Heat-resistant waterproof material

A waterproof material and heat-resistant technology, applied in the direction of non-polymer adhesive additives, adhesive additives, non-polymer organic compound adhesives, etc., can solve the problems of poor waterproofness, adhesion and durability, and poor construction Convenience, poor waterproof effect and other problems, to achieve the effect of good waterproof performance, short drying time and good elasticity

Inactive Publication Date: 2018-03-13
成都科创诺商贸有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, water-soluble waterproof adhesive materials and solvent-based waterproof adhesive materials are poor in waterproofness, adhesion and durability. Although reactive waterproof adhesive materials have the advantages of good adhesion and durability, they have High cost, inconvenient construction, large pollution and other disadvantages, most of the waterproof materials used in the waterproof treatment in the prior art are waterproof coiled materials, which are high in cost, prone to damage, and poor in waterproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The present invention will be further described in detail below through specific implementation examples.

[0011] The heat-resistant waterproof material provided by the present invention is prepared from the following parts by weight of raw materials: 30-60 parts by weight of deionized water, 17-25 parts of ethyl acrylate , 5-12 parts of hydroxymethyl cellulose, 8-10 parts of ammonium persulfate, 5-8 parts of aluminum sulfate, 10-15 parts of tourmaline powder, 6-12 parts of sepiolite powder, 3-6 parts of talc powder, quartz sand 5-10 parts, 20-30 parts of high-density polyethylene resin, 10-15 parts of polyacrylamide, 5-8 parts of cedarwood acetate, 8-12 parts of triethylene glycol monoethyl ether, calcium disodium ethylenediaminetetraacetate 5 -7 parts, acetone glycidol 5-9 parts, quartz sand 3-6 parts, hydroxypropyl fiber 3-5 parts, styrene-acrylic emulsion 15-20 parts, calcium borosilicate 1-2 parts, thermal insulation filler 3- 5 parts, 3-5 parts of heat insulation r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-resistant waterproof material, and relates to the field of buildings. The heat-resistant waterproof material is prepared from the following raw materials in parts by weight: 30 to 60 parts of deionized water, 17 to 25 parts of ethyl acrylate, 5 to 12 parts of hydroxymethyl cellulose, 8 to 10 parts of ammonium persulfate, 5 to 8 parts of aluminum sulfate, 10 to 15 parts of tourmaline powder, 6 to 12 parts of sepiolite powder, 3 to 6 parts of talcum powder, 5 to 10 parts of quartz sand, 20 to 30 parts of high density polyethylene resin, 10 to 15 parts of polyacrylamide, 5 to 8 parts of cedryl acetate, 8 to 12 parts of triethylene glycol monoethyl ether, 5 to 7 parts of Calcium disodium edetate, 5 to 9 parts of isopropylidene glycerol, 3 to 6 parts of quartz sand, 3 to 5 parts of hydroxypropyl cellulose, 15 to 20 parts of styrene-acrylate emulsion, 1 to 2 parts of calcium borosilicate, 3 to 5 parts of heat-insulation filler, 3 to 5 parts of heat-insulation reinforcing material and 1 to 5 parts of additive. The heat-resistant waterproof material is good in waterproof performance, good in elasticity, large in tensile amount and insoluble in water, has no water seepage, and is good in abrasion resistance, long in service life, further, quick in initial setting speed and short in drying time.

Description

Technical field [0001] The invention relates to the field of construction, in particular to a heat-resistant waterproof material. Background technique [0002] At present, the types of waterproof adhesive materials commonly used mainly include water-soluble waterproof adhesive materials, solvent-based waterproof adhesive materials, and reactive waterproof adhesive materials. Among them, water-soluble waterproof adhesive materials and solvent-based waterproof adhesive materials have poor water resistance, adhesiveness and durability. Although reactive waterproof adhesive materials have the advantages of good adhesiveness and durability, they are High cost, inconvenient construction, high pollution and other shortcomings. In the prior art, most of the waterproof materials used in the waterproof treatment are waterproof coiled materials, which are expensive, prone to damage, and have poor waterproof effects. Summary of the invention [0003] The object of the present invention is to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06C09J11/08
CPCC09J4/06C09J11/04C09J11/06C09J11/08
Inventor 张淞张光成
Owner 成都科创诺商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products