High wear-resistant high-tenacity rubber sealing element

A rubber seal, high toughness technology, applied in the sealing field, can solve the problems of poor wear resistance, toughness and high temperature resistance, inability to guarantee the sealing effect of the seal, hidden dangers of vehicle safety, etc., and achieve good elasticity and permanent compression deformation resistance , good elasticity and long service life

Inactive Publication Date: 2017-05-31
安徽亚兰密封件股份有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Automotive fuel pump seals are not only related to the normal use of the fuel pump but also to the safety of the vehicle. In the prior art, there are often problems such as oil leakage caused by the sealing performance of the seals, and even cause certain safety hazards to the vehicle.
The automotive fuel pump seals in the prior art are usually made of nitrile rubber, but nitrile rubber has the defects of poor wear resistance, toughness and high temperature resistance. Long-term use cannot guarantee the sealing effect of the seal, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of high wear-resisting high-toughness rubber sealing piece proposed by the present invention, its raw material comprises by weight: 30 parts of epichlorohydrin rubber, 20 parts of methyl vinyl silicone rubber, 20 parts of nitrile rubber, 12 parts of diatomite, carbonic acid 4 parts of calcium, 4 parts of magnesium oxide, 12 parts of bismuth oxide, 20 parts of barium metaborate, 8 parts of glass microspheres, 8 parts of modified abaca fiber, 2 parts of polydimethylsiloxane, methylphenyldiethyl 6 parts of oxysilane, 4 parts of epoxy fatty acid methyl ester, 3 parts of magnesium stearate, 2 parts of diisononyl phthalate, 1 part of triallyl isocyanurate, 2 parts of zinc diacrylate, 3 parts of dicumyl peroxide.

Embodiment 2

[0018] A kind of high wear-resisting and high-toughness rubber sealing part proposed by the present invention, its raw material comprises by weight: 50 parts of epichlorohydrin rubber, 12 parts of methyl vinyl silicone rubber, 30 parts of nitrile rubber, 6 parts of diatomite, carbonic acid 8 parts of calcium, 2 parts of magnesium oxide, 16 parts of bismuth oxide, 10 parts of barium metaborate, 16 parts of glass microspheres, 4 parts of modified abaca fiber, 4 parts of polydimethylsiloxane, methylphenyldiethyl 3 parts of oxysilane, 8 parts of epoxy fatty acid methyl ester, 1 part of magnesium stearate, 4 parts of diisononyl phthalate, 0.4 part of triallyl isocyanurate, 4 parts of zinc diacrylate, 1.5 parts of dicumyl peroxide.

[0019] The modified abaca fiber is prepared by the following process: the bamboo powder is soaked in sodium hydroxide solution, filtered, dried, and sent to a vacuum box to heat up, keep warm, heat up, keep warm, cool down, wash until it is neutral, add...

Embodiment 3

[0021] A kind of high wear-resisting and high-toughness rubber sealing part proposed by the present invention, its raw material comprises by weight: 35 parts of epichlorohydrin rubber, 18 parts of methyl vinyl silicone rubber, 22 parts of nitrile rubber, 10 parts of diatomaceous earth, carbonic acid 5 parts of calcium, 3.5 parts of magnesium oxide, 13 parts of bismuth oxide, 17 parts of barium metaborate, 10 parts of glass microspheres, 7 parts of modified abaca fiber, 2.5 parts of polydimethylsiloxane, methylphenyldiethyl 5 parts of oxysilane, 5 parts of epoxy fatty acid methyl ester, 2.5 parts of magnesium stearate, 2.5 parts of diisononyl phthalate, 0.8 parts of triallyl isocyanurate, 2.5 parts of zinc diacrylate, 2.5 parts of dicumyl peroxide.

[0022] The modified abaca fiber is prepared by the following process: sending 40 parts of bamboo powder into the sodium hydroxide solution with a concentration of 2mol / L by weight for soaking, filtering, drying, and sending it into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high wear-resistant high-tenacity rubber sealing element which comprises the following raw materials in parts by weight: 30-50 parts of epichlorohydrin rubber, 12-20 parts of methyl vinyl silicone rubber, 20-30 parts of nitrile rubber, 6-12 parts of kieselguhr, 4-8 parts of calcium carbonate, 2-4 parts of magnesium oxide, 12-16 parts of bismuth oxide, 10-20 parts of barium metaborate, 8-16 parts of a glass bead, 4-8 parts of modified aupoz fiber, 2-4 parts of a dimethyl silicone polymer, 3-6 parts of methylphenyldiethoxysilane, 4-8 parts of an epoxidized fatty acid methyl ester, 1-3 parts of magnesium stearate, 2-4 parts of diisononyl phthalate, 0.4-1 part of triallylisocyanurate, 2-4 parts of zinc diacrylate and 1.5-3 parts of dicumyl peroxide. The high wear-resistant high-tenacity rubber sealing element not only has excellent wear resistance and tenacity, but also has very good high temperature resistance, and meanwhile, the sealing element is difficult to age and long in service life.

Description

technical field [0001] The invention relates to the technical field of sealing, in particular to a rubber seal with high wear resistance and high toughness. Background technique [0002] Automotive fuel pump seals are not only related to the normal use of the fuel pump but also to the safety of the vehicle. In the prior art, there are often problems such as oil leakage caused by the sealing performance of the seals, which may cause certain safety hazards to the vehicle. The automotive fuel pump seals in the prior art are usually made of nitrile rubber, but nitrile rubber has the defects of poor wear resistance, toughness and high temperature resistance. Long-term use cannot guarantee the sealing effect of the seal, which needs to be solved urgently. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a high wear-resistant and high-toughness rubber seal, which has excellent wear resistance and tough...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/03C08L83/07C08L9/02C08L97/02C08K13/04C08K7/20C08K3/34C08K3/26C08K3/22C08K5/14C08K5/3492C08K5/098C08K5/5419C08K5/1515C08K5/12
CPCC08L71/03C08K2201/014C08L2201/08C08L2205/025C08L2205/035C08L2205/16C08L83/04C08L9/02C08L97/02C08K13/04C08K7/20C08K3/34C08K2003/265C08K2003/222C08K5/14C08K5/34924C08K5/098C08K3/22C08K5/5419C08K5/1515C08K5/12
Inventor 黄炳喜杨浩
Owner 安徽亚兰密封件股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap