Tung oil embossment wood grain transfer paint and preparation method and application thereof

A wood grain transfer printing and coating technology, which is applied in lignin coatings, powder coatings, polyester coatings, etc., can solve the problems of high powder consumption and lack of three-dimensional hand feeling, and achieve high powder coating rate and super three-dimensional hand feeling , clear texture effect

Active Publication Date: 2017-03-15
湖北永渤新材料科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a tung oil embossed wood grain transfer paint and its preparation method and application in view of the problems that the products prepared by the current wood grain transfer paint have high powder consumption and do not have a three-dimensional hand feeling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of tung oil embossed wood grain transfer printing coating of the present embodiment, the mass fraction of each component in the coating is: pure polyester 58%, triglycidyl isocyanurate 8%, wood powder 28%, pigment 0.8% , leveling agent 2.3%, brightening agent 2.2%, benzoin 0.7%.

[0024] The wood powder described in this example is obtained after drying at 125° C. for 2.5 hours and passing through a 110-mesh sieve.

[0025] A kind of preparation method of tung oil embossed woodgrain transfer printing coating of the present embodiment, comprises the following steps:

[0026] (1) Mixing: Weigh pure polyester, triglycidyl isocyanurate, wood powder, pigment, leveling agent, brightener, benzoin in proportion, and mix in a mixer for 8 minutes;

[0027] (2) Extrusion: Put the uniformly mixed material in an extruder at a temperature of 120°C. After the material is fully mixed and melted, it is extruded, pressed into sheets, cut into 1-2cm thick slices, and pressed Crus...

Embodiment 2

[0034] A kind of tung oil embossed woodgrain transfer printing coating of the present embodiment, the mass fraction of each component in the coating is: pure polyester 50%, triglycidyl isocyanurate 10%, wood powder 35%, pigment 0.5% , leveling agent 2.0%, brightening agent 2.0%, benzoin 0.5%.

[0035] The wood powder described in this example is obtained after drying at 120° C. for 3 hours and passing through a 120-mesh sieve.

[0036] A kind of preparation method of tung oil embossed woodgrain transfer printing coating of the present embodiment, comprises the following steps:

[0037] (1) Mixing: Weigh pure polyester, triglycidyl isocyanurate, wood powder, pigment, leveling agent, brightener, benzoin in proportion, and mix in a mixer for 5 minutes;

[0038] (2) Extrusion: Put the uniformly mixed material in an extruder at a temperature of 110°C. After the material is fully mixed and melted, it is extruded, pressed into sheets, cut into 1-2cm thick slices, and pressed Crush ...

Embodiment 3

[0045] A kind of tung oil embossed wood grain transfer printing coating of the present embodiment, the mass fraction of each component in the coating is: pure polyester 65%, triglycidyl isocyanurate 6%, wood powder 21%, pigment 1.0% , leveling agent 3.0%, brightening agent 3.0%, benzoin 1.0%.

[0046] The wood flour in the present invention is obtained after drying at 130° C. for 2 hours and passing through a 100-mesh sieve.

[0047] A kind of preparation method of tung oil embossed wood grain transfer printing coating of the present embodiment, comprises the following steps:

[0048](1) Mixing: Weigh pure polyester, triglycidyl isocyanurate, wood powder, pigment, leveling agent, brightener, benzoin in proportion, and mix in a mixer for 10 minutes;

[0049] (2) Extrusion: Put the uniformly mixed material in an extruder at a temperature of 130°C. After the material is fully mixed and melted, it is extruded, pressed into sheets, cut into 1-2cm thick slices, and pressed Crush t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses tung oil embossment wood grain transfer paint and a preparation method and application thereof. The paint is prepared from, by mass, 50-65% of pure polyester, 6-10% of triglycidyl isocyanurate, 21-35% of wood powder, 0.5-1.0% of pigments, 2.0-3.0% of a flatting agent, 2.0-3.0% of a gloss enhancer and 0.5-1.0% of benzoin, wherein the sum of mass fractions of the raw materials is 100%. In preparation, all components are subjected to mixing, extruding, sheeting, slicing and grinding to obtain the paint, the paint is sprayed to surfaces of workpieces subjected to pretreatment, and high-temperature curing and transferring are performed to obtain sectional materials subjected to wood grain transfer. The paint is high in powder coating rate and low in powder consumption, and the prepared sectional materials are clear in texture, appropriate in concave-convex structure and extraordinary in stereo handfeel.

Description

technical field [0001] The invention relates to the technical field of powder coatings, in particular to a tung oil embossed wood grain transfer coating and a preparation method and application thereof. Background technique [0002] Wood grain transfer printing is a common metal surface coating technology. It is a process and process of transferring the wood grain on the printing plate to the substrate through the transfer printing material. At present, there are mainly two types of wood grain transfer printing on metal materials. One is to use electrostatic spraying on the surface of electrostatic powder profiles to coat a layer of thermosetting organic polymer powder. Permeable coating; the other is the wood grain transfer electrophoretic profile, which is to form dense micro-pores through anodic oxidation of the substrate, and deposit metal ions or organic dyes in the oxidized pores by electrolysis or organic coloring, and then pass through Electrophoresis deposits water...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/00C09D197/02C09D5/03C09D7/12
CPCC08L2205/16C09D5/03C09D7/63C09D167/00C08L97/02C08K5/3492
Inventor 刘凉铭
Owner 湖北永渤新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com