Preparation method of synthetic leather slurry with flame retardancy, wear resistance and imitation leather feeling

A synthetic leather slurry, wear-resistant technology, applied in fire-resistant coatings, coatings, textiles and papermaking, etc., can solve problems such as human health hazards, environmental pollution, and inability to use organic fertilizers, and achieve the effect of reducing toxicity

Active Publication Date: 2019-04-02
福建中裕新材料技术有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Only a small amount of these discarded feathers are made into pillows, quilts, feather fans, badmintons, etc. Most of them are discarded as garbage, which not only causes environmental pollution, but also causes harm to human health.
Moreover, the main component of discarded feathers is keratin, which is not easy to degrade itself in the soil, and cannot be used directly as an organic fertilizer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] (1) Preparation of flame-retardant thermoplastic polyurethane: In a four-neck flask equipped with a stirring paddle, a thermometer, and a condenser tube of 500ml, mix 80g of polytetrahydrofuran ether glycol and 45g of diphenylmethane diisocyanate, and mix them in trifluoromethylaniline In the presence of 0.12g, react at 85°C for 2h to form a polyurethane prepolymer; add 3.5g of 4-amino-5-hydroxyl-2,7-naphthalene disulfonic acid, 3.5g of mannitol and 3.2g of N-methylolacrylamide, reacted at 85°C for 3h, added 2.4g of tetraisopropyl titanate, reacted at 70°C for 1h, added 9g of triethylamine for neutralization reaction for 60min, added deionized under high-speed stirring 100g of water was emulsified and dispersed, and 3.1g of tetrafluoroethylene, 1.6g of vinylidene fluoride and 1.5g of iodobenzene diacetate were added to the system, and 5.3g of 10% aqueous initiator solution was added dropwise at 80°C (the following initiator agent as a single substance) and 6.6g of chick...

example 2

[0029] (1) Preparation of flame-retardant thermoplastic polyurethane: In a four-neck flask equipped with a stirring paddle, a thermometer, and a condenser tube of 500ml, mix 80g of polytetrahydrofuran ether glycol and 45g of diphenylmethane diisocyanate, and mix them in p-nitrobenzyl alcohol In the presence of magnesium malonate monoester 0.12g, react at 85°C for 2h, polyurethane prepolymer; add 3.5g of 4-amino-5-hydroxy-2,7-naphthalene disulfonic acid to the polyurethane prepolymer , 3.5g of mannitol and 3.2g of N-methylolacrylamide, reacted at 85°C for 3h, added 2.4g of zirconium acetate, reacted at 70°C for 1h, added 9g of triethylamine for neutralization reaction for 60min, added under high-speed stirring 100g of deionized water was emulsified and dispersed, and 3.1g of tetrafluoroethylene, 1.6g of vinylidene fluoride and 1.5g of iodobenzene diacetate were added to the system, and 5.3g of 10% aqueous initiator solution and chicken feather hydrolysis were added dropwise at 8...

example 3

[0034] (1) Preparation of flame-retardant thermoplastic polyurethane: In a four-necked flask equipped with a stirring paddle, a thermometer, and a condenser tube of 500ml, mix 80g of polytetrahydrofuran ether diol and 45g of diphenylmethane diisocyanate, and dibenzyl maleate In the presence of 0.12g of ester, react at 85°C for 2h to form a polyurethane prepolymer; add 3.5g of 4-amino-5-hydroxy-2,7-naphthalene disulfonic acid and 3.5g of mannitol to the polyurethane prepolymer React with 3.2g of N-methylolacrylamide at 85°C for 3h, add 2.4g of phenyltriethoxysilane, react at 70°C for 1h, add 9g of triethylamine for neutralization reaction for 60min, add under high-speed stirring 100g of deionized water was emulsified and dispersed, and 3.1g of tetrafluoroethylene, 1.6g of vinylidene fluoride and 1.5g of iodobenzene diacetate were added to the system, and 5.3g of 10% aqueous initiator solution and chicken feather hydrolysis were added dropwise at 80°C. Liquid 6.6g and hexamethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wear resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of flame-retardant, anti-abrasion and leather-feeling simulation synthetic leather paste. The preparation method includes: mixing 80g of polytetrahydrofuran glycol with 45g of methylene diphenyl diisocyanate and allowing polyurethane prepolymer to occur in the reaction of 2 hours under 85DEG C in the presence of 0.12g of a catalyst; adding 4-amino-5-hydroxy-2, 3.5g of 7-naphthalene disulfonic acid, 3.5g of mannitol and 3.2g of N-hydroxymethyl acrylamide, dropwise adding 5.3g of 10% of an initiator aqueous solution and 6.6g of a chicken feather solution simultaneously at 80DEG C for 1 hour, performing thermal reaction for 2 hours after dropwise adding and adjusting pH value to be 7.5 after completion of reaction to obtain flame-retardant thermoplastic polyurethane; proportionally and evenly stirring 60 parts of the flame-retardant thermoplastic polyurethane, 15 parts of butanone, an HDI tripolymer curing agent and a bismuth quantitative catalyst to prepare the colorless and high-transparent paste. The synthetic leather paste is good in flame-retardant, anti-abrasion and leather-feeling simulation properties.

Description

technical field [0001] The invention relates to a method for preparing synthetic leather, in particular to a method for preparing synthetic leather slurry with flame retardancy, wear resistance and artificial leather feeling. Background technique [0002] Polyurethane synthetic leather has the characteristics of soft and natural luster, soft hand feeling, strong leather feeling, resistance to warping, anti-aging, etc. It is the most ideal substitute for natural leather and is widely used in clothing, shoemaking, bags, furniture and other industries , but the polyurethane synthetic leather currently on the market is far behind natural leather in terms of moisture permeability and wear resistance. Polyurethane synthetic leather products with poor moisture permeability will make people feel stuffy and cold. The properties of synthetic leather sizing are improved, but the process of changing the moisture permeability and wear resistance of polyurethane synthetic leather sizing i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D151/08C09D5/18C09D7/65C09D7/63C08F283/00C08G18/10C08G18/16C08G18/18C08G18/22C08G18/48C08G18/66C08G18/67C08G18/76D06N3/14D06N3/00
CPCC08F283/008C08G18/10C08G18/163C08G18/1825C08G18/1875C08G18/222C08G18/4854C08G18/6677C08G18/6681C08G18/6715C08G18/7671C08L2201/02C09D5/18C09D151/08D06N3/0059D06N3/0061D06N3/14D06N2209/067D06N2209/1685D06N2211/28C08G18/3855C08G18/3206C08F214/26C08F214/22C08L89/00C08K5/549
Inventor 乐建军姜慧向宇黄娇