White marble sand composite resin material and preparation method thereof

A technology of composite resin and white marble, which is applied in the field of white marble sand, can solve the problems of affecting the stability and strength of finished composite materials, poor compatibility of resin matrix, and easy formation of agglomeration, so as to improve compatibility, improve heat resistance stability, reduce The effect of reunion

Inactive Publication Date: 2018-02-23
宿松汉邦新型建材有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] White marble sand is an important industrial mineral raw material, non-chemical dangerous goods, widely used in glass, casting, ceramics and refractory materials, smelting ferrosilicon, metallurgical flux, metallurgy, construction, chemical industry, plastics, rubber, abrasives and other industries; white marble sand i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A white marble sand composite resin material, which is composed of the following parts by weight of raw materials:

[0020] White marble sand 40, polypropylene 70, tribasic lead sulfate 0.5, polyethylene wax 5, octyl isothiazolinone 2, ditetradecyl alcohol ester 4, 1-hydroxyethyl-2-oleyl imidazoline 0.2, Zinc ricinoleate 2, glyceryl monostearate 1, stannous caprylate 1, ethoxylated alkylphenol ammonium sulfate 3, carbon nanotubes 12, cellulose phosphate 9.

[0021] A preparation method of white marble sand composite resin material includes the following steps:

[0022] (1) Take the carbon nanotubes, add them to the mixed acid solution of 30 times its weight, heat and stir at 60°C for 2 hours, filter, wash the precipitate with water, and dry at room temperature to obtain activated carbon nanotubes;

[0023] (2) Take zinc ricinoleate and add it to 7 times its weight in absolute ethanol, stir evenly, add white marble sand, keep at 70℃ and stir for 40 minutes, add...

Example Embodiment

[0029] Example 2

[0030] A white marble sand composite resin material, which is composed of the following parts by weight of raw materials:

[0031] White marble sand 30, polypropylene 60, tribasic lead sulfate 0.3, polyethylene wax 4, octyl isothiazolinone 1, tetradecyl alcohol ester 2, 1-hydroxyethyl-2-oleyl imidazoline 0.1, Zinc ricinoleate 1, glyceryl monostearate 0.5, stannous caprylate 0.3, ethoxylated alkylphenol ammonium sulfate 2, carbon nanotube 10, cellulose phosphate 6.

[0032] A preparation method of white marble sand composite resin material includes the following steps:

[0033] (1) Take carbon nanotubes, add them to a mixed acid solution of 20 times their weight, keep them at 50°C and stir for 1 hour, filter, wash the precipitate with water, and dry at room temperature to obtain activated carbon nanotubes;

[0034] (2) Take zinc ricinoleate and add it to 4 times its weight in absolute ethanol, stir evenly, add white jade sand, keep at 60℃ and stir for 30 minutes, add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a white marble sand composite resin material. The white marble sand composite resin material comprises the following raw materials in parts by weight: 30 to 40 parts of white marble sand, 60 to 70 parts of polypropylene, 0.3 to 0.5 part of lead sulfate tribasic, 4 to 5 parts of polyethylene wax, 1 to 2 parts of octyl isothiazolinone, 2 to 4 parts of double decarboxyl alcohol ester, 0.1 to 0.2 part of 1-ethoxy-2-oleic imidazoline, 1 to 2 parts of zinc diricinoleate, 0.5 to 1 part of glycerin monostearate, 0.3 to 1 part of stannous octoate, 2 to 3 parts of ethoxylated alkyl phenol ammonium sulfate, 10 to 12 parts of a carbon nano-tube and 6 to 9 parts of phosphorylated cellulose. The lead sulfate tribasic, the stannous octoate and the zinc diricinoleate are added, sothat the heat-resistant stability of the finished product is effectively improved and the comprehensive performance of the finished product is improved.

Description

technical field [0001] The invention belongs to the field of white marble sand, and in particular relates to a white marble sand composite resin material and a preparation method thereof. Background technique [0002] The main component of white marble is calcium carbonate, which is mainly composed of CaCO3, MgCO3 and SiO2, and also contains a small amount of Al2O3, Fe2O3 and other components. It belongs to fine-grained marble with white color and hard quality. It is a first-class building and carving material. Basically it is not soluble in water. It can exist in the following forms: aragonite, calcite, chalk, limestone, marble, travertine, and can be found in rocks. The main component of animal back shells and snail shells. At the same time, it is also an important building material. White marble is hard and white. The output of white marble accounts for about 30% of all marble production; white marble sand is processed by multiple processes such as selection, crushin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L1/16C08K13/06C08K9/04C08K7/24C08K5/47C08K3/30C08K3/26
CPCC08L23/12C08K2003/265C08K2003/3045C08K2201/011C08L2201/08C08L2205/03C08L23/06C08L1/16C08K13/06C08K9/04C08K7/24C08K5/47C08K3/30C08K3/26
Inventor 何其
Owner 宿松汉邦新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap