Anti-cracking waterproof coating and preparation method thereof

A technology of waterproof coating and silicone acrylic emulsion, which is applied in the field of building materials, can solve problems such as construction difficulties, affecting the service life of buildings, disturbing normal life, work and production order, etc., to reduce raw material consumption and cost, and to achieve good physical isolation and waterproofing Function, save the effect of emulsification production process

Inactive Publication Date: 2017-08-29
肥西县碧涛建材有限公司
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the early days, people used asphalt and asphalt as waterproof materials. The use of this material not only consumes a lot of energy during construction, causes serious environmental pollution, poor adhesion, but also has poor weather resistance. It is easy to become hard and brittle in winter, and easy to stick and melt in summer; This waterproof material has the problems of difficult construction, short service life and poor waterproof performance.
[0003] Most waterproof projects in my country use traditional waterproof materials, which have disadvantages such as poor aging resistance, low tensile strength, and sensitivity to temperature.
Traditional waterproof coatings are used for roof waterproofing, which is easy to cause aging, cracking, deformation, breakage, delamination, etc. When used for indoor waterproofing, it is difficult to construct for places with complex shapes, and it is even more difficult to guarantee the quality of leakage. It takes a lot of money and labor to repair every few years, which not only disrupts people's normal life, work and production order, but also affects the service life of the entire building.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment relates to an anti-crack waterproof coating and its preparation method;

[0030] The anti-cracking waterproof coating is prepared from the following components in parts by weight:

[0031] 36 parts of silicone acrylic emulsion, 13 parts of acrylic resin, 10 parts of ethylene-vinyl acetate copolymer, 9 parts of epoxy resin, 1.2 parts of graphene, 8 parts of glass fiber, 5 parts of methyl cellulose, 3 parts of glass microspheres, high 12 parts of attapulgite clay, 15 parts of glyceryl stearate, 10 parts of filler, 5 parts of defoamer, and appropriate amount of water.

[0032] The high-viscosity attapulgite clay is a product of natural attapulgite clay after purification and thermal activation.

[0033] The filler includes a mixture of light calcium carbonate and white carbon black with a mass ratio of 1:1.

[0034] The defoamer is emulsified silicone oil.

[0035] The method for preparing anti-cracking waterproof coating of the present invention, compri...

Embodiment 2

[0045] This embodiment relates to an anti-crack waterproof coating and its preparation method;

[0046] The anti-cracking waterproof coating is prepared from the following components in parts by weight:

[0047]28 parts of silicone acrylic emulsion, 10 parts of acrylic resin, 7 parts of ethylene-vinyl acetate copolymer, 5 parts of epoxy resin, 0.3 parts of graphene, 5 parts of glass fiber, 3 parts of methyl cellulose, 2 parts of glass beads, high 10 parts of attapulgite clay, 12 parts of glyceryl stearate, 8 parts of filler, 3 parts of defoamer, and appropriate amount of water.

[0048] The high-viscosity attapulgite clay is a product of natural attapulgite clay after purification and thermal activation.

[0049] The filler includes light superfine talc.

[0050] The defoamer is polyoxypropylene glyceryl ether.

[0051] The method for preparing anti-cracking waterproof coating of the present invention, comprises the steps:

[0052] (1) Weigh acrylic resin and ethylene-viny...

Embodiment 3

[0061] This embodiment relates to an anti-crack waterproof coating and its preparation method;

[0062] The anti-cracking waterproof coating is prepared from the following components in parts by weight:

[0063] 39 parts of silicone acrylic emulsion, 18 parts of acrylic resin, 15 parts of ethylene-vinyl acetate copolymer, 12 parts of epoxy resin, 1.8 parts of graphene, 10 parts of glass fiber, 8 parts of methyl cellulose, 5 parts of glass microspheres, high 15 parts of attapulgite clay, 16 parts of glyceryl stearate, 17 parts of filler, 6 parts of defoamer, and appropriate amount of water.

[0064] The high-viscosity attapulgite clay is a product of natural attapulgite clay after purification and thermal activation.

[0065] The filler includes a mixture of light superfine talcum powder and titanium dioxide, and the mass ratio of the two is 1:1.

[0066] The defoamer is a high-carbon alcohol fatty acid ester compound.

[0067] The method for preparing anti-cracking waterpro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides anti-cracking waterproof coating and a preparation method thereof; the anti-cracking waterproof coating comprises silicone-acrylic emulsion, acrylic resin, ethylene-vinyl acetate copolymer, epoxy resin, graphene, glass fiber, methyl cellulose, glass beads, high-viscosity attapulgite clay, glyceryl stearate, a filling agent, and a defoaming agent. The preparation method comprises: subjecting acrylic resin and ethylene-vinyl acetate copolymer to modifying reaction with graphene, adding the remaining components batch by batch, and mixing well to obtain the anti-cracking waterproof coating. The anti-cracking waterproof coating is applicable to the building field, has good waterproof effect and good anti-cracking and anti-peeling effects, provides greatly improved application safety for a building and extended life for the building, and has good applicable value.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a crack-resistant waterproof coating and a preparation method thereof. Background technique [0002] The waterproof problem of buildings is not only related to people's work and living environment, but also affects the service life of buildings. With the rapid development of the national economy, my country's engineering construction is also booming, especially the construction of various projects such as housing, sports facilities, and road traffic, which provide material conditions for improving people's living standards. How to do a good job in various engineering constructions Waterproof and corrosion resistance issues are the most concerned issues of the project construction party. To overcome technical difficulties, we must rely on scientific and technological progress and adopt advanced technologies, including the application of new materials. In the early days,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D133/00C09D123/08C09D163/00C09D7/12
CPCC09D143/04C08L2205/035C09D7/65C09D7/70C08L33/00C08L23/0853C08L63/00C08L1/28C08K13/04C08K7/14C08K3/04C08K7/28C08K3/346
Inventor 俞克波
Owner 肥西县碧涛建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products