Preparation method of scrub-resistant calcium carbonate powder interior wall coating

A technology of calcium carbonate powder and interior wall coating, applied in fire-resistant coatings, coatings, etc., can solve the problems of low adhesion, slow coating drying, poor abrasion resistance, etc., and achieve smooth and smooth coating film, uniform color and wear resistance. Good results

Inactive Publication Date: 2017-05-24
苏州远略知识产权运营有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] This application aims at the technical problems of slow drying, poor abrasion resistance, poor water resistance, short storage period and low adhesion of existing coatings, and provides a preparation method for scrub-resistant calcium carbonate powder interior wall coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 100 parts of calcium carbonate, 1 part of hydrochloric acid, 1.5 parts of formaldehyde, 80 parts of pure water, 10 parts of sodium pentachlorophenate, 30 parts of styrene, 20 parts of butyl acrylate, and 15 parts of methacrylic acid according to the proportion of parts by weight. 30 parts of calcium hydroxide, 1 part of magnesium hydride, 0.3 parts of phosphoric acid, 0.5 parts of sodium hydroxide, 1 part of paraffin wax, 25 parts of calcium oxide.

[0022] Put hydrochloric acid, formaldehyde, pure water, sodium pentachlorophenate, styrene, butyl acrylate, methacrylic acid, phosphoric acid, and sodium hydroxide into a reactor equipped with a stirrer and a thermometer. The temperature is raised to 60°C and stirred for 30 minutes. The speed is 400 revolutions / minute, paraffin wax is added, the temperature is reduced to 30°C, and the stirring is continued for 20 minutes.

[0023] Warm up to 90°C, add the remaining raw materials, stir for 100 minutes, at a stirring speed o...

Embodiment 2

[0026] Weigh 100 parts of calcium carbonate, 5 parts of hydrochloric acid, 5.5 parts of formaldehyde, 100 parts of pure water, 30 parts of sodium pentachlorophenate, 50 parts of styrene, 40 parts of butyl acrylate, and 35 parts of methacrylic acid according to the parts by weight. 50 parts of calcium hydroxide, 5 parts of magnesium hydride, 0.7 parts of phosphoric acid, 2.5 parts of sodium hydroxide, 5 parts of paraffin wax, 45 parts of calcium oxide.

[0027] Put hydrochloric acid, formaldehyde, pure water, sodium pentachlorophenate, styrene, butyl acrylate, methacrylic acid, phosphoric acid, and sodium hydroxide into a reactor equipped with a stirrer and a thermometer, heat up to 80°C, stir for 50 minutes, and stir The speed is 600 rpm, adding paraffin, cooling to 50°C, and stirring for 40 minutes.

[0028] Raise the temperature to 100°C, add the remaining raw materials, stir for 120min at a stirring speed of 1000 revolutions per minute, grind by a three-roll mill, filter after c...

Embodiment 3

[0031] Weigh 100 parts of calcium carbonate, 2 parts of hydrochloric acid, 2.5 parts of formaldehyde, 85 parts of pure water, 15 parts of sodium pentachlorophenate, 35 parts of styrene, 25 parts of butyl acrylate, and 20 parts of methacrylic acid according to the parts by weight. 35 parts of calcium hydroxide, 2 parts of magnesium hydride, 0.4 parts of phosphoric acid, 1 part of sodium hydroxide, 2 parts of paraffin wax, 30 parts of calcium oxide.

[0032] Put hydrochloric acid, formaldehyde, pure water, sodium pentachlorophenate, styrene, butyl acrylate, methacrylic acid, phosphoric acid, and sodium hydroxide into a reactor equipped with a stirrer and a thermometer. The temperature is raised to 60°C and stirred for 30 minutes. The speed is 400 revolutions / minute, paraffin wax is added, the temperature is reduced to 30°C, and the stirring is continued for 20 minutes.

[0033] Warm up to 90°C, add the remaining raw materials, stir for 100 minutes, at a stirring speed of 800 revoluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a scrub-resistant calcium carbonate powder interior wall coating. The preparation method comprises the following steps: 1) weighing calcium carbonate, hydrochloric acid, formaldehyde, pure water, sodium pentachlorophenate, styrene, butyl acrylate, methacrylic acid, calcium hydroxide, magnesium hydride, phosphoric acid, sodium hydroxide, paraffin and calcium oxide; 2) putting hydrochloric acid, formaldehyde, pure water, sodium pentachlorophenate, styrene, butyl acrylate, methacrylic acid, phosphoric acid and sodium hydroxide into a reaction still provided with a stirrer and a thermometer, warming to 60 to 80 DEG C, stirring for 30 to 50 min, adding paraffin, cooling to 30 to 50 DEG C, and continuously stirring for 20 to 40 min; 3) warming to 90 to 100 DEG C, adding the remaining raw materials, stirring for 100 to 120 min, grinding through a three-roller grinder, cooling, filtering and examining to be qualified so as to obtain the coating. The coating is bright, clean and smooth and free of power removal or brush mark, the fineness is 25 to 45 microns, the surface dry lasts for 20 to 40 min, and the solid dry lasts for 18 to 22 h; the coating is free of caked paste or precipitate and and is uniform in color and luster, easy for brush application and free of sagging, the heat resistance at 100 DEG C is unchanged for 1 to 5 h, and the adhesive force is 100%.

Description

Technical field [0001] The invention relates to the field of coatings, in particular to a method for preparing a scrubbing-resistant calcium carbonate powder internal wall coating. Background technique [0002] Calcium carbonate is a valuable resource with a wide range of uses. Limestone is the trade name for limestone as a mineral raw material. Limestone has been widely used in the history of human civilization because of its wide distribution and easy access in nature. As an important building material, it has a long history of mining. In modern industry, limestone is the main raw material for the manufacture of cement, lime, and calcium carbide. It is also an indispensable flux limestone in the metallurgical industry. After superfine grinding, high-quality limestone is widely used. Used in the manufacture of paper, rubber, paint, coating, medicine, cosmetics, feed, sealing, bonding, polishing and other products. According to incomplete statistics, the ratio of limestone and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/18C09D7/12C08F212/08C08F220/18C08F220/06
CPCC08F212/08C08L2201/02C08L2201/08C09D5/18C09D7/61C09D125/14C08L91/06C08K13/02C08K2003/265C08F220/1804C08F220/06
Inventor 张惠元张宇
Owner 苏州远略知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap