into a curing kiln to carry out secondary curing, and controlling the curing temperature in a range of 25 to 30 DEG C and the humidity in a range of 70 to 85%; and (4) covering a film on the sheet in the outdoor and carrying out curing to obtain the finished product. The provided preparation method has the advantages that the quality of the prepared cement product is controllable, labor and time are saved, and the operation method is safe and reliable. The prepared cement product can be used as an exterior wall cladding of a building, has the advantages of low carbon, environment-friendliness, energy saving, deformation resistance, and recyclable property, and has the characteristics of quick moulding, short production period, good stability, fireproof property, corrosion resistant performance, and durability.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a method for preparing cement products. Background technique [0002] The curing process of cement products is an extremely important process link in the production process of cement products. It determines the quality of the product, and at the same time, it also has an important impact on the production cycle, production efficiency and energy consumption indicators. The traditional curing method is natural curing. Natural curing is to put the formed cement products in the natural environment, use the ambient temperature, and sprinkle water to keep them moist. The disadvantage of this method is that it requires a lot of manpower and can only be produced at room temperature. Continuous production, poor control of temperature and humidity, high production costs, and unguaranteed product quality. [0003] The information disclosed in this Background section is only for enhancing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/06C04B18/24B32B13/04
CPCB32B13/04B32B2262/06B32B2307/3065B32B2307/714B32B2419/04C04B18/24C04B28/06C04B2201/50C04B18/08C04B18/146C04B18/26C04B18/141C04B24/24C04B22/0013C04B24/383C04B2103/50C04B18/16C04B14/08C04B14/06C04B14/324C04B14/104C04B14/304C04B14/20C04B24/085C04B22/08C04B24/045Y02W30/91
Inventor 杨卓舒杨涛高春青
Owner ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com