Construction waste sintering-free brick and preparation method thereof

A technology for construction waste and non-burning bricks, which is applied in clay preparation devices, chemical instruments and methods, manufacturing tools, etc., can solve the problems of unsatisfactory properties such as strength, heat preservation, and energy saving of non-burning bricks, and saves maintenance costs and manpower. cost, improved utilization, and the effect of a wide range of applications

Inactive Publication Date: 2017-11-03
合肥一片美环保科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The construction waste unburned brick overcomes the problem that the current unburned brick's strength, heat preservation, energy saving and other properties cannot meet the needs of modern industrial development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment provides a construction waste unburned brick, which includes the following raw materials in parts by weight: 23 parts of basalt powder, 18 parts of glass powder, 28 parts of arsenic sandstone, 23 parts of construction waste, active 2 parts of white clay waste residue, 7 parts of vermiculite, 12 parts of high alumina fine powder, 14 parts of cement, 3 parts of calcium oxide, 4 parts of stabilizer, and 1 part of gelling agent. Wherein, the gelling agent includes the following components by weight percentage: 30% of ordinary Portland cement, 26% of lime, 21% of magnesium sulfate, and 170% of sodium silicate. Wherein, the lime component is composed of calcium oxide and calcium hydroxide.

[0026] Wherein, the construction waste is a mixture of yellow sand, gravel, block stone, slag, scrap steel bar, scrap iron wire, various scrap steel fittings, metal pipeline scrap, scrap bamboo and wood, sawdust, and wood shavings. The construction waste has been acidifie...

Embodiment 2

[0035] This embodiment provides a kind of unburned construction waste brick, which includes the following raw materials in parts by weight: 25 parts of basalt powder, 16 parts of glass powder, 46 parts of arsenic sandstone, 15 parts of construction waste, active 3 parts of clay waste residue, 5 parts of vermiculite, 14 parts of high alumina fine powder, 11 parts of cement, 6 parts of calcium oxide, 2 parts of stabilizer, and 2 parts of gelling agent. Wherein, the gelling agent includes the following components by weight percentage: 25% of ordinary Portland cement, 30% of lime, 18% of magnesium sulfate, and 20% of sodium silicate. Wherein, the lime component is composed of calcium oxide and calcium hydroxide.

[0036] Wherein, the construction waste is a mixture of yellow sand, gravel, block stone, slag, scrap steel bar, scrap iron wire, various scrap steel fittings, metal pipeline scrap, scrap bamboo and wood, sawdust, and wood shavings. The construction waste has been acidif...

Embodiment 3

[0045] This embodiment provides a kind of unburned construction waste brick, which includes the following raw materials in parts by weight: 20 parts of basalt powder, 29 parts of glass powder, 25 parts of arsenic sandstone, 28 parts of construction waste, active 1 part of clay waste residue, 11 parts of vermiculite, 9 parts of high alumina fine powder, 15 parts of cement, 1 part of calcium oxide, 5 parts of stabilizer, and 1 part of gelling agent. Wherein, the gelling agent includes the following components by weight percentage: 40% of ordinary Portland cement, 23% of lime, 30% of magnesium sulfate, and 15% of sodium silicate. Wherein, the lime component is composed of calcium oxide and calcium hydroxide.

[0046]Wherein, the construction waste is a mixture of yellow sand, gravel, block stone, slag, scrap steel bar, scrap iron wire, various scrap steel fittings, metal pipeline scrap, scrap bamboo and wood, sawdust, and wood shavings. The construction waste has been acidified ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of energy-saving construction materials and provides a construction waste sintering-free brick and a preparation method thereof. The construction waste sintering-free brick comprises the following raw materials in parts by weight: 20-25 parts of basalt powder, 16-29 parts of glass powder, 25-46 parts of arsenic rock, 15-28 parts of construction wastes, 1-3 parts of activated clay waste residues, 5-11 parts of vermiculite, 9-14 parts of high-bauxite fine powder, 11-15 parts of cement, 1-6 parts of calcium oxide, 2-5 parts of a stabilizing agent and 1-2 parts of a gelatinizing agent. The invention aims to provide the construction waste sintering-free brick and the preparation method thereof; the construction waste sintering-free brick overcomes the defect that the strength, the thermal insulation, the energy conservation and other performances of an existing sintering-free brick cannot meet the demands on modern industrial development.

Description

technical field [0001] The invention belongs to the technical field of energy-saving building materials, in particular, a non-burning brick for construction waste and a preparation method thereof. Background technique [0002] A new type of wall material produced by high-temperature calcination is called unfired brick. This product complies with China's "protection [0003] Farmland, energy conservation, adapting measures to local conditions, and local materials" is the general policy for the development of building materials. With the continuous deepening of the reform and opening up policy, the continuous development of the market economy, and the rapid development of urban construction, various municipal projects, public facilities, high-rise buildings, and civil buildings , Housing projects will rise from the ground and will require a large number of new wall materials. However, the existing unburned bricks have properties such as strength, heat preservation, and energy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00B28B3/00B28B11/24B28C5/08
CPCC04B28/00B28B3/00B28B11/245B28C5/08C04B2201/32C04B2201/50C04B14/14C04B14/22C04B14/02C04B18/16C04B18/04C04B14/202C04B14/303C04B22/064C04B2103/0068C04B7/04C04B22/142C04B12/04
Inventor 汪知明
Owner 合肥一片美环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com