Preparation method of antistatic surface protective film, and antistatic surface protective film

A surface protection film and antistatic technology, which is applied in the direction of film/sheet adhesive, conductive coating, optics, etc., can solve the problems of liquid crystal molecular orientation damage, drive IC and other circuit components damage, etc.

Active Publication Date: 2021-04-23
FUJIMORI KOGYO CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In recent years, in the production process of liquid crystal display panels, although the number of occurrences is small, the following phenomenon has occurred: due to the peeling static voltage generated when the surface protective film bonded to the optical film is peeled off Phenomenon in which circuit components such as driver ICs that control the display screen of a liquid crystal display panel are damaged, or the alignment of liquid crystal molecules is damaged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antistatic surface protective film, and antistatic surface protective film
  • Preparation method of antistatic surface protective film, and antistatic surface protective film
  • Preparation method of antistatic surface protective film, and antistatic surface protective film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0163] Nitrogen gas was introduced into a reaction device equipped with a stirrer, a thermometer, a reflux cooler, and a nitrogen introduction pipe, and the air in the reaction device was replaced with nitrogen gas. Afterwards, in reaction unit with the methyl acrylate of 10 weight parts, the 2-ethylhexyl acrylate of 90 weight parts, the acrylate-8-hydroxyoctyl ester of 5.0 weight parts, the polypropylene glycol monoacrylate (n =12) Add 60 parts by weight of solvent (ethyl acetate) together. After that, 0.1 parts by weight of azobisisobutyronitrile as a polymerization initiator was added dropwise over 2 hours, and reacted at 65°C for 6 hours to obtain the acrylic polymer solution of Example 1 with a weight average molecular weight of 500,000. . After adding 8.5 parts by weight of acetylacetone to this acrylic polymer solution and stirring, 2.0 parts by weight of CORONATE HX (isocyanurate body of hexamethylene diisocyanate compound) and 0.1 part by weight of titanium triacetyl...

Embodiment 2～6 and comparative example 1～3

[0165] Except that the composition of the adhesive composition of Example 1 was set as described in Table 1 and Table 2, the adhesive agent combinations of Examples 2 to 6 and Comparative Examples 1 to 3 were obtained in the same manner as in Example 1. things. In Table 1 and Table 2, the monomers (to be copolymerized) contained in the acrylic polymer are (A), (B), (F), and "carboxyl group-containing monomers".

[0166] [Table 1]

[0167]

[0168] [Table 2]

[0169] (D) (E) (F) (H) antistatic agent Example 1 Titanium Chelate (0.1) AA(8.5) F-1(10) - - Example 2 Iron chelate (0.05) AA(6.5) F-1(20) H-1(0.1) - Example 3 Titanium chelate (0.03) AA(4.5) F-2(15) - - Example 4 Titanium chelate (0.03) AA(4.0) F-3(5) H-2(0.1) - Example 5 Iron chelate (0.03) AA(5.0) F-5(10) H-3(0.05) - Example 6 Iron chelate (0.04) EtAcAc(20) F-4(5) H-4(0.1) Comparative example 1 Titanium Chelate (0.1) A...

Embodiment 2

[0186] Except that the adhesive composition of Example 1 is set as the adhesive composition of Example 2, the antistatic agent used for the release agent layer is set as LiCF 3 SO 3 Except that, in the same manner as in Example 1, the antistatic surface protection film of Example 2 was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides an antistatic surface protection film which has excellent anti-peeling static performance, which causes little contamination to an adherend, does not deteriorate over time, and has excellent anti-peeling static properties. An adhesive layer (2) formed of an adhesive composition is formed on one side of the base film (1), and a release film (5) with a release agent layer (4) laminated on the surface is bonded, and the release agent layer (4) ) is transferred to the surface of the adhesive layer (2), and the adhesive composition contains an acrylic polymer, and further contains: (C) an isocyanate compound with a functionality of more than two, (D) a crosslinking accelerator , and (E) keto-enol tautomeric compounds, the acrylic polymer is 1 to 30 parts by weight of (a1), 70 to 99 parts by weight of (a2), and 0.1 to 12 parts by weight (B) is an acrylic polymer of a copolymer obtained by copolymerization, wherein (a1) is a (meth)acrylate monomer having C1-C4 carbon atoms in the alkyl group, and (a2) is a carbon A (meth)acrylate monomer with an atomic number of C5-C18, (B) is a copolymerizable monomer containing a hydroxyl group.

Description

technical field [0001] The present invention relates to an antistatic surface protection film, and in more detail, relates to a preparation method of an antistatic surface protection film with antistatic performance, and an antistatic surface protection film; providing an antistatic surface protection film with less pollution to adherends, And the preparation method of the antistatic surface protection film which does not deteriorate with time and has excellent anti-static stripping performance, and the antistatic surface protection film. Background technique [0002] Production and transportation of optical films such as polarizers, retardation plates, lens films for displays, antireflection films, hard coat films, transparent conductive films for touch panels, and displays using these films At the time of production, a surface protection film is attached to the surface of the optical film to prevent dirt and scratches on the surface in the subsequent process. Regarding th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/30C09D183/04C09D5/20C09D5/24C09J133/14C09J11/06C08F220/18C08F220/28C08F220/14C08G18/62C08G18/73C08G18/75C08G18/76
CPCC09D183/04C09J11/06C09J133/14C08F220/18C08G18/6225C08G18/73C08G18/755C08G18/7642C08K5/56C08L2312/00C08L2205/02C08L2203/16C08L2201/04C09J2467/006C09J2467/005C09J2433/00C09J2483/005C08F220/1809C08F220/1806C08F220/1808C08L83/12C08K3/30C08F220/281C08F220/1804C08F220/58C08F220/14C08F283/06C08F220/1802G02B1/14G02B1/16C09J7/20C09J7/22C09J7/401C09J7/405C09J133/08C09J133/10C09J2301/312
Inventor 长仓毅新见洋人长谷川良吉田弘幸菱沼昌世铃木史惠大津贺健太郎
Owner FUJIMORI KOGYO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com