Antibacterial and oil-resistant rubber material for baseball core

A technology of oil-resistant rubber and baseball cores, applied in the field of rubber, can solve the problems of reducing the quality and safety of baseballs, poor antibacterial and oil resistance, and reducing the service life of baseballs

Inactive Publication Date: 2018-02-23
天长市良文运动器材有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The baseballs used in soft baseball are divided into hollow balls and solid balls. The core material of solid balls is generally synthetic rubber, while the synthetic rubber in the prior art has poor antibacterial and oil resistance, which seriously reduces the quality and safety of the baseball. It also reduces the service life of the baseball

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An antibacterial and oil-resistant rubber material for a baseball core proposed by the present invention, its raw materials include by weight: 45 parts of ABS resin, 20 parts of organic fluorine epoxy resin, 6 parts of urea-formaldehyde resin, 6 parts of epichlorohydrin rubber, and 46 parts of acrylic resin , 4 parts of vulcanizing agent TCY, 4.5 parts of trioctyl trimellitate, 3 parts of accelerator TT, 4 parts of accelerator BPP, 7 parts of epichlorohydrin, 4.5 parts of zeolite, 3 parts of calcium molybdate, 4 parts of wrought white powder , 4 parts of zeolite powder, 3 parts of nitrocellulose, 3 parts of trimethyl phosphate, 3 parts of cellulose hydroxyethyl ether, 6 parts of zinc stearate, 4.5 parts of fluorine micropowder, 5 parts of highly active magnesium oxide, 4 parts of calcium hydroxide 3 parts of bentonite, 4 parts of alumina, 15 parts of antimony trioxide, 5 parts of wood fiber powder, 8 parts of glass fiber, 4 parts of zinc borate, 5 parts of silane couplin...

Embodiment 2

[0019] An antibacterial and oil-resistant rubber material for a baseball core proposed by the present invention, its raw materials include by weight: 40 parts of ABS resin, 25 parts of organic fluorine epoxy resin, 4 parts of urea-formaldehyde resin, 8 parts of epichlorohydrin rubber, and 4 parts of acrylic resin , 5 parts of vulcanizing agent TCY, 3 parts of trioctyl trimellitate, 4 parts of accelerator TT, 2 parts of accelerator BPP, 10 parts of epichlorohydrin, 3 parts of zeolite, 5 parts of calcium molybdate, 2 parts of wrought white powder, 6 parts of zeolite powder, 1 part of nitrocellulose, 4 parts of trimethyl phosphate, 1 part of cellulose hydroxyethyl ether, 8 parts of zinc stearate, 3 parts of fluorine micropowder, 6 parts of highly active magnesium oxide, 2 parts of calcium hydroxide , 4 parts of bentonite, 2 parts of alumina, 20 parts of antimony trioxide, 1 part of wood fiber powder, 12 parts of glass fiber, 2 parts of zinc borate, 6 parts of silane coupling agent...

Embodiment 3

[0023] An antibacterial and oil-resistant rubber material for a baseball core proposed by the present invention, its raw materials include by weight: 50 parts of ABS resin, 15 parts of organic fluorine epoxy resin, 8 parts of urea-formaldehyde resin, 4 parts of epichlorohydrin rubber, and 8 parts of acrylic resin , 2 parts of vulcanizing agent TCY, 6 parts of trioctyl trimellitate, 2 parts of accelerator TT, 6 parts of accelerator BPP, 5 parts of epichlorohydrin, 6 parts of zeolite, 1 part of calcium molybdate, 6 parts of wrought white powder, 2 parts of zeolite powder, 4 parts of nitrocellulose, 1 part of trimethyl phosphate, 5 parts of cellulose hydroxyethyl ether, 4 parts of zinc stearate, 6 parts of fluorine micropowder, 3 parts of highly active magnesium oxide, 5 parts of calcium hydroxide , 1 part of bentonite, 6 parts of alumina, 10 parts of antimony trioxide, 9 parts of wood fiber powder, 4 parts of glass fiber, 6 parts of zinc borate, 3 parts of silane coupling agent K...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial and oil-resistant rubber material for a baseball core. The antibacterial and oil-resistant rubber material is prepared from the following raw materials of ABS(acrylonitrile butadiene styrene) resin, organic fluorine epoxy resin, urea resin, epichlorohydrin rubber, acrylic resin, a vulcanizing agent TCY, trioctyl trimellitate, an accelerant TT, an accelerant BPP, epichlorohydrin, zeolite, calcium molybdate, forging white powder, zeolite powder, nitrocotton, trimethyl phosphate, hydroethyl ether cellilose, zinc stearate, fluorine micropowder, high-activity magnesium oxide, calcium hydroxide, bentonite, aluminum oxide, antimonous oxide, wood fiber powder, glass fiber, zinc borate, a silane coupling agent KH-560, an antibacterial modifying additive andan oil-resistant modifying filler. The antibacterial and oil-resistant rubber material for the baseball core has excellent antibacterial and oil-resistant properties.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to an antibacterial and oil-resistant rubber material for a baseball core. Background technique [0002] The baseballs used in soft baseball are divided into hollow balls and solid balls. The core material of solid balls is generally synthetic rubber, while the synthetic rubber in the prior art has poor antibacterial and oil resistance, which seriously reduces the quality and safety of the baseball. Also reduced the service life of baseball simultaneously. Therefore, it is urgent to develop a kind of antibacterial and oil-resistant rubber material for baseball core to solve the problems in the prior art. Contents of the invention [0003] In order to solve the technical problems in the background technology, the present invention proposes an antibacterial and oil-resistant rubber material for baseball cores, which has excellent antibacterial and oil-resistant properties. [0004]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L63/00C08L61/24C08L33/00C08L23/16C08K13/06C08K9/06C08K7/26C08K3/22C08K3/34C08K5/3492
CPCC08L55/02C08K2003/2241C08K2003/2296C08K2201/011C08L2205/035C08L63/00C08L61/24C08L33/00C08L23/16C08K13/06C08K9/06C08K7/26C08K3/22C08K3/34C08K5/34922
Inventor 周良正
Owner 天长市良文运动器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com