Aqueous industrial coating material and production method thereof

An industrial and coating technology, applied in coatings and other directions, can solve the problems of water-based industrial coatings production and application performance gap, chemical properties and flexibility are not well solved, etc., to achieve excellent leveling and gloss, significant The effect of adhesion, strong adhesion

Inactive Publication Date: 2017-12-22
浙江华用材料技术有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Both have their own advantages and disadvantages, but relatively speaking, the most fundamental thing is that the comprehensive performance of all aspects of water-based industrial coatings needs to be further improved.
The subsequent water-based industrial coatings use the compound of acrylic acid and water-based polyurethane as the main raw material, which not only inherits the advantages of acrylic products in weather resistance and good construction tolerance, but also improves the hardness of water-based industrial coatings, but the chemical properties and flexibility are still the same. not well resolved
In addition, the main reason restricting the production and application of water-based industrial coatings is that there is still a gap between the performance of water-based industrial coatings and the performance of similar solvent-based industrial coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous industrial coating material and production method thereof
  • Aqueous industrial coating material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] raw material:

[0025] 30 parts of silicone modified acrylic resin, 10 parts of methyl etherified melamine formaldehyde resin, 0.1 part of polyether modified polyorganosiloxane, 0.1 part of defoamer, 0.1 part of leveling agent, 5 parts of methanol, 5 parts of ether, 35 parts of deionized water.

[0026] production method:

[0027] S1. According to the above formula, put silicone-modified acrylic resin, methyl etherified melamine formaldehyde resin, methanol and ether into the dispersion container, stir while feeding, control the speed at 400-600 rpm, stir for 5-20 minutes, Obtain a uniform mixed solution;

[0028] S2, then add polyether modified polyorganosiloxane, defoamer, leveling agent, deionized water to the mixed solution, stir while feeding, control the speed at 400-600 rpm, stir for 5-20 Minutes, and then filtered, packaged, and put into storage to obtain water-based industrial coatings.

Embodiment 2

[0030] raw material:

[0031] 35 parts of silicone modified acrylic resin, 12 parts of methyl etherified melamine formaldehyde resin, 0.5 part of octyl succinic acid sulfonate, 0.5 part of defoamer, 0.5 part of leveling agent, 6 parts of ethanol, 6 parts of dipropyl ether, 40 parts of deionized water.

[0032] Above water-based industrial paint production method is the same as embodiment 1.

Embodiment 3

[0034] raw material:

[0035] 38 parts of silicone modified acrylic resin, 14 parts of methyl etherified melamine formaldehyde resin, 1.5 parts of perfluoroalkane sulfonate, 1.5 parts of defoamer, 1.5 parts of leveling agent, 8 parts of alcohol solvent (ethylene glycol and propylene glycol , the mass ratio is 1:1), 8 parts of diisopropyl ether, and 45 parts of deionized water.

[0036] Above water-based industrial paint production method is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an aqueous industrial coating material and a production method thereof, wherein the raw materials comprise, by weight, 30-40 parts of an organic silicon modified acrylic resin, 10-15 parts of a methylated melamine formaldehyde resin, 0.1-2.0 parts of a wetting agent, 0.1-2.0 parts of an anti-foaming agent, 0.1-2.0 parts of a leveling agent, 5-10 parts of an alcohol-based solvent, 5-10 parts of an ether-based solvent, and 35-50 parts of deionized water. According to the present invention, the aqueous industrial coating material has characteristics of no environment pollution, remarkably strong adhesion, excellent leveling property, excellent gloss and the like, is the high-performance aqueous industrial coating material, further has advantages of excellent flexibility, excellent water resistance, excellent damp heat resistance, excellent chemical resistance, excellent salt spray resistance and easy construction, and is suitable for the automated spraying line of the industrial production of metal work-pieces.

Description

technical field [0001] The invention belongs to the technical field of processing PE water supply pipes, and in particular relates to a water-based industrial paint suitable for treating metal surfaces and a production method thereof. Background technique [0002] Objects are exposed to the atmosphere and are corroded by oxygen, moisture, etc., which are likely to cause damage such as metal corrosion, wood decay, and cement weathering. According to statistics, the metals due to rust and corrosion each year in the world account for about 20% of the annual output, and the annual economic losses caused by corrosion in my country account for about 4% of GDP, and the losses even exceed the sum of various natural disasters. And coating the surface of the object to form a protective film can prevent or delay the occurrence and development of these damage phenomena, and prolong the service life of various materials. Coatings can be coated on the surface of objects by different cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D161/32C09D7/12C09D7/00
CPCC08L2201/08C08L2205/03C09D143/04C08L61/32C08L83/12C08K5/42
Inventor 胡欣汉徐勤胡志旺
Owner 浙江华用材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap