Electrolytic ion grounding electrode filler

An electrolytic ion and grounding electrode technology, applied in circuits, conductive materials, conductive materials, etc., can solve problems such as improving grounding resistance, and achieve the effect of reducing earth resistivity, avoiding dust, and having a large degree of ionization.

Inactive Publication Date: 2018-03-06
北京海德思特科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main function of the filler in the grounding electrode is to improve the grounding resistance. Although this invention adopts a new formula to make a paste-like resistance reducing agent, the dust generated in the production process is relatively small, and there is almost no dust in the transportation and construction process. Dust is generated, which can reduce environmental pollution and physical damage to operators; and it does not need to be mixed with water when used, which is convenient to use, but it does not improve the grounding resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolytic ion grounding electrode filler
  • Electrolytic ion grounding electrode filler
  • Electrolytic ion grounding electrode filler

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The electrolytic ion ground electrode filler has the following components: sepiolite 13g, trisodium phosphate 5g, hydroxyethyl fiber 3g, alkaline earth metal halide 2g, sulfate 2g, carbonate 2g, triterpene saponin 1g, Nano-calcium carbonate 0.4g, meteorological silica 0.6g, conductive graphite 14g, silica fume 3g, calcium-based bentonite 6g, water 5g.

Embodiment 2

[0037] The electrolytic ion ground electrode filling agent consists of the following components: sepiolite 10g, trisodium phosphate 4g, hydroxyethyl fiber 2g, alkaline earth metal halide 3g, sulfate 1g, carbonate 4g, triterpene saponin 0.9g , Nano-calcium carbonate 0.5g, meteorological silica 0.5g, conductive graphite 15g, silica fume 5g, calcium-based bentonite 3g, moisture 6g.

Embodiment 3

[0039] The electrolytic ion ground electrode filler has the following components: sepiolite 15g, trisodium phosphate 6g, hydroxyethyl fiber 2g, alkaline earth metal halide 1g, sulfate 3g, carbonate 3g, triterpene saponin 1.1g , Nano-calcium carbonate 0.6g, meteorological silica 0.5g, conductive graphite 10g, silica fume 2g, calcium-based bentonite 4g, water 4g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an electrolytic ion grounding electrode filler which is characterized by comprising the components by weight: 10-15 parts of meerschaum, 4-6 parts of a passivation antirust agent, 8-10 parts of humectants, 1-3 parts of dispensing agent, 10-15 parts of conductive graphite, 2-5 parts of silica fume, 3-6 parts of bentonite, and 4-6 parts of water. The electrolytic ion grounding electrode filler has advantages of facilitating construction, and improving grounding resistance.

Description

technical field [0001] The invention relates to the technical field of conductive materials, more specifically, it relates to an electrolytic ion ground electrode filling agent. Background technique [0002] With the continuous development of the national economy and the rapid improvement of the modernization level, under the guidance of informatization to drive industrialization, various types of information equipment, electronic computers, precision instruments, and data network equipment are used more and more widely, and the hazards of lightning strikes are also increasing. bigger. In this case, it has become a mainstream to use lightning and surge protectors to discharge the lightning current into the ground, and grounding materials are also widely used in various grounding systems. The quality of the grounding effect is directly related to Therefore, grounding has become an important part of lightning protection. [0003] The content of active ions in the soil is one...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/00H01B1/18H01R4/66
CPCH01B1/00H01B1/18H01R4/66
Inventor 赵良斌
Owner 北京海德思特科技有限公司