Wear-resisting artificial color sand and preparation method thereof

A colored sand and artificial technology, which is applied in the field of wear-resistant artificial colored sand and its preparation, can solve the problems of poor alkali resistance and water resistance, and poor wear resistance, and achieve strong water resistance, strong alkali resistance and low price Effect

Active Publication Date: 2017-12-29
安徽好思家涂料股份有限公司 +1
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of poor wear resistance, alkali resistance and water resistance in the existing artificial colored sand, to provide a wear-resistant artificial colored sand and its preparat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing artificial colored sand, comprising the following steps:

[0023] (1) Preparation of aluminum dihydrogen phosphate: the mass ratio of phosphoric acid to aluminum hydroxide is 4:1, first add phosphoric acid to a three-necked flask equipped with a constant speed stirrer, reflux condenser, and thermometer and heat the temperature to 90-100 ℃, then slowly add aluminum hydroxide into the flask, the rotation speed is 500r / min, keep the temperature for 2h, after the reaction is complete, aluminum dihydrogen phosphate solution is obtained, and set aside;

[0024] (2) Take water glass with a solid content of 54.8% according to the mass ratio of 1:10 and mix well with the above-mentioned aluminum dihydrogen phosphate solution, and then add 1 / 3 of the mixed solution to dilute to obtain an inorganic binder;

[0025] (3) Preparation of polymer dispersant: use water as solvent, maleic anhydride (MA), acrylic acid (AA), butyl acrylate (BA) as monomers, ammonium ...

Embodiment 2

[0029] The preparation method of this embodiment is the same as that of Example 1, except that the sand grains are 40-80 mesh, and the binder in 4500g of Example 1.

Embodiment 3

[0031] The preparation method of this example is the same as that of Example 2, except that 7000g of iron red paste (containing 1000g of iron red) is used.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses wear-resisting artificial color sand and a preparation method thereof. The wear-resisting artificial color sand is prepared from raw materials in parts by mass as follows: 1000 parts of sand grains, 30-60 parts of a binding agent, 5-20 parts of inorganic pigment, 0.1-2 parts of a polymeric dispersant, 1-5 parts of borax and 30-80 parts of water, wherein the binding agent is an inorganic binding agent prepared from an aluminium dihydrogen phosphate solution and sodium silicate through mixing; the polymeric dispersant is a terpolymer dispersant prepared from water as a solvent, maleic anhydride (MA), acrylic acid (AA) and butyl acrylate (BA) as monomers, ammonium persulfate as an initiator and isopropyl alcohol as a chain transfer agent. A product has quite high wear resistance, is not dissolved in acid and alkali and has pure and stable color, the color sand in required color can be formed by mixing color sand in different colors and different mass ratios, and demands of the real stone paint market are met better; the preparation method is convenient to operate, the sintering temperature is low, and the preparation method has the advantages of being energy-saving, environmentally friendly and low in cost.

Description

technical field [0001] The invention relates to the field of functional sand materials, in particular to a wear-resistant artificial colored sand and a preparation method thereof. Background technique [0002] As a surface decoration material, colored sand has the advantages of bright colors, stable performance and environmental protection, and has been widely used in the field of architectural decoration. In recent years, due to the development of the construction industry, the market demand for colored sand is increasing. The limited reserves of natural colored sand can no longer meet the market demand. At the same time, natural colored sand is obtained by directly crushing natural colored ores. Most of them are chaotic in color, poor in strength, and easy to differentiate; while brightly colored colored sand is rare and expensive. Compared with natural colored sand, artificial colored sand has stable properties and convenient color matching. By changing the ratio of pigm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B14/06
Inventor 张勇涛王芳刘雪霆刘长明
Owner 安徽好思家涂料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap