High-temperature-resistant automobile tire and preparation method thereof

A technology for automobile tires and high temperature resistance, applied in special tires, tire parts, vehicle parts, etc., can solve the problems of easy aging of tires, reduced automobile driving performance, and easily deformed tire performance, etc. Excellent high temperature resistance

Active Publication Date: 2017-02-15
JINING XINRUIDA INFORMATION TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the current rubber tires can meet the needs of most cars, in hot summer, car tires are easily aged and deformed, which makes the performance of the tires drop sharply, thereby greatly reducing the driving performance of the car.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The invention provides a method for preparing a high-temperature-resistant automobile tire, comprising:

[0015] 1) Peel green bamboo, crush it, and then calcinate it in the presence of protective gas to make bamboo charcoal;

[0016] 2) Roasting titanium dioxide, barium carbonate, lithium carbonate and bamboo charcoal in the presence of protective gas to prepare modified barium metatitanate;

[0017] 3) Gelatinizing tetraethylthiuram disulfide, starch, caryophyllene, methylcellulose and water to prepare a modified vulcanizing agent;

[0018] 4) Butadiene rubber, methacrylic acid-butadiene-styrene copolymer, polyethylene oxide, pentaerythritol triacrylate, glycerin, nano-calcium carbonate, dimethyldiethoxysilane, zinc sulfide, over Benzoyl oxide and sulfur are mixed for the first time, then modified barium metatitanate and modified vulcanizing agent are added for second mixing, and finally molded and cooled to obtain high-temperature resistant automobile tires.

[001...

Embodiment 1

[0031] 1) Peel and crush green bamboo, and then calcinate at 530°C for 5 hours in the presence of protective gas (nitrogen) to obtain bamboo charcoal;

[0032] 2) Put titanium dioxide, barium carbonate, lithium carbonate and bamboo charcoal in the presence of protective gas (nitrogen) at a molar ratio of 1:0.8:0.2:0.6 and roast them (the roasting temperature is 1230°C and the roasting time is 8h) to obtain Modified barium metatitanate;

[0033] 3) Gelatinize tetraethylthiuram disulfide, starch, caryophyllene, methyl cellulose and water at a weight ratio of 100:36:5:2:250 at 45°C for 14 hours to obtain modified vulcanized agent;

[0034] 4) Butadiene rubber (weight-average molecular weight: 40,000), methacrylic acid-butadiene-styrene copolymer, polyethylene oxide (weight-average molecular weight: 6,000), pentaerythritol triacrylate, glycerin, nanocarbonic acid Calcium (particle size 30nm), dimethyldiethoxysilane, zinc sulfide, benzoyl peroxide and sulfur in a weight ratio of ...

Embodiment 2

[0036] 1) Peel and crush green bamboo, and then calcinate at 520°C for 4 hours in the presence of protective gas (helium) to obtain bamboo charcoal;

[0037] 2) Titanium dioxide, barium carbonate, lithium carbonate and bamboo charcoal were roasted in the presence of protective gas (helium) according to the molar ratio of 1:0.7:0.1:0.5 (the roasting temperature was 1200°C, and the roasting time was 7h) to produce Obtain modified barium metatitanate;

[0038] 3) Gelatinize tetraethylthiuram disulfide, starch, caryophyllene, methylcellulose and water at a weight ratio of 100:32:4:1:200 at 40°C for 12 hours to obtain modified vulcanized agent;

[0039]4) Butadiene rubber (weight-average molecular weight: 20,000), methacrylic acid-butadiene-styrene copolymer, polyethylene oxide (weight-average molecular weight: 5,000), pentaerythritol triacrylate, glycerin, nanocarbonic acid Calcium (particle size 20nm), dimethyldiethoxysilane, zinc sulfide, benzoyl peroxide and sulfur in a weigh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant automobile tire and a preparation method thereof. The preparation method comprises the steps that 1, green bamboos are peeled and smashed and then are calcined in the presence of shielding gas to obtain bamboo charcoal; 2, nano titanium dioxide, barium carbonate, lithium carbonate and the bamboo charcoal are calcined in the presence of shielding gas to obtain modified barium metatitanate; 3, tetraethylthiuram disulfide, starch, caryophyllene, methylcellulose and water are subjected to gelatinization processing to obtain a modified vulcanizing agent; 4, butadiene rubber, a methyl acrylic acid-butadiene-styrene copolymer, polyethylene oxide, pentaerythritol triacrylate, glycerol, nano calcium carbonate, dimethyldiethoxylsilane, zinc sulfide, benzoyl peroxide and sulfur are mixed primarily, then the modified barium metatitanate and the modified vulcanizing agent are added for secondary mixing, and finally forming and cooling are performed to obtain the high-temperature-resistant automobile tire. The automobile tire prepared by adopting the method has excellent high-temperature-resistant, aging-resistant and mechanical properties.

Description

technical field [0001] The invention relates to automobile tires, in particular to a high-temperature-resistant automobile tire and a preparation method thereof. Background technique [0002] Automobile tires are one of the important parts of automobiles. Their main functions are: to ease the impact of the car while driving together with the car suspension, to ensure that the car has good seating comfort and smooth driving; to ensure that the wheels and the road surface have Good adhesion, improve the traction, braking and passability of the car; bear the weight of the car. As a result, the important role played by tires on automobiles has been paid more and more attention by people. [0003] The advent of rubber tires was a prerequisite for the further development of automobiles. When it comes to rubber, people naturally think of Charles Goodyear, the father of rubber. In 1834, inspired by coke steelmaking, he began experimenting with the hardening of soft rubber. Aft...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L51/04C08L71/02C08L3/02C08L1/28C08K13/06C08K9/00C08K3/24C08K5/40C08K3/26
CPCB60C1/00C08K2003/2241C08K2003/262C08K2003/265C08K2201/003C08K2201/011C08L9/00C08L2201/08C08L2205/035C08L51/04C08L71/02C08L3/02C08L1/28C08K13/06C08K9/00C08K3/24C08K5/40C08K3/04C08K3/26C08K5/053C08K3/22
Inventor 卢国孝石宝军张华
Owner JINING XINRUIDA INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com