Method for preparing molybdenum silicide coating on surface of molybdenum or molybdenum alloy

A technology of molybdenum alloy and molybdenum silicide, which is applied in the field of high-temperature protective coatings, can solve the problems of further improvement and large difference in thermal expansion coefficients, and achieve good high-temperature oxidation resistance, reduce thermal expansion coefficient mismatch, and high efficiency.

Active Publication Date: 2018-02-09
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, MoSi prepared by a single plasma spraying technique 2 The bonding mode between the coating and the Mo matrix is ​​mainly mechanical occlusion, and there is a relatively obvious interface. Due to the large differe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing molybdenum silicide coating on surface of molybdenum or molybdenum alloy
  • Method for preparing molybdenum silicide coating on surface of molybdenum or molybdenum alloy
  • Method for preparing molybdenum silicide coating on surface of molybdenum or molybdenum alloy

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Preparation of silicon coating. Specifically, silicon powder with a certain particle size distribution and purity is selected, and a silicon coating with a certain thickness is prepared on the surface of molybdenum or molybdenum alloy by plasma spraying technology. Among them, the particle size of the selected silicon powder is 10-120 μm, and the purity is greater than 98 wt.%. Dry the silicon powder at 100-120°C for 1 to 3 hours for later use. The silicon powder is sprayed onto the surface of molybdenum or molybdenum alloy by plasma spraying technology to form a silicon coating, and the thickness of the silicon coating is 30-300 μm. The process parameters of plasma sprayed silicon coating include: plasma gas Ar: 30-50 slpm (standard liters / minute); plasma gas H 2 : 6~15slpm; powder carrier gas Ar: 2~7slpm; spraying distance: 100~200mm; spraying power: 30~50kW; powder feeding rate: 10~30rpm (revolutions per minute). By controlling the process parameters of the plasma s...

Example Embodiment

[0038] Example 1

[0039] A molybdenum silicide coating on the surface of molybdenum metal. The preparation of the coating includes the following steps:

[0040] 1) Sandblasting the surface of the Mo metal substrate with a sandblasting pressure of 0.4MPa, sonicating 2 times in anhydrous ethanol solution for 5 minutes each time, drying at 100°C for 2 hours, standby;

[0041] 2) Choose silicon powder with a median particle size of about 30μm and a purity of greater than 98wt.% as the spraying raw material, and dry it at 100°C for 3 hours, for use;

[0042] 3) Using a plasma spraying system (A-2000, Sulzer Metco AG, Switzerland), using the process parameters in Table 2 to spray silicon powder on the surface of the Mo substrate to form a silicon coating, the thickness of the silicon coating is about 110μm, figure 1 The XRD results show that the silicon coating is cubic phase;

[0043] Table 2 shows the process parameters of plasma sprayed Si coating:

[0044]

[0045] 4) A vacuum-atmosphere ...

Example Embodiment

[0060] Example 2

[0061] A molybdenum silicide coating on the surface of molybdenum metal. The preparation of the coating includes the following steps:

[0062] 1) Sandblasting the surface of the Mo metal substrate with a sandblasting pressure of 0.4MPa, sonicating 2 times in anhydrous ethanol solution for 5 minutes each time, drying at 100°C for 2 hours, standby;

[0063] 2) Choose silicon powder with a median particle size of about 30μm and a purity of greater than 98wt.% as the spraying raw material, and dry it at 100°C for 3 hours, for use;

[0064] 3) Using plasma spraying technology, select the process parameters in Table 4, spray silicon powder on the surface of the Mo substrate to form a silicon coating, the thickness of the silicon coating is about 60μm, and the silicon coating is cubic phase;

[0065] Table 4 shows the process parameters of plasma sprayed Si coating:

[0066]

[0067]

[0068] 4) A vacuum-atmosphere sintering furnace protected by argon gas is used to make a di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a molybdenum silicide coating on the surface of molybdenum or a molybdenum alloy. Silicon powder serves as a raw material, a plasma spraying technologyis adopted to prepare the silicide coating on the surface of the molybdenum or a molybdenum alloy matrix, then, heat treatment is carried out for 1-10 hours under the inert atmosphere at the temperature of 1,000 DEG C-1,500 DEG C, and therefore the molybdenum silicide coating is formed on the surface of the molybdenum or the molybdenum alloy. The preparation method has the advantages that the process is simple, the cost is low, the efficiency is high, repeatability is good, and method is suitable for scale production.

Description

technical field [0001] The invention relates to a method for preparing a silicide coating, in particular to a method for preparing a molybdenum silicide coating on the surface of molybdenum or a molybdenum alloy, and belongs to the technical field of high-temperature protective coatings. Background technique [0002] Molybdenum (Mo) and its alloys are one of the important high-temperature structural materials. However, when the temperature of the aerobic environment is about 500 ° C, Mo will be oxidized, and as the temperature increases, the degree of oxidation will intensify, and the formed oxide (MoO 3 ) is easy to volatilize, leading to the loose structure of Mo, which eventually leads to material failure, which greatly limits the application of Mo as a high-temperature material. In order to improve its high temperature and oxidation resistance, a more feasible method is to prepare a high temperature and oxidation resistance coating on its surface. [0003] Molybdenum d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C4/134C23C4/10C23C4/18
CPCC23C4/10C23C4/134C23C4/18
Inventor 牛亚然翟翠红赵君李红郑学斌孙晋良丁传贤
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap