Preparation method of water-soluble N-P-codoping carbon dot

A carbon quantum dot and co-doping technology, applied in chemical instruments and methods, luminescent materials, etc., can solve the problems of unfavorable continuous and large-scale production of fluorescent carbon quantum dots, non-renewable energy, low carbon quantum yield, etc. The effect of abundant source, stable fluorescence and high quantum yield

Inactive Publication Date: 2017-11-03
GUANGXI TEACHERS EDUCATION UNIV
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method often requires strict experimental conditions and special energy sources, the cost is high, and the obtained carbon quantum yield is relatively low
Bottom-up synthesis method, that is, direct synthesis of fluorescent carbon quantum dots by pyrolysis or carbonization of suitable p...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-soluble N-P-codoping carbon dot
  • Preparation method of water-soluble N-P-codoping carbon dot
  • Preparation method of water-soluble N-P-codoping carbon dot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of water-soluble nitrogen and phosphorus co-doped carbon quantum dots, comprising the following steps:

[0029] Step 1. In step 1, dissolve 0.2g p-aminobenzenesulfonic acid in 20mL ultrapure water to prepare a precursor solution, and uniformly mix tetrakishydroxymethylphosphine chloride and the precursor solution at a volume ratio of 1:10 to obtain a mixed solution ;

[0030] Step 2. Stir the mixed solution prepared in step 1 evenly, put it into the polytetrafluoroethylene liner of the hydrothermal synthesis reaction kettle, and then place the hydrothermal synthesis reaction kettle in a constant temperature box for heating to obtain a light yellow solution. The temperature of the incubator is 180°C, and the reaction time is 6h;

[0031] Step 3, filter the light yellow solution obtained in step 2 to obtain the filtrate, then dialyze the filtrate, use a dialysis bag with a shear molecular weight of 1000, dialyze for 72 hours to obtain a dialysate, an...

Embodiment 2

[0033] A preparation method of water-soluble nitrogen and phosphorus co-doped carbon quantum dots, comprising the following steps:

[0034] Step 1. In step 1, dissolve 0.2g p-aminobenzenesulfonic acid in 20mL ultrapure water to prepare a precursor solution, and uniformly mix tetrakishydroxymethylphosphine chloride and the precursor solution at a volume ratio of 1:12 to obtain a mixed solution ;

[0035] Step 2. Stir the mixed solution prepared in step 1 evenly, put it into the polytetrafluoroethylene liner of the hydrothermal synthesis reaction kettle, and then place the hydrothermal synthesis reaction kettle in a constant temperature box for heating to obtain a light yellow solution. The temperature of the incubator is 180°C, and the reaction time is 6h;

[0036] Step 3, filter the light yellow solution obtained in step 2 to obtain the filtrate, then dialyze the filtrate, use a dialysis bag with a shear molecular weight of 1000, dialyze for 72 hours to obtain a dialysate, an...

Embodiment 3

[0038] A preparation method of water-soluble nitrogen and phosphorus co-doped carbon quantum dots, comprising the following steps:

[0039] Step 1. In step 1, dissolve 0.2g p-aminobenzenesulfonic acid in 20mL ultrapure water to prepare a precursor solution, and uniformly mix tetrakishydroxymethylphosphine chloride and the precursor solution at a volume ratio of 1:14 to obtain a mixed solution ;

[0040] Step 2. Stir the mixed solution prepared in step 1 evenly, put it into the polytetrafluoroethylene liner of the hydrothermal synthesis reaction kettle, and then place the hydrothermal synthesis reaction kettle in a constant temperature box for heating to obtain a light yellow solution. The temperature of the incubator is 180°C, and the reaction time is 6h;

[0041] Step 3, filter the light yellow solution obtained in step 2 to obtain the filtrate, then dialyze the filtrate, use a dialysis bag with a shear molecular weight of 1000, dialyze for 72 hours to obtain a dialysate, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a water-soluble N-P-codoping carbon dot. The preparation method comprises the following steps of (1) dissolving sulfanilic acid into ultrapure water to prepare a precursor solution, and uniformly mixing tetrahydroxymethyl phosphonium chloride and the precursor solution according to the volume ratio of 1:(10 to 20) to obtain a mixed solution; (2) carrying out hydrothermal reaction on the mixed solution prepared in the step (1), and thus obtaining the water-soluble N-P-codoping carbon dot. According to the preparation method of the water-soluble N-P-codoping carbon dot provided by the invention, the water-soluble N-P-codoping carbon dot is prepared by adopting a one-step hydrothermal method, the carbon source is rich and cheap, the preparation process is simple and easy, the whole preparation process is free of pollution and toxicity, and is green and environmentally friendly, and preparation in large scale can be realized.

Description

technical field [0001] The invention relates to the field of preparation of nanometer materials. More specifically, the present invention relates to a preparation method of water-soluble nitrogen and phosphorus co-doped carbon quantum dots. Background technique [0002] In recent years, fluorescent carbon nanomaterials have attracted extensive research by researchers because of their good optical properties and low cytotoxicity. It has good photostability and no toxic side ions, is suitable for long-term detection and tracing experiments, and has broad application prospects in biomarkers and analysis and detection. Carbon quantum dots (CQDs) exhibit excellent properties such as hydrophilicity, low cytotoxicity, chemical and photostability, etc., which have attracted extensive attention and applications in the fields of chemistry, biomedicine, sensing and optoelectronics. [0003] There are currently two main methods for preparing carbon quantum dots: top-down method and bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K11/65
CPCC09K11/70
Inventor 黄珊肖琦杨二利刘义
Owner GUANGXI TEACHERS EDUCATION UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap