Wearproof antifouling two-component polyurethane paint and preparation method thereof

A two-component polyurethane and coating technology, applied in the field of coatings, can solve the problems of dirt adhesion, affect the appearance, friction of other objects, etc., and achieve the effect of improving anti-fouling, enhancing wear resistance and good film-forming properties

Inactive Publication Date: 2017-06-16
汤子宁
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the paint generally needs to be attached to the outer surface of the object, it will often be rubbed by other objects, or be attached by some dirt, which will affect the appearance, so a wear-resistant and anti-fouling polyurethane paint is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A wear-resistant and anti-fouling two-component polyurethane coating, prepared from the following raw materials in parts by weight (kg): Polyoxypropylene glycol 70, hexamethylene diisocyanate 140, sorbitol 4, ethanolamine 2, acrylate 7 , Dipropylene glycol dibenzoate 5, tert-butyl peroxide tert-valerate 2, cobalt naphthenate 1, polypropylene glycol 12, sub-white corundum fine powder 14, white graphite 6, inulin lauryl aminomethyl Ester 7, tridecafluorooctyltriethoxysilane 3, calcium hypophosphite 4, aluminum titanate 6, polyethylene wax 8, hydroxyethyl methylcellulose 4, sodium methylene dinaphthalene sulfonate 2 , polyoxypropylene glyceryl ether 3, pentaerythritol distearate 5, calcium stearate 7, cetyl polydimethylsiloxane 8, propylene glycol butyl ether 5, polyvinylpyrrolidone 2, appropriate amount of deionized water.

[0016] A method for preparing a wear-resistant and anti-fouling two-component polyurethane coating, comprising the following steps:

[0017] (1) Mix...

Embodiment 2

[0022] A wear-resistant and anti-fouling two-component polyurethane coating, prepared from the following raw materials in parts by weight (kg): polyoxypropylene glycol 75, hexamethylene diisocyanate 145, sorbitol 5, ethanolamine 3, acrylate 8 , Dipropylene glycol dibenzoate 5.5, tert-butyl peroxy tert-valerate 2.5, cobalt naphthenate 1.5, polypropylene glycol 13, sub-white corundum fine powder 15, white graphite 7, inulin lauryl aminomethyl Ester 8, tridecafluorooctyltriethoxysilane 4, calcium hypophosphite 5.5, aluminum titanate 7, polyethylene wax 9, hydroxyethyl methylcellulose 5.5, sodium methylene dinaphthalene sulfonate 2.5 , polyoxypropylene glyceryl ether 4.5, pentaerythritol distearate 6.5, calcium stearate 8, cetyl polydimethylsiloxane 9, propylene glycol butyl ether 6, polyvinylpyrrolidone 3, appropriate amount of deionized water.

[0023] The preparation method is the same as in Example 1.

Embodiment 3

[0025] A wear-resistant and anti-fouling two-component polyurethane coating is characterized in that it is prepared from the following raw materials in parts by weight (kg): polyoxypropylene glycol 80, hexamethylene diisocyanate 150, sorbitol 6, ethanolamine 4 , acrylate 9, dipropylene glycol dibenzoate 6, tert-butyl peroxy tert-valerate 3, cobalt naphthenate 2, polypropylene glycol 14, sub-white corundum fine powder 16, white graphite 8, inulin Lauryl carbamate 9, tridecafluorooctyltriethoxysilane 5, calcium hypophosphite 7, aluminum titanate 8, polyethylene wax 10, hydroxyethyl methylcellulose 7, methylene dinaphthalene Sodium Sulfonate 3, Polyoxypropylene Glyceryl Ether 6, Pentaerythritol Distearate 8, Calcium Stearate 9, Cetyl Dimethicone 10, Propylene Glycol Butyl Ether 7, Polyvinylpyrrolidone 4, Deionized Appropriate amount of water.

[0026] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wearproof antifouling two-component polyurethane paint and a preparation method thereof. The wearproof antifouling two-component polyurethane paint is prepared from the following raw materials by weight: 70-80 parts of polypropylene oxide glycol, 140-150 parts of hexamethylene diisocyanate, 4-6 parts of sorbitol, 2-4 parts of ethanolamine, 7-9 parts of acrylic ester, 5-6 parts of dipropylene glycol dibenzoate, and 2-3 parts of tert-butyl peroxypivalate, etc. According to the invention, polyurethane, acrylic ester and the like are adopted for cooperation to serve as film-forming matters, so that the wearproof antifouling two-component polyurethane paint has good film-forming characteristics. The added sub-white corundum fine powder, white graphite, aluminum titanate and other raw materials can be evenly and stably dispersed in the paint under the action of polypropylene glycol and sodium methylene dinaphthalene sulfonate to enhance the wear resistance of the paint. The added dipropylene glycol dibenzoate, perfluorooctyl triethoxysilane and other raw materials can improve the antifouling and water resistant performance of the paint.

Description

technical field [0001] The invention relates to a coating, in particular to a wear-resistant and antifouling two-component polyurethane coating and a preparation method thereof. Background technique [0002] Polyurethane coatings are currently the most common type of coatings, which can be divided into two-component polyurethane coatings and one-component polyurethane coatings. Two-component polyurethane coatings are generally composed of isocyanate prepolymers and hydroxyl resins, commonly known as curing agent components and main agent components. There are many varieties of this type of coating, and the application range is also very wide. According to the difference of the hydroxyl group-containing components, it can be divided into acrylic polyurethane, alkyd polyurethane, polyester polyurethane, polyether polyurethane, epoxy polyurethane and other varieties. Generally, it has good mechanical properties, high solid content, and good performance in all aspects. It is a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D5/16C09D7/12C08F283/00C08G18/73C08G18/66C08G18/48C08G18/32
CPCC09D151/08C08F283/006C08G18/6688C08G18/73C08L2205/035C09D5/1625C09D5/1662C09D5/1687C08L1/284C08L39/06C08K13/02C08K3/32C08K3/04C08K5/5419C08K5/103
Inventor 汤子宁
Owner 汤子宁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap